a mno x -mof-gr composite material and its preparation method and application

A mnox-mof-gr, composite material technology, applied in the field of composite materials, can solve problems such as poor formaldehyde removal effect, and achieve the effects of improving adsorption performance, increasing specific surface area, and low material cost

Active Publication Date: 2021-03-16
SICHUAN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the invention is to provide a kind of MnO x -MOF-Gr composite material and its preparation method and application solve the problem of poor formaldehyde removal effect of existing materials at room temperature, and can decompose low-concentration formaldehyde gas at room temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a mno <sub>x</sub> -mof-gr composite material and its preparation method and application
  • a mno <sub>x</sub> -mof-gr composite material and its preparation method and application
  • a mno <sub>x</sub> -mof-gr composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of MnO x -The preparation method of MOF-Gr-1 composite material, comprising:

[0031] (1) Preparation of Mn-MOFs material: 1.2g of manganese chloride tetrahydrate and 0.3g of terephthalic acid were fully dissolved in a mixture containing 3mL of water and 15mL of N,N dimethylformamide (DMF), and then the mixture was Heat water at 100-160°C for 1-5 hours, filter, wash and dry the reactant to obtain Mn-MOFs crystal material;

[0032] (2) Mix Mn-MOFs material with graphene dispersion: add 5mg graphene into 10mL deionized water and ultrasonically disperse for 10-30min to obtain graphene dispersion, then add Mn-MOFs into graphene dispersion and stir ultrasonically to disperse the mixture evenly;

[0033] (3) Preparation of oxidant solution: take 5g potassium permanganate and dissolve it in 40mL deionized water to ensure complete dissolution to obtain oxidant solution;

[0034] (4) Fully mix the mixed solution prepared in step (2) with the oxidant solution prepared i...

Embodiment 2

[0039] A kind of MnO x -The preparation method of the MOF-Gr-2 composite material is basically the same as the method in Example 1, the difference is that in step (2), the amount of graphene is 15mg. The yield of Example 2 was also 50%.

[0040] Such as figure 1 Shown, is the MnO prepared by Example 2 of the present invention x - The FT-IR spectrum of the MOF-Gr-2 composite material, qualitatively determined the surface groups of the catalyst, located at 3400cm in the figure -1 The peak is the infrared characteristic absorption peak of -OH, located at 500cm -1 The peak is the absorption peak of the Mn-O bond, which verifies the generation of manganese dioxide in the product. Located at 1620cm -1 , 1050cm -1 and 900cm -1 The infrared absorption peaks of corresponding to the C=C stretching vibration absorption peak in aromatics, the C-OH stretching vibration absorption peak in alkoxy groups and the C-O stretching vibration in epoxides, these representative oxygen-containi...

Embodiment 3

[0050] A kind of MnO x -The preparation method of the MOF-Gr-3 composite material is basically the same as the method in Example 1, the difference is that in step (2), the amount of graphene is 25 mg.

[0051] Adopt the same testing method as embodiment 1 to the MnO prepared by present embodiment 3 x -1.0mg / m of MOF-Gr-3 composite material 3 The low-concentration formaldehyde catalytic oxidation static test experiment, the specific implementation method is as follows:

[0052] Weigh 0.1g of the MnO prepared in Example 3 x -MOF-Gr-3 composite material, put it in a petri dish and seal the petri dish with plastic wrap and put it into a formaldehyde reactor. The volume of the reactor is 150L. Seal it, place the formaldehyde volatilization device in the reaction chamber, wait for it to volatilize completely, after reaching equilibrium, put the MnO x - The MOF-Gr-3 composite is fully exposed to the air containing formaldehyde in the reactor.

[0053] Measure the MnO prepared by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
clearance rateaaaaaaaaaa
clearance rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a MnO x ‑MOF‑Gr composite material and its preparation method and application, the method comprises: (1) dissolving manganese chloride tetrahydrate and p-benzoic acid in a mixed solution of water and N,N dimethylformamide, at 100~ Hydrothermal reaction at 160°C, post-treatment after the reaction, to obtain Mn-MOFs crystal material; (2) adding the Mn-MOFs crystal material to the graphene dispersion liquid, and dispersing evenly; (3) adding the Mn-MOFs crystal material obtained in step (2) The mixed liquid and the aqueous oxidant solution are mixed and reacted at 20-60°C to obtain MnO x ‑MOF‑Gr composites. The composite material prepared by the invention has a high specific surface area, is rich in surface adsorbed oxygen species, can quickly and effectively degrade low-concentration formaldehyde at room temperature, and its preparation process is simple, energy-saving, does not add any precious metals, and the material cost is low. capable of mass production.

Description

technical field [0001] The invention relates to a composite material, in particular to a MnO x -MOF-Gr (manganese oxide-metal organic framework compound-graphene) composite material and its preparation method and application. Background technique [0002] With the wide application of formaldehyde as an industrial raw material in interior furniture materials and car interior decoration materials in modern life, the problem of formaldehyde pollution in the indoor environment is also becoming more and more serious. Formaldehyde is very harmful to the human respiratory system. It can irritate the throat and be accompanied by symptoms such as nausea and vomiting. Long-term exposure to formaldehyde may even cause cancer. [0003] At present, there are two main methods that have been practically applied in the field of indoor air purification: ① using porous materials such as activated carbon for physical adsorption; ② using noble metal materials for catalytic oxidation. For exam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/32B01J35/10B01D53/86B01D53/72
CPCB01J31/32B01D53/8668B01J2531/72B01J2531/0213B01J35/615B01J35/633B01J35/647
Inventor 陈金伟王瑞林王刚陈旺
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com