Anti-aging garbage can and preparation process thereof

A preparation process and technology of trash cans, which are applied in the field of trash cans, can solve the problems of shortened service life of polypropylene materials, deterioration of mechanical properties of polypropylene materials due to aging and degradation, and impact on the service life of trash cans, etc., to achieve reduced exposure and excellent mechanical properties , Excellent anti-corrosion effect

Pending Publication Date: 2020-03-06
江苏林辉塑料制品有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned existing technical solutions have the following defects: although the above-mentioned garbage can has good thermal stability and excellent flame retardant performance, when the garbage can is used outdoors for a long time, because polypropylene is very sensitive to ultraviolet rays, it is easily affected by light, The effect of heat and oxygen will cause the aging degradation of polypropylene material and the deterioration of mechanical properties, which will shorten the service life of polypropylene material and affect the service life of the trash can

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-aging garbage can and preparation process thereof
  • Anti-aging garbage can and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An anti-aging trash can specifically includes the following components: 50kg of polypropylene, 20kg of modified montmorillonite, 5kg of ultraviolet absorber, 3kg of filler, 1kg of lubricant and 3kg of flame retardant, wherein the preparation method of modified montmorillonite As follows: 1) Add cyanuric chloride to acetone, under ice-water bath conditions, stir until cyanuric chloride is completely dissolved; 2) Dissolve sodium p-aminobenzenesulfonate in deionized water to make a solution, and drop by drop Add it to the solution in step 1), and control the pH of the solution to 5 during the dropwise addition. After the dropwise addition, continue to stir for 2 hours, and the molar ratio of sodium p-aminobenzenesulfonate to cyanuric chloride is 1:1; When the temperature reaches 45°C, add tetramethylpiperidinamine to the above reaction system, the molar ratio of tetramethylpiperidinamine to cyanuric chloride is 1:1, adjust the pH of the reaction system to 6.5, and continue...

Embodiment 2

[0040] An anti-aging trash can specifically includes the following components: 55kg of polypropylene, 15kg of modified montmorillonite, 2kg of ultraviolet absorber, 4kg of filler, 2kg of lubricant and 0.5kg of flame retardant, wherein the preparation of modified montmorillonite The method is as follows: 1) Add cyanuric chloride to acetone, under the condition of ice-water bath, stir until the cyanuric chloride is completely dissolved; 2) Dissolve sodium p-aminobenzenesulfonate in deionized water to make a solution, and dropwise Add dropwise to the solution in step 1), the dropwise addition process controls the pH of the solution to be 6, after the dropwise addition, continue to stir for 4h, the molar ratio of sodium p-aminobenzenesulfonate to cyanuric chloride is 1:1; 3) rise When the temperature of the system reaches 60°C, add tetramethylpiperidinamine to the above reaction system, the molar ratio of tetramethylpiperidinamine to cyanuric chloride is 1:1, adjust the pH of the r...

Embodiment 3

[0047] An anti-aging trash can specifically includes the following components: 60kg of polypropylene, 18kg of modified montmorillonite, 5kg of ultraviolet absorber, 4kg of filler, 3kg of lubricant and 2kg of flame retardant, wherein the preparation method of modified montmorillonite As follows: 1) Add cyanuric chloride to acetone, under ice-water bath conditions, stir until cyanuric chloride is completely dissolved; 2) Dissolve sodium p-aminobenzenesulfonate in deionized water to make a solution, and drop by drop Add it to the solution in step 1), and control the pH of the solution to 5.5 during the dropwise addition. After the dropwise addition, continue to stir for 3 hours, and the molar ratio of sodium p-aminobenzenesulfonate to cyanuric chloride is 1:1; When the temperature reaches 55°C, add tetramethylpiperidinamine to the above reaction system, the molar ratio of tetramethylpiperidinamine to cyanuric chloride is 1:1, adjust the pH of the reaction system to 7, and continue...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Relating to the technical field of garbage cans, the invention relates to an anti-aging garbage can and a preparation process thereof. The anti-aging garbage can comprises the following components bymass: 50-60 parts of polypropylene, 15-20 parts of modified montmorillonite, 2-5 parts of an ultraviolet light absorber, 3-5 parts of filler, 1-3 parts of a lubricant and 0.5-3 parts of a flame retardant. According to the invention, cyanuric chloride, sodium sulfanilate and tetramethylpiperidine amine are employed to synthesize a hindered amine light stabilizer, and through ion exchange, the hindered amine light stabilizer is intercalated to the interlayer of montmorillonite, the prepared modified montmorillonite has anti-aging effect, and the modified montmorillonite is uniformly dispersed inpolypropylene, thus guaranteeing a consistent anti-aging effects at all parts. The anti-aging garbage prepared according to the invention has the effects of excellent anti-aging performance and prolonged service life.

Description

technical field [0001] The invention relates to the technical field of trash cans, in particular to an anti-aging trash can and a preparation process thereof. Background technique [0002] Garbage disposer, has another name called litter box or dustbin, is a container specially for holding rubbish, waste. Trash cans are rich in materials, mainly including plastic, ceramics, stainless steel, wood, cement, pulp, metal, glass steel, steel and wood, etc. Plastic trash cans have the advantages of simple processing, easy cleaning, wide application range, and low price. be more and more widely used. At present, plastic trash cans on the market are mainly made of high-density polyethylene or polypropylene. Polypropylene is more widely used because of its excellent physical and chemical properties. Polypropylene is a non-toxic, odorless, highly crystalline polymer that is extremely stable to water. In terms of thermal stability, polypropylene will not degrade at 100°C and has good ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L83/04C08L23/06C08K13/06C08K9/04C08K3/34C08K3/26C08K3/36C08K3/32
CPCC08K2003/265C08K2003/323C08L23/12C08L2201/02C08L2201/08C08L2205/03C08L2205/035C08L83/04C08L23/06C08K13/06C08K9/04C08K3/346C08K3/26C08K3/36C08K3/32
Inventor 周林辉金丽周慧微陈朝阳周玲丹潘友聪
Owner 江苏林辉塑料制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com