Silicon carbide anti-skinning castable and preparation method thereof
A castable and anti-skin technology, applied in the field of refractory materials, can solve the problems of large explosion-proof fiber gaps, easy erosion of castables, infiltration of external substances, etc., so as to reduce labor intensity, avoid surface skinning, and reduce friction. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] Silicon carbide anti-skinning castable, the castable is prepared from the following raw materials in parts by weight: 20 parts of burnt gemstone brick waste, 18 parts of corundum brick waste, 16 parts of aluminum magnesium spinel brick waste, 7 parts of silicon carbide powder, micro 6 parts of silicon powder, 8 parts of alumina powder, 9 parts of calcium aluminate cement, 6 parts of silicon nitride powder, 0.1 part of explosion-proof fiber, 1 part of high temperature binder, 0.5 part of water reducer, 6 parts of water;
[0039] The high temperature adhesive is prepared by the following steps:
[0040] Step S1, add dimethyl silicone resin and silicone resin to the reaction kettle with agitator, heat to 50-55°C at the same time, set the stirring speed to 1000-1200r / min, and then add emulsifier while stirring After continuing to stir for 15 minutes, set the rotation speed to 1500-2000r / min, and add distilled water to the reaction kettle, and continue to stir for 10 minutes...
Embodiment 2
[0061] Silicon carbide anti-skinning castable, the castable is prepared from the following raw materials in parts by weight: 22 parts of burnt gemstone brick waste, 20 parts of corundum brick waste, 18 parts of aluminum magnesium spinel brick waste, 9 parts of silicon carbide powder, micro 8 parts of silicon powder, 10 parts of alumina powder, 10 parts of calcium aluminate cement, 7 parts of silicon nitride powder, 0.15 parts of explosion-proof fiber, 1.5 parts of high-temperature binder, 0.5 parts of water reducing agent, and 7 parts of water;
Embodiment 3
[0063] Silicon carbide anti-skinning castable, the castable is prepared from the following raw materials in parts by weight: 23 parts of burnt gemstone brick waste, 21 parts of corundum brick waste, 19 parts of aluminum magnesium spinel brick waste, 10 parts of silicon carbide powder, micro 9 parts of silicon powder, 12 parts of alumina powder, 10.5 parts of calcium aluminate cement, 7.5 parts of silicon nitride powder, 0.2 parts of explosion-proof fiber, 1.5 parts of high-temperature binder, 0.55 parts of water reducing agent, and 8 parts of water;
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com