Waterborne salt spray-resistant epoxy primer

An epoxy primer and salt spray-resistant technology, applied in primers, epoxy resin coatings, coatings, etc., can solve problems such as solvent volatilization, human and environmental hazards, and incomplete drying, and achieve the effect of improving water resistance

Inactive Publication Date: 2019-09-27
山东海思蓝高分子材料有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of this invention is to solve the problem that the existing oil pipelines and storage tanks have higher and higher requirements for salt spray resistance. During the production and construction of oil-based paints, a large amount of solvents volatilize, which is harmful to the human body and the environment, and some have a long curing time. Winter 48 Due to the problem of incomplete drying within hours, a water-based salt spray resistant epoxy primer was designed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A water-based salt spray resistant epoxy primer, which mainly includes: A component and B component;

[0020] Among them, component A includes: 15 parts of low molecular weight epoxy emulsion, 20 parts of high molecular weight epoxy emulsion, 20 parts of water, 0 parts of leveling agent, 0 parts of drier, and 0 parts of polyurethane;

[0021] Among them, component B includes: 25 parts of curing agent, 20 parts of zinc powder, 0 parts of graphene, 5 parts of water, 0 parts of dispersant, 0 parts of organic bentonite, and 0 parts of defoaming agent.

[0022] The specific ratio of the A component to the B component is 1:1.

[0023] High hardness, poor adhesion, poor flexibility, average salt spray resistance.

Embodiment 2

[0025] Component A includes: 25 parts of low molecular weight epoxy emulsion, 30 parts of high molecular weight epoxy emulsion, 35 parts of water, 0.2 parts of leveling agent, 0.2 parts of drier, 0.2 parts of polyurethane;

[0026] Among them, component B includes: 35 parts of curing agent, 30 parts of zinc powder, 0.1 part of graphene, 5 parts of water, 0.2 part of dispersant, 0.1 part of organic bentonite, and 0.1 part of defoamer.

[0027] The specific ratio of the A component to the B component is 2:1.

Embodiment 3

[0029] Component A includes: 25 parts of low molecular weight epoxy emulsion, 30 parts of high molecular weight epoxy emulsion, 35 parts of water, 0.2 parts of leveling agent, 0.2 parts of drier, 0.2 parts of polyurethane;

[0030] Among them, component B includes: 35 parts of curing agent, 30 parts of zinc powder, 0.1 part of graphene, 5 parts of water, 0.2 part of dispersant, 0.1 part of organic bentonite, and 0.1 part of defoamer.

[0031] The specific ratio of the A component to the B component is 3:1.

[0032] Good flexibility, poor hardness, poor water resistance and smoke resistance, the effect is average.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses waterborne salt spray-resistant epoxy primer. The primer is prepared from a component A and a component B, wherein the component A comprises 15 to 55 parts of an epoxy emulsion with low molecular weight, 20 to 55 parts of an epoxy emulsion with high molecular weight, 20 to 60 parts of water, 0 to 1 part of a leveling agent, 0 to 2 parts of a drier, and 0 to 5 parts of polyurethane; the component B comprises 25 to 70 parts of a curing agent, 10 to 50 parts of zinc powder, 0 to 1 part of graphene, 5 to 30 parts of water, 0 to 2 parts of a dispersant, 0 to 2 parts of organic bentonite, and 0 to 3 parts of an antifoaming agent. The primer has the following beneficial effects: 1, the salt spray resistance of the epoxy primer prepared by adopting a natural drying technology can reach 1500 hours; 2, the production mode of existing traditional paint is changed, the water is used as a diluent, the discharge of pollution sources is reduced and the safety of production and transportation is improved; 3, water resistance is increased by 20% while the salt spray resistance is increased.

Description

technical field [0001] The invention relates to the field of epoxy primers, in particular to a water-based salt spray resistant epoxy primer. Background technique [0002] Oil pipelines (also called pipelines, pipelines) are composed of oil pipes and their accessories, and are equipped with corresponding oil pump units according to the needs of the process flow, designed and installed as a complete pipeline system to complete oil unloading and transportation Task. [0003] The oil pipeline system, that is, the pipeline system used to transport oil and petroleum products, is mainly composed of oil pipelines, oil stations and other auxiliary related equipment. For transportation equipment, compared with railway and highway oil transportation, which are also land transportation methods, pipeline oil transportation has the characteristics of large transportation volume, good airtightness, low cost and high safety factor. [0004] The pipes of oil pipelines are generally steel ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/10C09D7/20C09D7/61C09D7/62
CPCC08K2003/0893C08L2205/025C08L2205/03C09D5/002C09D5/106C09D7/20C09D7/61C09D7/62C09D163/00C08L63/00C08K3/08C08L75/04C08K3/042C08K9/00C08K3/346
Inventor 唐茂强
Owner 山东海思蓝高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com