Transparent polyurethane paint for dyed veneer and preparation method of transparent polyurethane paint

A technology of polyurethane paint and polyurethane resin, applied in the field of polyurethane paint, can solve the problems of not being able to guarantee the viscosity, strength and drying speed at the same time, and achieve the effect of wide application range, convenient work and convenient use.

Inactive Publication Date: 2019-12-20
君子兰涂料(天津)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a transparent polyurethane paint for dyeing veneer and its preparation method, which solves the problem that the traditional transparent polyurethane paint cannot guarantee the viscosity, strength and drying speed at the same time due to the limitation of materials. , only one of them can be guaranteed to meet the standard problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent polyurethane paint for dyed veneer and preparation method of transparent polyurethane paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] S1, 35 parts of polyurethane resin, 10 parts of xylene, 15 parts of butyl acetate, 4 parts of cyclohexanone, 6 parts of cyanoacetoxy compound, 5 parts of polyvinyl acetate emulsion, 10 parts of 107 glue, whitening agent 5 parts, 5 parts of flocculant, and 10 parts of clear water;

[0027] S2. Screen all the xylene, butyl acetate, cyclohexanone and cyanoacetoxy compounds to remove the impurities inside, and then use a filter to filter the clear water, and the whitening agent, flocculant, 107 Glue and polyvinyl acetate emulsion are taken out of the original packaging and do not need to be filtered;

[0028] S3. Before adding the flocculant, it is necessary to add a whitening agent. After adding the whitening agent, stir several times, and choose the standing time according to the mixing amount. After standing for 10 minutes, add the flocculant and fully mix and stir. After mixing Stand still again and wait for the flocculation to end;

[0029] S4. Take out the transpare...

Embodiment 2

[0033] S1, 30 parts of polyurethane resin, 20 parts of xylene, 10 parts of butyl acetate, 5 parts of cyclohexanone, 5 parts of cyanoacetoxy compound, 5 parts of polyvinyl acetate emulsion, 10 parts of 107 glue, whitening agent 4 parts, 6 parts of flocculant, and 5 parts of clear water;

[0034] S2. Screen all the xylene, butyl acetate, cyclohexanone and cyanoacetoxy compounds to remove the impurities inside, and then use a filter to filter the clear water, and the whitening agent, flocculant, 107 Glue and polyvinyl acetate emulsion are taken out of the original packaging and do not need to be filtered;

[0035] S3. Before adding the flocculant, it is necessary to add a whitening agent. After adding the whitening agent, stir several times, and choose the standing time according to the mixing amount. After standing for 10 minutes, add the flocculant and fully mix and stir. After mixing Stand still again and wait for the flocculation to end;

[0036] S4. Take out the transparen...

Embodiment 3

[0040] S1, 40 parts of polyurethane resin, 10 parts of xylene, 5 parts of butyl acetate, 5 parts of cyclohexanone, 4 parts of cyanoacetoxy compounds, 6 parts of polyvinyl acetate emulsion, 15 parts of 107 glue, and whitening agent 4 parts, 6 parts of flocculant, and 5 parts of clear water;

[0041] S2. Screen all the xylene, butyl acetate, cyclohexanone and cyanoacetoxy compounds to remove the impurities inside, and then use a filter to filter the clear water, and the whitening agent, flocculant, 107 Glue and polyvinyl acetate emulsion are taken out of the original packaging and do not need to be filtered;

[0042] S3. Before adding the flocculant, it is necessary to add a whitening agent. After adding the whitening agent, stir several times, and choose the standing time according to the mixing amount. After standing for 10 minutes, add the flocculant and fully mix and stir. After mixing Stand still again and wait for the flocculation to end;

[0043] S4. Take out the transp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses transparent polyurethane paint for dyed veneer and a preparation method of the transparent polyurethane paint. The raw materials of the transparent polyurethane paint include,in parts by weight, 30-45 parts of polyurethane resin, 10-20 parts of xylene, 10-20 parts of butyl acetate, 4-6 parts of cyclohexanone, 4-8 parts of a cyanoacetoxy compound, 4-6 parts of a polyvinyl acetate emulsion, 10-15 parts of 107 glue, 4-5 parts of a whitening agent, 2-6 parts of a flocculant and 6-10 parts of clear water. The invention relates to the technical field of polyurethane paint. According to the transparent polyurethane paint for dyed veneer and the preparation method of the transparent polyurethane paint, the produced transparent polyurethane paint has three characteristics,a high condensation speed, more convenient use and a wider application range, use of the transparent polyurethane paint is not restricted, application is facilitated, and the problems are solved thatadhesion viscosity, adhesion strength and drying speed of existing transparent polyurethane paint cannot be ensured at the same time due to limitation of materials, and it is ensured that only one ofthe three indexes can be met.

Description

technical field [0001] The invention relates to the technical field of polyurethane paint, in particular to a transparent polyurethane paint for dyeing veneer and a preparation method thereof. Background technique [0002] Polyurethane paint is polyurethane paint. It has strong paint film, full luster, strong adhesion, water resistance, wear resistance and corrosion resistance. It is widely used in high-grade wooden furniture and can also be used on metal surfaces. Its shortcomings mainly include problems such as foaming when it is wet, and powdering of the paint film. Like polyester paint, it also has the problem of yellowing. The varnish variety of polyurethane paint is called polyurethane varnish. Polyurethane coating is a relatively common type of coating, which can be divided into two-component polyurethane coatings and one-component polyurethane coatings. Two-component polyurethane coatings are generally composed of isocyanate prepolymers (also known as low-molecular...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D131/04C09D129/14
CPCC08L2201/10C08L2205/03C09D175/04C08L31/04C08L29/14
Inventor 詹成钢王有为吴子成
Owner 君子兰涂料(天津)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com