Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Pervious concrete

A technology of permeable concrete and water reducing agent, which is applied in the field of building materials to achieve significant temperature peaks, small thermal expansion coefficients, and excellent durability

Inactive Publication Date: 2019-11-22
SINOHYRDO ENG BUREAU 3 CO LTD
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of anti-corrosion high-performance permeable concrete in order to overcome the general technical problems encountered in the popularization and application of the existing permeable concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pervious concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment provides a kind of permeable concrete. According to the mass parts, the permeable concrete is prepared from the following components: 1500kg of limestone aggregate, 240kg of cement, 32kg of silica fume, 32kg of silicon nitride, 16kg of fly ash, water reducing Agent 4.5kg and water 105kg.

Embodiment 2

[0047] This embodiment provides a kind of permeable concrete. According to the mass parts, the permeable concrete is prepared from the following components: 1542kg of granite aggregate, 257kg of cement, 37kg of silica fume, 37kg of silicon nitride, 37kg of fly ash, water reducing Agent 5.1kg and water 110kg.

Embodiment 3

[0049] This embodiment provides a kind of permeable concrete. According to the parts by mass, the permeable concrete is prepared from the following components: 1600kg of basalt aggregate, 273kg of cement, 42kg of silica fume, 42kg of silicon carbide, 63kg of fly ash, and water reducer 5.9kg and 114kg of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses pervious concrete which is characterized in that the pervious concrete is prepared from the following components in parts by mass: 1500-1600 parts of coarse aggregate, 320-420parts of a cementing material, 105-114 parts of water and 4.5-5.9 parts of a water reducing agent. An anti-corrosion material in the formula has remarkable plasticizing effect, micro-aggregate effect,morphological effect and temperature peak reduction effect, and the mechanical property, abrasion resistance and denudation resistance of the pervious concrete can be improved through the excellent characteristics of the anti-corrosion material itself and the improvement of the continuous grading of the microstructure of the cementing material, so that the durability of the pervious concrete is improved, and the service lifetime of the pervious concrete is prolonged.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to permeable concrete. Background technique [0002] The country proposes and strongly calls for the construction of a "sponge city", that is, when it rains, the city should have a better ability to absorb, store, purify and infiltrate water, and infiltrate the water on the surface through itself and the grassroots, thereby reducing the surface water. runoff, maintain the groundwater level, purify water quality, and effectively reduce the load on urban drainage systems and rainwater accumulation in low-lying areas. As the key material of sponge city, permeable concrete also develops rapidly. Due to the poor mechanical properties of existing permeable concrete (compressive strength of actual permeable concrete in engineering construction is about 20MPa, flexural strength is about 2MPa), plus Due to the particularity of the structure of permeable concrete, ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/00C04B111/20
CPCC04B28/00C04B2111/00284C04B2111/2038C04B2201/50C04B14/28C04B18/146C04B18/08C04B14/328C04B2103/302C04B38/0041C04B14/048C04B14/324C04B14/14
Inventor 焦凯陈晨李磊史迅褚立波赵文升
Owner SINOHYRDO ENG BUREAU 3 CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com