A kind of silicon carbon negative electrode material slurry and preparation method thereof

A negative electrode material and slurry technology, applied in the field of silicon carbon negative electrode material slurry and its preparation, can solve the problems of silicon carbon particle damage, uneven dispersion, poor graphite wrapping, etc., to prevent secondary agglomeration and improve cycle life , Improve the effect of dispersion effect

Active Publication Date: 2022-05-03
SHAANXI COAL & CHEM TECH INST
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The uniformity of dispersion when silicon carbon is mixed with graphite will have a crucial impact on the performance of silicon carbon materials and the overall performance of the battery. It is easy to agglomerate, and there is a huge volume change when the silicon carbon material is charged and discharged, the dispersion is uneven, the graphite is not well wrapped, and the electrode sheet is prone to powder drop phenomenon. At the same time, the dispersion process will cause damage to the silicon carbon particles, resulting in the exposure of the silicon particles. Affect battery cycle performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of silicon carbon negative electrode material slurry and preparation method thereof
  • A kind of silicon carbon negative electrode material slurry and preparation method thereof
  • A kind of silicon carbon negative electrode material slurry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the silicon carbon negative electrode material slurry of the present invention comprises the following steps:

[0027] 1) According to the pulping ratio, add part of the CMC glue, all the conductive agent and all the silicon carbon particles, mix and wet at a low speed of 10-100 rpm for 10-100 minutes, and then disperse at a high speed of 2000-3000 rpm for 60- 180 minutes, obtain slurry 1;

[0028] 2) Add all the graphite materials to the slurry 1, mix and wet at a low speed of 10-100 rpm for 10-100 minutes, then disperse at a high speed of 2000-3000 rpm for 60-180 minutes to obtain slurry 2;

[0029] 3) Add the remaining CMC glue and part of the deionized water to the slurry 2, vacuumize, and disperse at a high speed of 2000-3000 rpm for 60-180 minutes to obtain the slurry 3;

[0030] 4) Add SBR binder with a solid content of 45% to the slurry 3, disperse at a high speed of 2000-3000 rpm for 20-90 minutes, add deionized water to adjust the vi...

Embodiment 1

[0040] 1) According to the mass ratio of silicon carbon, graphite, conductive agent, sodium carboxymethyl cellulose (CMC), and SBR 10:85:1:1.5:2.5, add carboxymethyl with a solid content of 1% accounting for 30% of the total glue amount Base cellulose sodium (CMC) glue 720g, conductive agent SP16g and core-shell silicon carbon particles 160g (900mAh / g), wherein the silicon carbon particle D50 is 15μm, first mix and wet at low speed at 10 rpm for 10 minutes, and then 2000 rpm high-speed dispersion for 60 minutes to obtain slurry 1;

[0041] 2) Then add 1360g of all graphite materials to the slurry 1, wherein the graphite particle D50 is 10 μm, mix and wet at a low speed of 10 rpm for 10 minutes, and then disperse at a high speed of 2000 rpm for 60 minutes, slurry 2;

[0042] 3) Add 1680g of remaining glue and deionized water to slurry 2, vacuumize at 2000 rpm and disperse at high speed for 60 minutes, slurry 3;

[0043] 4) Add 88g of binder SBR to the slurry 3, disperse at a h...

Embodiment 2

[0045] 1) According to the mass ratio of silicon carbon, graphite, conductive agent, sodium carboxymethylcellulose (CMC), and SBR of 20:70:6:2:2, add carboxymethyl, which accounts for 35% of the total glue amount and has a solid content of 1.5%. Cellulose sodium (CMC) glue 778g, conductive agent Ketjen black 100g and embedded silicon carbon negative electrode material 333g (600mAh / g), in which the silicon carbon particle D50 is 19μm, mixed and wetted at low speed at 10 rpm for 30 minutes , and then dispersed at a high speed of 2200 rpm for 100 minutes, slurry 1;

[0046] 2) Then add 1166g of all graphite materials to the slurry 1, wherein the graphite particle D50 is 10 μm, mix and wet at a low speed of 10 rpm for 30 minutes, and then disperse at a high speed of 2200 rpm for 100 minutes, slurry 2;

[0047] 3) Add 1444g of remaining glue solution and deionized water to slurry 2, vacuumize at 2200 rpm and disperse at high speed for 100 minutes, slurry 3;

[0048] 4) Add 74.07g ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a silicon carbon negative electrode material slurry and a preparation method thereof, comprising the following steps: 1) dividing the CMC glue into two parts, and mixing the first part of the CMC glue, a conductive agent and a silicon carbon material to obtain a slurry 1 2) Add graphite material to slurry 1, and disperse to obtain slurry 2; 3) Add second part of CMC glue and water to slurry 2, vacuumize, and disperse to obtain slurry 3; 4) To slurry 3 SBR binder is added to the medium, and after dispersion, the slurry is sieved to remove air bubbles to obtain a silicon carbon negative electrode material slurry. Eliminate the agglomeration of silicon carbon particles during the pulping process, ensure that the graphite material is evenly wrapped around the silicon carbon particles, and improve the overall cycle life of the battery.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, and in particular relates to a silicon-carbon negative electrode material slurry and a preparation method thereof. Background technique [0002] With the increasing demand for battery energy density in the current market, conventional graphite anode materials are no longer able to meet the growing requirements. Therefore, in recent years, silicon-carbon anode materials have been considered as anode materials for next-generation high-energy-density lithium-ion batteries due to their higher gram capacity, environmental friendliness, and abundant reserves. The uniformity of dispersion when silicon carbon is mixed with graphite will have a crucial impact on the performance of silicon carbon materials and the overall performance of the battery. It is easy to agglomerate, and there is a huge volume change when the silicon carbon material is charged and discharged, the dispersion is uneve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/583H01M10/0525
CPCH01M4/366H01M4/386H01M4/583H01M10/0525H01M2004/027Y02E60/10
Inventor 范瑞娟田占元邵乐沈晓辉曹国林
Owner SHAANXI COAL & CHEM TECH INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com