Porous ceramic atomizing core and preparation method thereof

A technology of porous ceramics and atomizing cores, applied in the field of ceramic materials, can solve the problems of affecting the taste of electronic cigarettes, oil leakage, low production process efficiency, etc., and achieve the effects of high dimensional stability, simple process flow and low cost

Active Publication Date: 2020-01-21
湖南福美来电子陶瓷有限公司
View PDF12 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the method of producing the heating and vaporization module is to roast the atomizing core first, then wrap cotton cloth around the atomizing core, and then insert the atomizing core into the oil guide rod. This production process has low efficiency, and the oil guide rod and There will be gaps between the atomizing cores, resulting in oil leakage during use, which seriously affects the taste of electronic cigarettes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous ceramic atomizing core and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] According to the mass percentage, weigh 55% diatomite, 25% low-temperature glass, 19% PMMA, 1% vermiculite, and weigh 40% of the total mass of the above-mentioned diatomite, low-temperature glass, PMMA and vermiculite Paraffin wax and 5% beeswax, among them, the median particle size of diatomaceous earth is 20 μm, the median particle size of low temperature glass is 25 μm, the median particle size of PMMA is 15 μm, and the median particle size of vermiculite is 12 μm.

[0021] Mix diatomaceous earth, low-temperature glass powder, PMMA and vermiculite evenly, ball mill for 2 hours, and dry at 90°C for 5 hours to obtain a mixture. Melt paraffin and beeswax at 95°C into a liquid and mix with the mixture. Stir for 2 hours, pour the uniformly mixed slurry into the oil guide rod, and hot die-cast it to make a prefabricated green body. Heat the green body at a heating rate of 130°C / h to 160°C, and then at a heating rate of 145°C / h Raise the temperature to 340°C, then raise the...

Embodiment 2

[0023] According to mass percentage, take by weighing 60% diatomite, 25% low-temperature glass, 14% PMMA, 1% vermiculite, and weigh 42% of the total mass of diatomite, low-temperature glass, PMMA and vermiculite. % paraffin and 6% beeswax, among which, the median particle size of diatomaceous earth is 25 μm, the median particle size of low temperature glass is 30 μm, the median particle size of PMMA is 20 μm, and the median particle size of vermiculite is 15 μm .

[0024] Mix diatomaceous earth, low-temperature glass powder, PMMA and vermiculite evenly, ball mill for 3 hours, and dry at 85°C for 5 hours to obtain a mixture. Melt paraffin and beeswax at 95°C into a liquid and mix with the mixture. Stir for 2.5 hours, pour the uniformly mixed slurry into the oil guide rod, and hot die-cast it to make a prefabricated body. Raise the temperature of the green body to 180°C at a heating rate of 145°C / h, and then increase the temperature at a rate of 145°C / h The temperature was rais...

Embodiment 3

[0026] According to mass percentage, take by weighing 65% diatomite, 20% low-temperature glass, 13.5% PMMA, 1.5% vermiculite, and weigh 45% of the total mass of diatomite, low-temperature glass, PMMA and vermiculite. % paraffin and 7% beeswax, among them, the median particle size of diatomaceous earth is 30 μm, the median particle size of low temperature glass is 35 μm, the median particle size of PMMA is 25 μm, and the median particle size of vermiculite is 15 μm .

[0027] Mix diatomaceous earth, low-temperature glass powder, PMMA and vermiculite evenly, ball mill for 3 hours, and dry at 90°C for 5 hours to obtain a mixture. Melt paraffin and beeswax at 95°C into a liquid and mix with the mixture. Stir for 2.5 hours, pour the uniformly mixed slurry into the oil guide rod, and make a prefabricated green body by hot die-casting. The green body is heated up to 180°C at a heating rate of 130°C / h, and then heated at a rate of 145°C / h The temperature was raised to 340°C at a rate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a porous ceramic atomizing core and a preparation method thereof. The porous ceramic atomization core is composed of a mixture and a molten material, wherein the mixture comprises: 40%-69% of diatomite, 20%-35% of low-temperature glass powder, 10%-20% of a pore-forming agent and 1%-2% of vermiculite and / or perlite; and the molten material comprises paraffin accounting for 40%-50% of the mass of the mixture and beewax accounting for 5%-10% of the mass of the mixture. The preparation method of the porous ceramic atomization core comprises the steps of material mixing, blank making and sintering. The porous ceramic atomization core material and the oil guide rod are integrally roasted and formed, so that the production efficiency is remarkably improved, the technological process is simple, the cost is low, the prepared porous ceramic atomization core is extremely high in size stability, the atomization core is tightly attached to the oil guide rod, and the oil leakage phenomenon cannot occur.

Description

technical field [0001] The invention belongs to the field of ceramic materials, and in particular relates to a porous ceramic atomizing core and a preparation method thereof. Background technique [0002] Porous ceramics are widely used in the field of vaping cores due to their high porosity, good oil storage, high oil absorption, and high temperature resistance, which are not suitable for burning. The electronic cigarette heating and vaporizing module is the core component of the electronic cigarette, usually including the oil guide rod and the atomizing core. At present, the method of producing the heating and vaporization module is to roast the atomizing core first, then wrap cotton cloth around the atomizing core, and then insert the atomizing core into the oil guide rod. This production process has low efficiency, and the oil guide rod and There will be gaps between the atomizing cores, resulting in oil leakage during use, which seriously affects the taste of electroni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B38/06C04B35/64A24F40/40
CPCC04B35/16C04B35/64C04B38/0645C04B38/067C04B38/0675C04B2235/36C04B2235/349C04B2235/48C04B2235/3463C04B2235/6562C04B38/0074C04B38/0067
Inventor 陆挺
Owner 湖南福美来电子陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com