Method for making austenitic stainless steel weld defect test plate with unfused defect

A technology for austenitic stainless steel and unfused defects, which is used in the field of defect test plates

Active Publication Date: 2021-07-06
WUHAN YIYE STEEL STRUCTURE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since there is no formal PAUT testing standard in China, it is necessary to make a defect test plate to conduct a comparative test of different nondestructive testing methods to determine the PAUT testing process of austenitic stainless steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making austenitic stainless steel weld defect test plate with unfused defect
  • Method for making austenitic stainless steel weld defect test plate with unfused defect
  • Method for making austenitic stainless steel weld defect test plate with unfused defect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Manufacturing method of austenitic stainless steel weld defect test plate with unfused defects on the longitudinal groove side, such as Figure 1 to Figure 3 shown, including the following steps:

[0056] (1) Welding blanking: 304L material, thickness 40mm, cutting by CNC plasma, blanking size 500×150×40mm, two pieces of austenitic stainless steel weldment 1 adopt groove machining groove, in order to prevent welding For deformation, symmetrical X-shaped grooves are adopted, and the angle of paired grooves is 40°;

[0057] (2) Preparation before welding: Grinding both sides of the groove to remove oil and debris to ensure the cleanliness of the groove, and spot welding at both ends of the weldment by gas tungsten shielded welding;

[0058] (3) Backing welding: Gas tungsten arc welding is used for root backing welding, and the welding wire is ER317L (mod.) from Bo-Le, with a diameter of 2.4mm, which is a fully austenitic welding wire. The back side is protected by argon...

Embodiment 2

[0063] Method for manufacturing austenitic stainless steel weld defect test plate with transverse non-fusion defects, such as Figure 4 to Figure 6 shown, including the following steps:

[0064] (1) Welding blanking: 304L material, thickness 40mm, cutting by CNC plasma, blanking size 500×150×40mm, two pieces of austenitic stainless steel weldment 1 adopt groove machining groove, in order to prevent welding For deformation, symmetrical X-shaped grooves are adopted, and the paired groove angle is 40°;

[0065] (2) Preparation before welding: Grinding both sides of the groove to remove oil and debris to ensure the cleanliness of the groove, and spot welding at both ends of the weldment by gas tungsten shielded welding;

[0066] (3) Backing welding: Gas tungsten arc welding is used for root backing welding, and the welding wire is ER317L (mod.) from Bo-Le, with a diameter of 2.4mm, which is a fully austenitic welding wire. The back side is protected by argon gas, and the front a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing an austenitic stainless steel weld defect test plate with unfused defects. Gas tungsten electrode shielded welding is used for bottom welding first, and then electrode arc welding is used for filling welding; according to the preset number and position of unfused metal layers, gas tungsten shielded welding is used to make unfused defects in the corresponding weld metal layer; After the defect is made, the weldment is adjusted to the flat welding position, and a layer of weld meat is welded on the top or side of the unfused defect by MIGA welding for post-processing, and the remaining positions continue to be filled by electrode arc welding. The manufacturing method of the austenitic stainless steel weld defect test plate with non-fusion defects proposed by the present invention can realize the preparation of non-fusion defects at any part of the weld, thereby satisfying the comparison test of various detection methods. Application requirements for testing personnel training.

Description

technical field [0001] The invention relates to the technical field of a method for manufacturing a defect test plate, in particular to a method for manufacturing an austenitic stainless steel weld defect test plate with unfused defects. Background technique [0002] At present, the commonly used non-destructive testing methods for austenitic stainless steel in engineering include radiographic testing (RT), ultrasonic testing (UT), and penetrant testing (PT). Austenitic stainless steel grains are coarse, and there are many clutter and low sensitivity when performing UT testing. The experience requirements for non-destructive testing personnel are high. PT is generally used as an auxiliary detection method. Therefore, it is best to detect internal defects in austenitic stainless steel welds. The commonly used method is RT. However, for thick plates, especially those over 50 mm, the contrast of RT detection is poor, and a radioactive source with stronger penetrating power is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/167B23K9/173B23K9/28B23K9/235B23K9/32B23K103/04
CPCB23K9/167B23K9/173B23K9/235B23K9/28B23K9/32B23K2103/05
Inventor 闵晓峰莫芝林潘伍覃侯华东黄壮
Owner WUHAN YIYE STEEL STRUCTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com