PVC resin composition with high pressure resistance and excellent plasticity, and PVC pipe prepared therefrom

A technology of PVC resin and PVC pipe, applied in the field of plastic processing, can solve the problems such as the unsatisfactory pressure resistance and internal pressure resistance of pipes, and achieve the promotion of plasticization performance and plasticization uniformity, excellent compression resistance and processing performance, and easy The effect of extrusion processing

Inactive Publication Date: 2019-09-06
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The impact strength and hydrostatic strength of the PVC-U pipe have been significantly improved, but the pressure resistance of the entire pipe, especially the internal pressure resistance, is still not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC resin composition with high pressure resistance and excellent plasticity, and PVC pipe prepared therefrom

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The PVC resin composition with high pressure resistance and excellent plasticity described in the present embodiment comprises the following components in an amount:

[0037] PVC resin 100kg;

[0038] Mercaptan methyl tin stabilizer 0.8kg;

[0039] Processing aid 1.5kg;

[0040] MBS resin 2.0kg;

[0041] Methyl methacrylate-styrene copolymer resin (9:1) 3.0kg;

[0042] Calcium stearate 0.5kg;

[0043] Paraffin 0.4kg;

[0044] PE wax 0.3kg.

Embodiment 2

[0046] The PVC resin composition with high pressure resistance and excellent plasticity described in the present embodiment comprises the following components in an amount:

[0047] PVC resin 100kg;

[0048] Mercaptan methyl tin stabilizer 0.9kg;

[0049] Processing aid 1.3kg;

[0050] MBS resin 2.5kg;

[0051] Methyl methacrylate-styrene copolymer resin (9:1) 4.5kg;

[0052] Calcium stearate 0.6kg;

[0053] Paraffin 0.5kg;

[0054] PE wax 0.3kg.

Embodiment 3

[0056] The PVC resin composition with high pressure resistance and excellent plasticity described in the present embodiment comprises the following components in an amount:

[0057] PVC resin 100kg;

[0058] Mercaptan methyl tin stabilizer 1.0kg;

[0059] Processing aid 1.0kg;

[0060] MBS resin 3.0kg;

[0061] Methyl methacrylate-styrene copolymer resin (9:1) 6.0kg;

[0062] Calcium stearate 0.8kg;

[0063] Paraffin 0.6kg;

[0064] PE wax 0.4kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of plastic processing, concretely relates to a PVC resin composition with a high pressure resistance and an excellent plasticity, and further discloses a PVC pipe prepared therefrom. The PVC resin composition with high pressure resistance and excellent plasticity adopts PVC resin, a PVC stabilizer, methyl methacrylate-styrene copolymer resin, toughnessmodified resin, a processing aid, calcium stearate, paraffin and PE wax as processing raw materials, and the coordination effects of all above components are used to effectively promote the plasticizing performance and plasticizing uniformity of the pipe and effectively improve the internal pressure resistance of the pipe. The methyl methacrylate-styrene copolymer resin and MBS resin can especially produce good synergistic effects, so the plasticization of the whole system is further promoted, and the internal pressure resistance and the processing plasticity of the entire PVC pipe are effectively improved.

Description

technical field [0001] The invention belongs to the technical field of plastic processing, specifically relates to a PVC resin composition with high pressure resistance and excellent plasticity, and further discloses a PVC pipe prepared by the composition. Background technique [0002] Polyvinyl chloride (PVC, Polyvinyl chloride) is a polymer formed by the polymerization of vinyl chloride monomer in peroxide, azo compound and other initiators, or under the action of light and heat according to the mechanism of free radical polymerization. PVC used to be the world's largest general-purpose plastic. It is used in building materials, industrial products, daily necessities, floor leather, floor tiles, artificial leather, pipes, wires and cables, packaging films, bottles, foaming materials, sealing materials, fibers, etc. widely used. [0003] As we all know, due to its excellent chemical stability, excellent electrical insulation, good flexibility and colorability, PVC pipes ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L33/12C08L51/04C08L91/06C08L23/06C08K5/098C08K5/58
CPCC08L27/06C08L2203/18C08L2205/035C08L2205/06C08L33/12C08L51/04C08L91/06C08L23/06C08K5/098C08K5/58
Inventor 刘浩刘容德王晶张新华王晓敏王秀丽孙丽朋高磊
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products