A composite body pigment and filler with antirust and flame retardant properties and preparation method thereof

A technology of flame retardant properties and composites, applied in the field of composite pigments and fillers and its preparation, can solve problems such as performance needs to be improved, insufficient adhesion, environmental pollution, etc., to enhance market competitiveness and application range, and improve antirust performance , Expand the effect of high value-added applications

Active Publication Date: 2021-07-30
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the existing technology cannot use steel slag and montmorillonite on a large scale and with high added value, the filler pigments currently used contain a large amount of heavy metal oxides such as chromium, zinc, and lead, which will cause serious environmental pollution after entering the antirust coating, and the existing Body pigments and fillers have problems of single function, insufficient adhesion, high price and performance to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite body pigment and filler with antirust and flame retardant properties and preparation method thereof
  • A composite body pigment and filler with antirust and flame retardant properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Taking the preparation of product 100g of the present invention as an example, the used component and its mass ratio are:

[0033] Phosphoric acid solution 1.6%

[0034] Steel slag powder 32%

[0035] Graphene 1%

[0036] Cetyltrimethylammonium bromide 1.4%

[0037] Dilute hydrochloric acid solution 48%

[0038] Montmorillonite 16%

[0039] The mass fraction of the phosphoric acid solution is 86%; the steel slag micropowder is electric furnace drum slag micropowder, and its particle size is 25µm to 45µm; the graphene is analytically pure; the cetyltrimethylammonium bromide is Analytical purity; the mass fraction of the dilute hydrochloric acid solution is 3%; the montmorillonite is calcium-based montmorillonite.

[0040]Firstly, the phosphoric acid solution and the steel slag micropowder were mixed at room temperature with a constant temperature magnetic stirrer, the stirring speed was 800r / min, and the stirring time was 7h to obtain the porous steel slag micropowd...

Embodiment 2

[0045] Taking the preparation of product 100g of the present invention as an example, the used component and its mass ratio are:

[0046] Phosphoric acid solution 1.8%

[0047] Steel slag powder 28%

[0048] Graphene 3%

[0049] Cetyltrimethylammonium bromide 1.2%

[0050] Dilute hydrochloric acid solution 44%

[0051] Montmorillonite 22%

[0052] The mass fraction of the phosphoric acid solution is 82%; the steel slag micropowder is a mixture of hot slag micropowder and converter drum slag micropowder, and its particle size is 25µm to 45µm; the graphene is analytically pure; the hexadecyl Trimethylammonium bromide is of analytical grade; the mass fraction of the dilute hydrochloric acid solution is 6%; the montmorillonite is magnesium-based montmorillonite.

[0053] First, the phosphoric acid solution and the steel slag micropowder were mixed at room temperature with a constant temperature magnetic stirrer, the stirring speed was 950r / min, and the stirring time was 6h to...

Embodiment 3

[0058] Taking the preparation of product 100g of the present invention as an example, the used component and its mass ratio are:

[0059] Phosphoric acid solution 2%

[0060] Steel slag powder 16%

[0061] Graphene 2%

[0062] Cetyltrimethylammonium bromide 2%

[0063] Dilute hydrochloric acid solution 53%

[0064] Montmorillonite 25%

[0065] The mass fraction of the phosphoric acid solution is 80%; the steel slag micro-powder is a mixture of air-quenched slag micro-powder and electric furnace hot-splashing slag micro-powder, and its particle size is 25µm-45µm; the graphene is analytically pure; the hexadecane The base trimethylammonium bromide is of analytical grade; the mass fraction of the dilute hydrochloric acid solution is 5%; the montmorillonite is sodium-calcium montmorillonite.

[0066] Firstly, the phosphoric acid solution and the steel slag micropowder were mixed at room temperature with a constant temperature magnetic stirrer, the stirring speed was 1000r / min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite body pigment and filler with antirust and flame retardant properties and a preparation method thereof, belonging to the field of solid waste resource utilization. The pigment and filler include phosphoric acid solution, steel slag fine powder, graphene, cetyltrimethylammonium bromide, dilute hydrochloric acid solution and montmorillonite. The steel slag fine powder is one of hot stuffy slag fine powder, wind quenching slag fine powder, molten iron desulfurization slag fine powder, casting residual slag fine powder, converter hot slag fine powder, converter drum slag fine powder, electric furnace hot slag fine powder, electric furnace drum slag fine powder or more. The invention not only reduces the production cost of the existing body pigments and fillers by 30% to 50%, but also improves the antirust performance, flame retardancy and adhesion of the body pigments and fillers, and realizes the antirust performance, flame retardancy and high adhesion The integration of texture pigments and fillers has greatly enhanced the market competitiveness and application scope of texture pigments and fillers; expanded the high value-added applications of steel slag and montmorillonite, and realized the new idea of ​​"using waste to increase efficiency".

Description

technical field [0001] The invention belongs to the field of solid waste resource utilization, and in particular relates to a composite body pigment and filler with anti-rust and flame-retardant properties and a preparation method thereof. Background technique [0002] Steel slag is a solid waste generated in the steelmaking process, accounting for about 15% to 20% of the steelmaking output. The main components are CaO and Fe. 2 O 3 , Al 2 O 3 , SiO 2 , MgO, P 2 O 5 , MnO, SO 3 and a small amount of free calcium oxide, of which CaO (35.0% to 55.0%), Fe 2 O 3 (10.0%~35.0%), Al 2 O 3 The content of (2.0% to 12.0%) is relatively high. At present, the accumulation of a large amount of steel slag not only occupies valuable land, but also pollutes the surrounding environment and groundwater. In my country, there are a large number of montmorillonite composed of nanometer-thick silicate sheets, which mainly include calcium-based montmorillonite, sodium-based montmorillon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/08C09D5/18
CPCC08K3/346C08K3/36C08K9/04C08K9/12C08K13/06C08K2003/2206C08K2003/222C08K2003/2227C08K2003/2272C08K2201/003C09D5/084C09D5/18C08K3/042
Inventor 张浩龙红明宗志芳高青叶雯静张梦莉
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com