A kind of polyoxymethylene monofilament and its preparation method and polyoxymethylene wear-resistant rope for ecological fence

A technology of polyoxymethylene and monofilament, which is applied in the manufacture of rayon, conjugated synthetic polymer rayon, applications, etc., can solve the problems of poor comprehensive performance of ropes and ropes, difficulty in adapting to the development requirements of ecological fence breeding, etc. Achieve the effects of improving toughness and knotting strength, good spinnability and comprehensive performance, and improving flow uniformity

Active Publication Date: 2022-02-08
EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The comprehensive performance of existing ropes and rope wires is relatively poor, and it is difficult to adapt to the development requirements of ecological fence breeding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A polyoxymethylene monofilament is made of the following components by weight:

[0035] N60520922 polyoxymethylene 100 parts (molecular weight 30 ~ 35W), 8842 polyethylene octene copolymer elastomer 5 parts (melt index 0.5g / 10min ~ 1.0g / 10min), SJ-4 nano silicon dioxide 0.5 parts (particle size range 3nm-15nm), 0.1 part of antioxidant 1010, 0.1 part of auxiliary antioxidant 168, 0.1 part of FSQY lubricant silicone powder (organic silicon content is 65-100%); the diameter of the polyoxymethylene monofilament is 0.1 mm.

[0036] A preparation method of the polyoxymethylene monofilament, comprising the following steps:

[0037] According to the ratio, polyoxymethylene, polyvinyl octene copolymerized elastomer, nano silicon dioxide, stabilizer (antioxidant, secondary antioxidant), lubricant are pre-mixed, and then poured into a high-speed kneader, Knead at a high speed for 30-60 minutes at a speed of 750r / min-800r / min, and raise the temperature of the mixture in the high-...

Embodiment 2

[0045] A polyoxymethylene monofilament is made of the following components by weight:

[0046] 100 parts of MC90 polyoxymethylene (molecular weight is 30~35W), 10 parts of 6102 polyethylene octene copolymer elastomer (melt index is 0.5g / 10min~1.0g / 10min), 2 parts of VK-SP15 nano silicon dioxide (particle size range 3nm-15nm), 0.5 part of antioxidant 1010, 0.5 part of auxiliary antioxidant 168, 0.5 part of HNC-100 lubricant silicone powder (organic silicon content is 65~100%); the diameter of the polyoxymethylene monofilament 0.2mm.

[0047] The preparation method of the polyoxymethylene monofilament is the same as in Example 1.

[0048] A method for preparing a polyoxymethylene wear-resistant rope for ecological fences prepared from the polyoxymethylene monofilament, comprising the following steps: using a plying machine to first twist the polyoxymethylene monofilament with an internal twist of 8T / m to obtain S twist Polyoxymethylene rope strands in the same direction; 8 S-t...

Embodiment 3

[0050] A polyoxymethylene monofilament is made of the following components by weight:

[0051] 100 parts of 300PNC polyoxymethylene (molecular weight is 30~35W), 15 parts of 8150 polyethylene octene copolymer elastomer (melt index is 0.5g / 10min~1.0g / 10min), 5 parts of S01W nano silicon dioxide (particle size range is 5nm -30nm), 1 part of antioxidant 1010, 1 part of secondary antioxidant 168, 0.5 part of HZTL lubricant silicone powder (organic silicon content is 65-100%); the diameter of the polyoxymethylene monofilament is 1 mm.

[0052] The preparation method of the polyoxymethylene monofilament is the same as in Example 1.

[0053] A method for preparing a polyoxymethylene wear-resistant rope for ecological fences prepared from the polyoxymethylene monofilament, comprising the following steps: using a plying machine to first twist the polyoxymethylene monofilament with an internal twist of 8T / m to obtain S twist Polyoxymethylene rope strands in the same direction; through ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle sizeaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyoxymethylene monofilament, which is made of the following components in parts by weight: 100 parts of polyoxymethylene, 5-25 parts of polyethylene octene copolymerized elastomer, 0.5-10 parts of nano silicon dioxide, anti-oxidation 0.1-1 part of anti-oxidant, 0.1-1 part of antioxidant, 0.1-0.5 part of lubricant. The invention also discloses a polyoxymethylene wear-resistant rope for ecological fences prepared from the polyoxymethylene monofilament. The obtained rope has the advantages of good safety, low price, excellent wear resistance and high breaking strength, and has a certain Antibacterial antifouling effect.

Description

technical field [0001] The invention belongs to the technical field of fishing materials, and in particular relates to a polyoxymethylene monofilament for fishing and a preparation method thereof, and a polyoxymethylene wear-resistant rope for an ecological fence. Background technique [0002] The ecological fence breeding mode is an effective way to adjust the structure to adapt to the transformation of aquaculture in my country after the cage culture, and to improve the quality and efficiency of the aquaculture industry. In the field of fishery, a product made of twisted strands with a diameter greater than 4mm is called a rope, and the rope is one of the essential materials for ecological fence farming. At present, fishery synthetic fibers are constantly receiving national and international marine fishery research attention. Fishery synthetic fibers provide a good choice for the selection or research and development of ecological fence culture, culture cages, fishing gear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/16D01F8/06D01F1/10D07B1/02
CPCD01F8/16D01F8/06D01F1/10D01F1/103D07B1/02D07B2201/1044D07B2201/2009D07B2205/2035D07B2401/2065D07B2501/2038
Inventor 闵明华王鲁民曾毅成刘永利王磊李子牛
Owner EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com