GVTi wear-resistant type semisteel roller and preparation method thereof

A semi-steel roll and molten steel technology, which is applied in the field of GVTi wear-resistant semi-steel roll and its preparation, can solve the problems of low wear resistance, poor thermal crack resistance, and short service life of the roll, and achieve roll strength improvement and casting The effect of performance optimization and service life improvement

Inactive Publication Date: 2019-10-18
宜兴市国昌轧辊有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the high-quality development of the iron and steel industry, major steel mills pay more attention to energy saving and consumption reduction, especially the semi-steel rolls often used in the primary and secondary rolling mills involved in H-beams and rods and wires. The material has not been obtained for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1:

[0018] Melt the molten steel to control the mass percentage content of each element of the molten steel: C1.60, Si 0.80, Mn 0.60, Ni1.20, Cr 0.80, Mo 0.50, V 0.10, Ti 0.10, S≤0.03, P≤0.03, AL0.05 , CaSi0.10, the rest is Fe and unavoidable impurities; it is prepared by coarse-opening processing, diffusion annealing, normalizing and secondary tempering. Wherein, the diameter direction of the allowance of the roll body in the coarse opening processing step is controlled to be 8mm; in the secondary tempering step, the primary tempering temperature is controlled at 550°C, and the secondary tempering temperature is controlled at 560°C.

Example Embodiment

[0019] Example 2:

[0020] The molten steel is smelted to control the mass percentage content of each element in the molten steel: C2.00, Si 1.60, Mn1.20, Ni 3.00, Cr 2.00, Mo 1.00, V0.60, Ti 0.30, S≤0.03, P≤0.03, AL0. 10. CaSi0.30, the rest is Fe and unavoidable impurities; it is made by coarse-opening processing, diffusion annealing, normalizing and secondary tempering. Wherein, the diameter direction of the roll body allowance in the coarse-opening processing step is controlled to 12 mm; in the secondary tempering step, the primary tempering temperature is controlled at 600°C, and the secondary tempering temperature is controlled at 560°C.

Example Embodiment

[0021] Example 3:

[0022] Melt the molten steel to control the mass percentage content of each element of the molten steel: C1.80, Si 1.20, Mn 0.80, Ni2.10, Cr 1.40, Mo 0.80, V 0.40, Ti 0.20, S≤0.03, P≤0.03, AL0.07 , CaSi0.20, the rest is Fe and unavoidable impurities; it is made by coarse-opening processing, diffusion annealing, normalizing and secondary tempering. Wherein, the diameter direction of the roll body allowance in the coarse-opening processing step is controlled at 10 mm; in the secondary tempering step, the primary tempering temperature is controlled at 580°C, and the secondary tempering temperature is controlled at 550°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a GVTi wear-resistant type semisteel roller. The GVTi wear-resistant type semisteel roller comprises the following components of, in percentage by mass, 1.60-2.00 parts of C, 0.80-1.60 parts of Si, 0.60-1.20 parts of Mn, 1.20-3.00 parts of Ni, 0.80-2.00 parts of Cr, 0.50-1.00 part of Mo, 0.10-0.60 parts of V, 0.10-0.30 parts of Ti, less than or equal to 0.03 parts of S, less than or equal to 0.03 parts of P, 0.05-0.10 parts of AL, 0.10-0.30 parts of CaSi, and the balance Fe and inevitable impurities. The invention also discloses a preparation method of the GVTI wear-resistant semisteel roller. According to the GVTi wear-resistant type semisteel roller and the preparation method thereof, through silicon/carbon ratio, the heat crack resistance of the roller is improved, the strength of the roller is further improved, and the tensile strength of the roller is more than or equal to 650 Mpa; the reasonable proportion of nickel, chromium, molybdenum, vanadium and titanium alloy is added, especially the vanadium and titanium alloy is added, so that the overall casting performance is further optimized, the good hardness from inside to outside can be ensured, the hardness of the roller reaches 55/70HSD, and the wear resistance of the final product of the roller can be improved by 20%-30%.

Description

technical field [0001] The invention belongs to the field of high-speed steel casting, and in particular relates to a GVTi wear-resistant semi-steel roll and a preparation method thereof. Background technique [0002] With the high-quality development of the iron and steel industry, major steel mills pay more attention to energy saving and consumption reduction, especially the semi-steel rolls often used in the primary and secondary rolling mills involved in H-beams and rods and wires. The material has not been obtained for a long time Good breakthrough, low wear resistance of the roll (hardness is generally 40~55HSD), poor thermal crack resistance (hardness difference between the roll surface and the bottom of the pass is generally ≥5HSD), short service life, etc., due to the influence of the roll change cycle It may form a deep crack and cause the roll to break and so on. Contents of the invention [0003] Purpose of the invention: The purpose of the invention is to pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/44C22C38/46C22C38/50C22C38/56B23P15/00C22C33/04C21D9/38
CPCB23P15/00C21D9/38C21D2211/004C21D2211/008C21D2211/009C22C33/04C22C38/02C22C38/04C22C38/06C22C38/44C22C38/46C22C38/50C22C38/56
Inventor 邵黎军范建中刘素琴李武
Owner 宜兴市国昌轧辊有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com