A kind of pp nanocomposite material and preparation method thereof

A nano-composite material and nano-material technology, applied in the field of PP nano-composite materials and its preparation, can solve the problems of polyamide not entering the interlayer in time and affecting product performance, and achieve the goals of suitable promotion, prevention of agglomeration, and improvement of impact performance Effect

Active Publication Date: 2021-09-07
INST OF CHEM CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method is simple and the production cost is low, but this method is to add montmorillonite mud after polyamide melting, which will cause the montmorillonite mud to be completely mixed with the copolymer in the future, and the water between the layers will be gasified due to high temperature. As a result, the polyamide failed to enter the interlayer in time. At the same time, the energy generated only by water vaporization was not enough to completely peel off the montmorillonite layer, so a completely peeled composite material could not be obtained, and its product performance was greatly affected. influences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pp nanocomposite material and preparation method thereof
  • A kind of pp nanocomposite material and preparation method thereof
  • A kind of pp nanocomposite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0101] In this embodiment, the mass ratio of nanomaterials to polypropylene is 20:100, the liquid medium used is water, the auxiliary agent used is cetylpyridinium chloride, and the nanomaterials used are layered nano-montmorillonite. Nanocomposites were prepared as follows:

[0102] (1) Stir the liquid medium, and at the same time add nanomaterials at a speed of 5.6g / min for continuous stirring to disperse evenly, and the weight ratio of liquid medium to nanomaterials is 20:1;

[0103] (2) Add additives in batches or once to the continuous stirring solution of step (1) at a speed of 0.1g / min to obtain a paste, the consistency of which is 32mm, the additives and nanomaterials The weight ratio is 10:1;

[0104] (3) the paste obtained in step (2) is mixed with polypropylene to obtain a premix;

[0105] (4) feeding the premixed material in step (3) into a screw extruder from a pressureless feeding zone, melt blending and performing subsequent processing to obtain a nanocomposit...

Embodiment 2

[0109] In this embodiment, the mass ratio of nanomaterials to polypropylene is 10:100, the liquid medium used is acetone and water, and the mass ratio of acetone to water is 7:93, and the auxiliary agents used are polyacrylic acid and polymarine Toic anhydride, the weight ratio is 1:1, the nanomaterial that adopts is kaolin, prepares nanocomposite material according to the following method:

[0110] (1) Stir the liquid, and at the same time add nanomaterials at a speed of 10g / min for continuous stirring to disperse evenly, and the weight ratio of the liquid medium to the nanomaterials is 100:1;

[0111] (2) add auxiliary agent in the continuous stirring solution of step (1) with the speed of 0.5g / min, obtain paste, the consistency of described paste is 15mm, and the weight ratio of described auxiliary agent and nanometer material is 50:1;

[0112] (3) the paste obtained in step (2) is mixed with polypropylene to obtain a premix;

[0113] (4) feeding the premixed material in ...

Embodiment 3

[0117] In this example, the mass ratio of nanomaterials to polypropylene is 0.1:100, the liquid medium used is water, the auxiliary agent used is sodium alginate, the nanomaterials used are nano-montmorillonite and kaolin, and the mass ratio is 8 : 2, prepare nanocomposite material according to the following method:

[0118] (1) Stir the liquid medium, and at the same time add nanomaterials at a speed of 0.01g / min for continuous stirring to disperse evenly, and the weight ratio of liquid medium to nanomaterials is 50:1;

[0119] (2) Add auxiliary agent to the continuous stirring solution of step (1) at a speed of 15g / min to obtain a paste, the consistency of the paste is 26mm, and the weight ratio of the auxiliary agent to nanomaterial is 0.1 :1;

[0120] (3) the paste obtained in step (2) is mixed with polypropylene to obtain a premix;

[0121] (4) feeding the premixed material in step (3) into an internal mixer, melt blending and performing subsequent processing to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of nanocomposite materials, in particular to a polypropylene nanocomposite material and a preparation method thereof, wherein the nanocomposite material is prepared by melt-blending a premixed material, and the premixed material is prepared from The nanometer material combined with the liquid medium is formed by filling and adhering between polypropylene particles; when the nanocomposite material is within a certain strength and / or stiffness range, the toughness increases with the increase of the strength and / or stiffness. The preparation method comprises mixing the liquid medium and the nano material to obtain a paste, adhering the paste to the surface of polypropylene particles and performing melt blending to obtain a nanocomposite material. The nanocomposite material provided by the invention has excellent toughness, short process flow and low cost, and is suitable for popularization and use.

Description

technical field [0001] The invention relates to the field of nanocomposite materials, in particular to a PP nanocomposite material and a preparation method thereof. Background technique [0002] In the existing technology, nanomaterials and polymers are often mixed and extruded to form composite materials. Although the tensile strength of such composite materials has been improved, due to problems such as poor compatibility between nanomaterials and polymers, this type of material The impact resistance performance is generally not high. [0003] In order to solve the above problems, methods such as intercalation in-situ polymerization are often used to make the polymer react between the layers of nanomaterials to improve the impact resistance of the composite material. However, this process takes a long time, the polymerization reaction conditions are harsh, and the solvent is not easy. Recycling will bring derivative problems such as environmental pollution. [0004] Pate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08J3/20C08J5/00C08K3/34C08K3/22C08K3/24C08K3/04
CPCC08J3/2053C08J5/005C08J2323/12C08J2405/04C08J2405/08C08J2433/02C08J2435/00C08K3/22C08K3/24C08K3/34C08K2003/2224C08K2201/011C08K2201/014C08K3/042
Inventor 马永梅庄亚芳郑鲲张京楠曹新宇尚欣欣
Owner INST OF CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com