Preparation method of graphite carbon coated iron-nitrogen-carbon solid-phase Fenton catalyst and its application

A catalyst, graphitic carbon technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problem of decomposing action to be studied, high cost, and achieve the promotion of decomposing action, excellent performance, synthesis simple steps

Active Publication Date: 2019-11-08
SOUTH CENTRAL UNIVERSITY FOR NATIONALITIES
View PDF10 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently, reported graphitic carbon-wrapped Fe 3 Most of the synthesis methods of C catalysts are compounded by graphene, carbon nanotubes and iron phthalocyanine and processed through a series of complicated steps, and the cost is relatively high
[0007] Catalyst synthesis methods with iron-nitrogen active sites or the coexistence of iron-nitrogen species and carbon-iron species need to be further developed. 2 o 2 The role of decomposition remains to be studied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphite carbon coated iron-nitrogen-carbon solid-phase Fenton catalyst and its application
  • Preparation method of graphite carbon coated iron-nitrogen-carbon solid-phase Fenton catalyst and its application
  • Preparation method of graphite carbon coated iron-nitrogen-carbon solid-phase Fenton catalyst and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalyst, the preparation method of which is as follows:

[0045] 1) Mix 3g of glucose and 8g of urea (the molar ratio of carbon source to nitrogen source is 1:8), heat and melt at 150°C until clarified, then add 3.03g of ferric nitrate nonahydrate and stir until completely dissolved, transfer to Dry in an oven at 180°C for 12h, and then calcined at 750°C for 2h under the protection of nitrogen atmosphere to obtain a graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalyst. The mass fraction of Fe in the synthesized catalyst is 35%, labeled as FeNC@C-35.

Embodiment 2

[0047] A graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalyst, the preparation method of which is as follows:

[0048] Mix 3g of glucose and 5g of urea (the molar ratio of carbon source to nitrogen source is 1:5), heat and melt at 150°C until clarified, then add 1.73g of ferric nitrate nonahydrate and stir until completely dissolved, then transfer to 180°C Drying in an oven for 12 hours, followed by calcining at 750°C for 2 hours under the protection of a nitrogen atmosphere to obtain a graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalyst, the mass fraction of Fe in the synthesized catalyst is 20% , labeled as FeNC@C-20.

Embodiment 3

[0050] A graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalyst, the preparation method of which is as follows:

[0051] Mix 3g of glucose with 11g of urea (the molar ratio of carbon source to nitrogen source is 1:11), heat and melt at 150°C until clarified, then add 4.32g of ferric nitrate nonahydrate and stir until completely dissolved, then transfer to 180 ℃ in an oven for 24 hours, and then under the protection of nitrogen atmosphere, calcined at 750 ℃ ​​for 2 hours to obtain the iron-nitrogen-carbon solid-phase Fenton catalyst wrapped in graphite carbon. The mass fraction of Fe element in the synthesized catalyst is 50 %, marked as FeNC@C-50.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparing solid-phase Fenton catalyst, in particular to a preparation method of graphite carbon coated iron-nitrogen-carbon solid fenton catalyst and its application in organic wastewater treatment. The preparation method of the catalyst comprises the following steps: after mixing and melting the carbon source and the nitrogen source in a certain proportion, adding a certain proportion of iron source, fully stirring and dissolving the mixture, transferring the mixture to an oven at 150-180 DEG C for drying for 12-24 hours, and calcining under theprotection of nitrogen atmosphere to obtain the catalyst. The catalyst prepared by the invention is a graphite carbon coated FeN and Fe3C coexisting iron-nitrogen-carbon catalyst, the size of the nanoparticles is 5-30nm, the specific surface area of the catalyst is 80-300m2 / g, and the FeN is the main active site for decomposing hydrogen peroxide. The catalyst of the present invention can be applied to electric-Fenton and Fenton systems and an organic wastewater with pH range of 3-9 is treated. The preparation method of the invention has the advantages of simple steps, easy availability of rawmaterials, excellent performance, high stability and recyclability.

Description

technical field [0001] The invention relates to the technical field of preparation of solid-phase Fenton catalysts, in particular to a preparation method of graphite carbon-wrapped iron-nitrogen-carbon solid-phase Fenton catalysts and its application in treating organic wastewater. Background technique [0002] Fenton reaction (Fenton reaction), as an advanced oxidation technology, mainly refers to the use of Fe 2+ catalytic decomposition of H 2 o 2 , the process of generating a highly oxidative free radical product·OH (2.8eV), as shown in formula (1). Fe 2+ and H 2 o 2 Called Fenton's reagent. [0003] Fe 2+ +H 2 o 2 +H + → Fe 3+ +H 2 O+ OH (1) [0004] The Fenton method has been widely studied because it can generate a large amount of highly active OH and can efficiently degrade and treat organic wastewater. At present, the common Fenton methods include electric-Fenton, photo-Fenton, homogeneous-phase Fenton and solid-phase Fenton. In general, these methods c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/24C02F1/72C02F101/30
CPCB01J27/24C02F1/722C02F2101/30Y02W10/37
Inventor 胡晶晶孙杰余佳棋雷炜东李金林张煜华
Owner SOUTH CENTRAL UNIVERSITY FOR NATIONALITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap