A kind of preparation method of spandex fiber with low broken filament rate

A technology of spandex fiber and broken filament rate, which is applied in rayon manufacturing, fiber chemical characteristics, single-component synthetic polymer rayon, etc., can solve the problems of large difference between the surface and the inside of spandex, weak adsorption, and insufficient oil film strength, etc. Achieve good physical properties and improve the problem of broken wires

Active Publication Date: 2022-05-03
ZHEJIANG HUAFENG SPANDEX
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, CN100338300C improves the unwinding of spandex yarn by adding divalent stearic acid metal salt as an anti-adhesive additive to the oil agent, and patent CN101440574B adds silicone resin as an anti-blocking additive to improve the unwinding of the silk cake , although stearate and silicone resin can indeed play the role of anti-adhesive and slippery, but the anti-adhesive durability is insufficient, due to the low surface energy of silicone oil and mineral oil in the oil component, the strength of the oil film is insufficient, and the adsorption Weakness, once the tension of the spandex yarn is too high or it is placed for a long time, the oil agent will easily migrate from the bottom of the yarn cake to the surface, resulting in a large difference between the surface and the inside of the spandex yarn, and it is easy to break the yarn in the subsequent application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1) Add polystyrene, acrylic resin and N,N-dimethylacetamide into the reaction kettle, heat the temperature to 60°C, and stir evenly to obtain a blend solution A with a solid content of 35%. According to the solid content of spandex fiber, polystyrene accounts for 0.5%, and acrylic resin accounts for 1.0%.

[0030] 2) Add polytetramethylene ether glycol with a number average molecular weight of 1810, 4,4'-diphenylmethane diisocyanate and N,N-dimethylacetamide to form a 69% mass fraction of solution, and reacted at 45°C for 120 minutes to prepare a prepolymer. After the prepolymer is cooled to 8°C, chain extension reaction is carried out with a mixed amine solution of ethylenediamine and diethylamine having a mass fraction of 5.5%, wherein the molar ratio of ethylenediamine to diethylamine is 20 :1. According to the solid content of polyurethane urea elastic fiber, 0.5wt% of 2-(2'-hydroxyl-3', 5'-di-tert-butylphenyl)-benzotriazole), 0.5wt% of bis(N, Add N-dimethylhydra...

Embodiment 2

[0034] Spandex fibers were prepared according to the same method described in Example 1, except that the proportion of polystyrene was 5.0%. The abrasion amount thereof was evaluated, and the evaluation results are shown in Table 1 below.

Embodiment 3

[0036] Spandex fibers were prepared according to the same method described in Example 1, except that the proportion of polystyrene was 10.0%. The abrasion amount thereof was evaluated, and the evaluation results are shown in Table 1 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a method for preparing spandex fiber with a low breakage rate, and more particularly, to a method for manufacturing spandex by introducing a blended solution of an anti-wear agent and a flow promoter into a polyurethaneurea spinning solution, 1) By blending and dissolving the anti-wear agent and the flow promoter in an organic solvent, a blended solution A is prepared; 2) the above-mentioned blended solution A is added to the polyurethaneurea spinning solution B to prepare a spinning dope C, Spinning and winding of the above-mentioned spinning dope C were carried out. The manufacturing method has a simple and convenient implementation process, and can be widely applied to different varieties of spandex fibers, and the situation of the prepared spandex fibers being broken is obviously reduced.

Description

technical field [0001] The invention relates to a method for manufacturing a novel functionalized spandex fiber, in particular to a method for manufacturing a spandex fiber with improved filament breakage, and the invention belongs to the technical field of polymer material preparation. Background technique [0002] Spandex is a highly elastic chemical fiber, its elongation at break is 500% to 700%, its elastic recovery rate is generally greater than 90%, and its breaking strength is high. Therefore, spandex fiber is widely used in knitted and woven fabrics. However, during the weaving and unwinding process of spandex fiber, it needs to pass through many driven wire guide wheels. When running for a long time, spandex fiber is prone to broken wires. After the wire wheel has been running for a long time, the inner wall will be worn to varying degrees, which will make the spandex yarn in a state of obstruction or even cut during the guiding process, increasing the number of bro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/94D01F1/10C08G18/76C08G18/66C08G18/48C08G18/10C08G18/32
CPCD01F6/94D01F1/10C08G18/7671C08G18/4854C08G18/10C08G18/3228
Inventor 王靖梁红军杨晓印许图远周志伟
Owner ZHEJIANG HUAFENG SPANDEX
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap