Anion generating agent, white top-coating and preparation methods

A negative ion generating agent, white technology, applied in the field of coatings, can solve the problems of affecting the coating effect, not easy to disperse and agglomerate, affecting the use effect of the negative ion generating agent, etc. low effect

Inactive Publication Date: 2019-06-21
江苏六杯茶健康科技有限公司
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, during the use of the above-mentioned coating, due to the nano-powder material contained, there will be problems that the nano-powder material is not easy to disperse and agglomerate when the nano-powder material is dispersed in the coating during use. It will affect the coating effect of the paint, and on the other hand, it will also affect the use effect of the negative ion generator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion generating agent, white top-coating and preparation methods
  • Anion generating agent, white top-coating and preparation methods

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] In the present embodiment, the negative ion generating agent is prepared by the following raw materials in terms of mass percentage: 8wt% of hydrous magnesium-rich silicate (attapulgite), 30wt% of magnesium-rich polar material, and 62wt% of amorphous silicon dioxide; Wherein, the magnesium-rich polar material is composed of magnesium-containing silicate and polar ore material, and in the magnesium-rich polar material, the mass ratio of magnesium-containing silicate and polar ore material is 1:2 ;

[0052] In the present embodiment, the magnesium-containing silicate includes the following raw materials in terms of mass percentage of magnesium-containing silicate: 30 wt% of fibrous hydrous magnesium silicate (sepiolite), hydrous magnesium silicate (talc powder) 70wt%; the polar ore material, in terms of mass percentage of the polar ore material, includes the following raw materials: 2wt% labradorite, 15wt% fluorite, 7wt% amazonite, 11wt% turquoise, alabaster 15wt%, Lvbil...

Embodiment 2

[0071] In the present embodiment, the negative ion generating agent is prepared by the following raw materials in terms of mass percentage: 10wt% of hydrous magnesium-rich silicate (attapulgite), 25wt% of magnesium-rich polar material, and 65wt% of amorphous silicon dioxide; Wherein, the magnesium-rich polar material is composed of magnesium-containing silicate and polar ore material, and in the magnesium-rich polar material, the mass ratio of magnesium-containing silicate and polar ore material is 1:4 ;

[0072] In this embodiment, the magnesium-containing silicate, in terms of mass percentage of the magnesium-containing silicate, is composed of the following raw materials: 40 wt% of fibrous hydrous magnesium silicate (sepiolite), hydrous magnesium silicate ( Talcum powder) 60wt%; In the polar ore material, the mass percentage of the polar ore material includes the following raw materials: 5% labradorite, 9% fluorite, 8% amazonite, 7% turquoise, white Tridacna 5.5%, red smel...

Embodiment 3

[0091] In the present embodiment, the negative ion generating agent is prepared by the following raw materials in terms of mass percentage: 20wt% of hydrous magnesium-rich silicate (attapulgite), 36wt% of magnesium-rich polar material, and 44wt% of amorphous silicon dioxide; Wherein, the magnesium-rich polar material is composed of magnesium-containing silicate and polar ore material, and in the magnesium-rich polar material, the mass ratio of magnesium-containing silicate and polar ore material is 2:5 ;

[0092] In the present embodiment, the magnesium-containing silicate includes the following raw materials in terms of mass percentage of magnesium-containing silicate: 60 wt% of fibrous hydrous magnesium silicate (sepiolite), hydrous magnesium silicate (talc powder) 40wt%; the polar ore material, in terms of the mass percentage of the polar ore material, includes the following raw materials: 10% of labradorite, 14% of fluorite, 13.5% of amazonite, 10.5% of turquoise, and gian...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to an anion generating agent, a white top-coating and preparation methods. The anion generating agent is mainly prepared from raw materials as follows: hydrous magnesium-rich silicate, a magnesium-rich polar material and armorphous silicon dioxide, wherein the magnesium-rich polar material contains magnesium-containing silicate and a polar ore material. The anion generating agent can produce anions, and has the beneficial effects of purifying air, removing aldehyde, killing bacteria and improving air quality.

Description

technical field [0001] The invention relates to a negative ion generating agent, a white finish paint and a preparation method, belonging to the field of paint. Background technique [0002] With the improvement of living standards, traditional common building materials can no longer meet people's needs, and research on materials with healthy environmental functions has become a new direction for the development of building materials. Especially the quality of indoor air quality is directly related to the physiological health of the human body, and the negative ions in the indoor air are called "air vitamins", which have the functions of fresh air, eliminating odors and antibacterial effects; appropriately increasing the concentration of negative ions in the indoor air The significant impact of concentration on human health, longevity and ecology has been confirmed by domestic and foreign medical experts and scientific workers. [0003] In the prior art, the concentration o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/61C09D133/00C09D5/16
Inventor 宋怡锟夏学进史仲广
Owner 江苏六杯茶健康科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com