Nylon elastomer nano composite material and preparation method thereof

A technology of nanocomposite materials and nylon elastomers, applied in the field of nanocomposite materials, can solve the problems of polyamide failing to enter the interlayer in time, product performance impact, etc.

Active Publication Date: 2019-09-13
INST OF CHEM CHINESE ACAD OF SCI
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method is simple and the production cost is low, but this method is to add montmorillonite mud after polyamide melting, which will cause the montmorillonite mud to be completely mixed with the copolymer in the future, and the water between the layers will be gasified due to high temperature. As a result, the polyamide failed to enter the interlayer in time. At the same time, the energy generated only by water vaporization was not enough to completely peel off the montmorillonite layer, so a completely peeled composite material could not be obtained, and its product performance was greatly affected. influences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nylon elastomer nano composite material and preparation method thereof
  • Nylon elastomer nano composite material and preparation method thereof
  • Nylon elastomer nano composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] In this embodiment, the mass ratio of nanomaterials to nylon elastomer is 2:100, the nylon elastomer is PA6 series, the mass ratio of PA6 to polyether block is 95:5, and the liquid medium used is water. The auxiliary agent is benzalkonium bromide, the nanomaterial used is layered nano-montmorillonite, and the anti-aging agent used is tris(2,4-di-tert-butylphenyl) phosphite, and the nanocomposite is prepared according to the following method Material:

[0103] (1) Stir the liquid medium, and at the same time add nanomaterials at a speed of 5g / min for continuous stirring and disperse evenly, and the weight ratio of liquid medium to nanomaterials is 20:1;

[0104] (2) Add additives in batches or at a time to the continuously stirring solution of step (1) at a speed of 0.1g / min to obtain a paste, the consistency of which is 66mm, and the additives and nanomaterials The weight ratio is 10:1;

[0105] (3) the paste obtained in step (2) is mixed with nylon elastomer to obtai...

Embodiment 2

[0110] In this embodiment, the mass ratio of nanomaterials to nylon elastomer is 10:100, the nylon elastomer is PA66 series, the mass ratio of PA66 to polyether block is 95:5, and the liquid medium used is trifluoro Acetic acid and water, the mass ratio of trifluoroacetic acid and water is 2:98, the auxiliary agent that adopts is polyacrylic acid and sodium stearyl sulfate, and weight ratio is 1:1, and the nanometer material that adopts is sepiolite, adopts The anti-aging agent is antioxidant 1035, and the nanocomposite material is prepared according to the following method:

[0111] (1) Stir the liquid, and at the same time add nanomaterials at a speed of 10g / min for continuous stirring to disperse evenly, and the weight ratio of the liquid medium to the nanomaterials is 100:1;

[0112] (2) Add auxiliary agent to the continuous stirring solution of step (1) with the speed of 5g / min, obtain paste, the consistency of described paste is 16mm, and the weight ratio of described au...

Embodiment 3

[0118] In this embodiment, the mass ratio of nanomaterials to nylon elastomer is 0.1:100, the nylon elastomer is PA12 series, the mass ratio of PA12 to polyether block is 95:5, the liquid medium used is water, and The auxiliary agent is polyamide epichlorohydrin resin and its oligomers, and the nanomaterials used are kaolin and sepiolite, and the mass ratio is 3:7. The nanocomposite material is prepared according to the following method:

[0119] (1) Stir the liquid medium, and at the same time add nanomaterials at a speed of 0.05g / min for continuous stirring to disperse evenly, and the weight ratio of the liquid medium to the nanomaterials is 50:1;

[0120] (2) Add additives to the continuous stirring solution of step (1) at a speed of 5g / min to obtain a paste, the consistency of the paste is 49mm, and the weight ratio of the additives to nanomaterials is 0.1 :1;

[0121] (3) the paste obtained in step (2) is mixed with nylon elastomer to obtain a premix;

[0122] (4) feedi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Consistencyaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of nano composite materials and in particular to a nylon elastomer nano composite material and a preparation method thereof. The nano composite material is preparedfrom a premix through melting blending, and the premix is prepared from a nano material which is combined with a liquid medium and is adhered to nylon elastomer granules and fills space among the nylon elastomer granules. The preparation method comprises the following steps: mixing the liquid medium with the nano material so as to obtain an ointment, and pasting the ointment to surfaces of the nylon elastomer granules, and carrying out melting blending, so as to obtain the nano composite material. The nano composite material provided by the invention has excellent toughness, and in addition isshort in process procedure, low in cost and applicable to popularization and use.

Description

technical field [0001] The invention relates to the field of nanocomposite materials, in particular to a nylon elastomer nanocomposite material and a preparation method thereof. Background technique [0002] In the existing technology, nanomaterials and polymers are often mixed and extruded to form composite materials. Although the tensile strength of such composite materials has been improved, due to problems such as poor compatibility between nanomaterials and polymers, this type of material The impact resistance performance is generally not high. [0003] In order to solve the above problems, methods such as intercalation in-situ polymerization are often used to make the polymer react between the layers of nanomaterials to improve the impact resistance of the composite material. However, this process takes a long time, the polymerization reaction conditions are harsh, and the solvent is not easy. Recycling will bring derivative problems such as environmental pollution. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/02C08L77/06C08K3/34C08K3/02C08K3/24C08K5/098C08K3/04C08K3/18C08J3/20C08J5/00
CPCC08J3/2053C08J5/005C08J2377/02C08J2377/06C08J2405/00C08J2433/02C08K3/18C08K3/24C08K3/346C08K5/098C08K2003/023C08K2003/026C08K2201/011C08K2201/014C08K3/042
Inventor 马永梅庄亚芳向前郑鲲张京楠曹新宇尚欣欣
Owner INST OF CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com