Formaldehyde-free building paint and preparation method thereof

A construction and coating technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve the problems of slow volatilization of formaldehyde, injury, pollution in homes and public places, etc., achieve good bacteriostasis, easy operation, Not easy to fall off effect

Inactive Publication Date: 2019-06-18
CHINA CONSTR SEVENTH ENG BUREAU THE SECOND CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these environmentally-friendly latex paints cannot be directly painted on the wall, and putty is used as the bottom layer. During the construction of the putty, glue containing formaldehyde will be added. After the decoration, the formaldehyde in the putty will slowly volatilize, which will also cause pollution and damage to homes and public places.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A formaldehyde-free architectural coating made of the following parts by weight of raw materials: 25 parts of water-based fluorocarbon emulsion, 6 parts of ethylene glycol tert-butyl ether, 5 parts of polyaniline-graphene hollow microspheres, 2 parts of clove oil, 6 parts of ZSM molecular sieve, 8 parts of ceramic fiber, 8 parts of dibutyltin dilaurate, 10 parts of sepiolite powder, 3 parts of comfrey oil, 25 parts of softened water, 2 parts of defoamer, 2 parts of dispersant, 2 parts of hydrophobic agent , 1 part of film-forming assistant.

[0022] Preferably, the defoamer is tributyl phosphate.

[0023] Preferably, the dispersant is a mixture of a polydiethanol with a molecular weight of 5000 and a polydiethanol with a molecular weight of 4000 in a mass ratio of 3:2, which can achieve a better dispersion effect.

[0024] Preferably, the film forming aid is propylene glycol methyl ether acetate.

[0025] Preferably, the hydrophobic agent is a polysiloxane-polyalkoxy ether cop...

Embodiment 2

[0031] A formaldehyde-free architectural coating made of the following raw materials by weight: 35 parts of water-based fluorocarbon emulsion, 12 parts of ethylene glycol tert-butyl ether, 7 parts of polyaniline-graphene hollow microspheres, 7 parts of clove oil, 10 parts of ZSM molecular sieve, 12 parts of ceramic fiber, 12 parts of dibutyltin dilaurate, 15 parts of sepiolite powder, 8 parts of comfrey oil, 35 parts of softened water, 5 parts of defoamer, 7 parts of dispersant, 6 parts of hydrophobic agent , 3 parts of film forming aids.

[0032] Preferably, the defoamer is tributyl phosphate.

[0033] Preferably, the dispersant is a 3:2 mass ratio mixture of polydiethanol with a molecular weight of 5000 and polydiethanol with a molecular weight of 4000, which can achieve a better dispersion effect.

[0034] Preferably, the film forming aid is propylene glycol methyl ether acetate.

[0035] Preferably, the hydrophobic agent is a polysiloxane-polyalkoxy ether copolymer or a silicone ...

Embodiment 3

[0041] A formaldehyde-free architectural coating made of the following raw materials by weight: 30 parts of water-based fluorocarbon emulsion, 9 parts of ethylene glycol tert-butyl ether, 6 parts of polyaniline-graphene hollow microspheres, 4.5 parts of clove oil, 8 parts of ZSM molecular sieve, 10 parts of ceramic fiber, 10 parts of dibutyltin dilaurate, 13 parts of sepiolite powder, 5.5 parts of comfrey oil, 30 parts of softened water, 3.5 parts of defoamer, 5 parts of dispersant, 4 parts of hydrophobic agent , 2 parts of film forming aids.

[0042] Preferably, the defoamer is tributyl phosphate.

[0043] Preferably, the dispersant is a mixture of a polydiethanol with a molecular weight of 5000 and a polydiethanol with a molecular weight of 4000 in a mass ratio of 3:2, which can achieve a better dispersion effect.

[0044] Preferably, the film forming aid is propylene glycol methyl ether acetate.

[0045] Preferably, the hydrophobic agent is a polysiloxane-polyalkoxy ether copolyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses formaldehyde-free building paint. The formaldehyde-free building paint is prepared by, by weight, 25-35 parts of water-based fluorocarbon emulsion, 6-12 parts of ethylene glycol tertiary butyl ether, 5-7 parts of polyaniline-graphene hollow microspheres, 2-7 parts of clove oil, 6-10 parts of ZSM molecular sieve, 8-12 parts of ceramic fibers, 8-12 parts of dibutyltin dilaurate, 10-15 parts of sepiolite powder, 3-8 parts of radix lithospermi oil, 25-35 parts of softened water, 2-5 parts of defoaming agent, 2-7 parts of defoaming agent, 2-7 parts of dispersing agent, 2-6 parts of hydrophobic agent and 1-3 parts of coalescing agent. The formaldehyde-free building paint has the advantages that the waterproof coating has excellent environment protection performance and isnontoxic and odorless, the surface of the paint film does not generate pungent smell during and after construction, influence on human bodies is avoided, and the paint is green and safe and good in elasticity, flexibility and water resistance.

Description

Technical field [0001] The invention relates to the field of coatings, in particular to a formaldehyde-free building coating and a preparation method thereof. Background technique [0002] Coating is a kind of liquid or fixed material that is coated on the surface of an object and forms a thin film under certain conditions to play a protective, decorative and specific role. With the development of economy, coatings are used in industry and agriculture, national defense, scientific research and people. It is more and more widely used in life. With the development of the industry, the variety of coatings is increasing, and the quality and performance of coatings are constantly improving. Coatings can no longer meet people's requirements for protection. Especially in people's daily life, waterproof and moisture-proof are also attracting more and more attention. [0003] With the acceleration of people's life pace and the improvement of their taste in life, health issues have become a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D5/14C09D5/08C09D7/61C09D7/63C09D7/65
Inventor 完颜健飞熊攀登刘峰
Owner CHINA CONSTR SEVENTH ENG BUREAU THE SECOND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com