Environmental protection composite gold beneficiation collector

A collector and composite technology, applied in flotation, solid separation and other directions, can solve the problems of easy loss of fine-grained gold, low recovery rate of beneficiation, low recovery rate of gold-sulfur separation, etc. Good yield and selectivity

Active Publication Date: 2020-12-29
YANTAI MOUJIN MINING
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to solve the problems of low fine-grained and fine-grained gold beneficiation recovery rate and the easy loss of fine-grained gold during separation of gold with high sulfur content, and low recovery rate of gold-sulfur separation, and to provide a high-capacity collector. , good selectivity, small dosage and good foaming environment-friendly composite gold beneficiation collector

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental protection composite gold beneficiation collector
  • Environmental protection composite gold beneficiation collector
  • Environmental protection composite gold beneficiation collector

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The environment-friendly composite gold mineral processing collector of the present embodiment comprises the following proportioning components in parts by weight: 35 parts of main collectors, 34 parts of secondary collectors, and 20 parts of water;

[0039] Wherein, the main collector is composed of the following raw materials in parts by weight: 45 parts of dibutyl dithiophosphate, 28 parts of isooctyl thioglycolate, 12 parts of ethyl thiocarbamate, 8 parts of sodium oleate, 9 parts of dihydrocarbyl thionocarbamate; Described secondary collector is made up of the raw material of following parts by weight: C 7 33 parts of hydroxamic acid, 28 parts of polyacrylamide, 13 parts of isooctyl phosphate.

[0040] The preparation method of collector in the present embodiment comprises the following steps:

[0041] ① Dissolve sodium oleate and dihydrocarbylthionocarbamate into the thiourethane solution in turn, and stir and react for 5.2 hours at a temperature of 70°C to prepare...

Embodiment 2

[0053] The environment-friendly composite gold mineral processing collector of the present embodiment comprises the following proportioning components in parts by weight: 40 parts of main collector, 22 parts of secondary collector, and 15 parts of water;

[0054] Wherein, the main collector is composed of the following raw materials in parts by weight: 47 parts of diisopropyl dithiophosphate, 25 parts of isooctyl mercaptoacetate, 10 parts of ethyl thiocarbamate, 9 parts of sodium oleate , 8 parts of dihydrocarbylthionocarbamate; the secondary collector consists of the following raw materials in parts by weight: 35 parts of C8 hydroxamic acid, 27 parts of polyacrylamide, and 11 parts of isooctyl phosphate.

[0055] The preparation method of collector in the present embodiment comprises the following steps:

[0056] ① Dissolve sodium oleate and dihydrocarbylthionocarbamate into the thiourethane solution in sequence, and stir and react for 5 hours at a temperature of 71°C to prep...

Embodiment 3

[0068] The environment-friendly composite gold mineral processing collector of the present embodiment comprises the following proportioning components in parts by weight: 42 parts of main collectors, 30 parts of secondary collectors, and 17 parts of water;

[0069] Wherein, the main collector is composed of the following raw materials in parts by weight: 50 parts of dibutyl dithiophosphate, 20 parts of isooctyl thioglycolate, 9 parts of ethyl thiocarbamate, 7 parts of sodium oleate, 9 parts of dihydrocarbylthionocarbamate; the secondary collector consists of the following raw materials in parts by weight: 31 parts of C9 hydroxamic acid, 27 parts of polyacrylamide, and 15 parts of isooctyl phosphate.

[0070] The preparation method of collector in the present embodiment comprises the following steps:

[0071] ① Dissolve sodium oleate and dihydrocarbylthionocarbamate into the thiourethane solution in turn, and stir and react for 5.5 hours at a temperature of 75°C to prepare a mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel environment-friendly composite collector for gold ore dressing. This novel environment-friendly composite gold beneficiation collector comprises the following components: 35-45 parts of the main collector, 20-35 parts of the secondary collector, and 15-20 parts of water; wherein, the main collector consists of the following weight Raw material composition in parts: 45‑50 parts of dihydrocarbyl dithiophosphate, 20‑28 parts of isooctyl mercaptoacetate, 8‑12 parts of thiourethane, 5‑9 parts of sodium oleate, dihydrocarbyl thionocarbamate 8-10 parts of acid ester; the secondary collector consists of the following raw materials in parts by weight: 30-35 parts of alkyl hydroxamic acid, 26-28 parts of polyacrylamide, 10-15 parts of isooctyl phosphate. The new environment-friendly composite gold mineral processing collector of the present invention has the characteristics of strong collecting ability, good selectivity, small dosage and foaming for gold minerals, and effectively solves the problem of low recovery rate of fine-grained and fine-grained gold. And the problems of easy loss of fine-grained gold and low recovery rate of gold-sulfur separation during the separation of gold with high sulfur content.

Description

technical field [0001] The invention relates to an environment-friendly composite gold beneficiation collector, which belongs to the technical field of nonferrous metal mining. Background technique [0002] Flotation is the most widely used mineral comprehensive recovery technology. In principle, it can separate various minerals. It is a high-efficiency "separation process". Most gold ore dressings in the world are recovered by flotation. The flotation process Collectors are usually added to improve gold recovery. [0003] Gold ore resources are important mineral resources. With the increasing demand, the easy-to-handle gold ore resources are getting less and less, while the refractory gold ore resources are getting more and more attention. Refractory gold ore resources mainly include carbon-bearing gold ore, fine-grained embedded gold ore, gold-bearing polymetallic sulfide ore, and arsenic-containing gold sulfide ore. For the fine-grained embedded gold ore in the refracto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B03D1/014B03D103/02B03D101/02
CPCB03D1/014B03D2203/025B03D2201/02
Inventor 高绪广张尚美杨志国
Owner YANTAI MOUJIN MINING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com