A kind of oyster shell powder modified water treatment agent and its preparation method and application

A technology of oyster shell powder and modified water, which is applied in the field of biomedicine, can solve the problems of high cost of calcination and surfactant, ineffective modification effect of oyster shell, inconspicuous water treatment ability, etc., and achieve fast and efficient adsorption effect, Excellent stability and durability, excellent effect of repeated use performance

Active Publication Date: 2022-05-17
GUANGDONG OCEAN UNIVERSITY
View PDF19 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the modification effect of the modified agent on the oyster shell is not obvious, and the improvement of the treatment ability of the water body is not obvious. 2+ 、Co 2+ The removal rate is low, the adsorption selectivity is poor, and it is easily interfered by other high-content substances; in addition, the cost of calcination and surfactant is high, if it cannot be recycled, it will cause a significant increase in processing costs, limiting its use as an excellent The application prospects of adsorbents; moreover, the reprocessing of modified oyster shell materials is often a big problem, which is easy to cause secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oyster shell powder modified water treatment agent and its preparation method and application
  • A kind of oyster shell powder modified water treatment agent and its preparation method and application
  • A kind of oyster shell powder modified water treatment agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The preparation of embodiment 1 oyster shell powder modified water treatment agent

[0048] A preparation method of oyster shell powder modified water treatment agent, comprising the following steps:

[0049] S1. Mix oyster shell powder, polyacrylamide and solvent water evenly to obtain a suspension, and add a pH regulator to adjust the pH of the suspension to 7.5; wherein, the amount of polyacrylamide added is 15% of the mass of oyster shell powder;

[0050] S2. Ultrasonic emulsification suspension, heated at 80°C for 120 minutes with constant magnetic stirring, cooled to room temperature, centrifuged for 4 to 8 times, dried and pulverized at 70°C, passed through a 100-mesh sieve to obtain modified oyster shell powder;

[0051] S3. Mix the modified oyster shell powder with sodium carboxymethyl cellulose (the mass ratio of modified oyster shell powder to sodium carboxymethyl cellulose is 30:1), stir evenly, add water to make it coagulate Finally, a hollow ring adsorben...

Embodiment 2

[0052] The preparation of embodiment 2 oyster shell powder modified water treatment agent

[0053] A preparation method of oyster shell powder modified water treatment agent, comprising the following steps:

[0054] S1. Mix oyster shell powder, polyacrylamide and solvent water evenly to obtain a suspension, and add a pH regulator to adjust the pH of the suspension to 8; wherein, the amount of polyacrylamide added is 20% of the mass of oyster shell powder;

[0055] S2. Ultrasonic emulsified suspension, heated at 70°C for 150 minutes with constant magnetic stirring, cooled to room temperature, centrifuged for 4 to 5 times, dried and pulverized at 70°C, passed through a 100-mesh sieve to obtain modified oyster shell powder;

[0056] S3. Mix the modified oyster shell powder with sodium carboxymethyl cellulose (the mass ratio of modified oyster shell powder to sodium carboxymethyl cellulose is 35:1), stir evenly, add water to make it coagulate Finally, make a hollow ring adsorbent...

Embodiment 3

[0057] The preparation of embodiment 3 oyster shell powder modified water treatment agent

[0058] A preparation method of oyster shell powder modified water treatment agent, comprising the following steps:

[0059] S1. Mix oyster shell powder, polyacrylamide and solvent water evenly to obtain a suspension, and add a pH regulator to adjust the pH of the suspension to 7; wherein, the amount of polyacrylamide added is 20% of the mass of oyster shell powder;

[0060] S2. Ultrasonic emulsified suspension, heated at 90°C for 90 minutes with constant magnetic stirring, cooled to room temperature, centrifuged for 4 to 5 times, dried and pulverized at 70°C, passed through a 100-mesh sieve to obtain modified oyster shell powder;

[0061] S3. Mix the modified oyster shell powder with sodium carboxymethyl cellulose (the mass ratio of modified oyster shell powder to sodium carboxymethyl cellulose is 30:1), stir evenly, add water to make it coagulate Finally, make a hollow ring adsorbent,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oyster shell powder modified water treatment agent as well as its preparation method and application. The preparation method is as follows: uniformly mix oyster shell powder, polyacrylamide (PAM) and a solvent, add a pH regulator to adjust the pH; ultrasonic emulsification, stir and heat at 50-90° C. for 30-150 minutes, cool to room temperature, and centrifuge , dried, pulverized, and sieved to obtain modified oyster shell powder; mix evenly modified oyster shell powder with sodium carboxymethyl cellulose, dry naturally, calcined at medium and low temperature, and cool to obtain The oyster shell powder modified water treatment agent. Oyster shell powder modified water treatment agent of the present invention is to Ni 2+ 、Co 2+ 、Cu 2+ Such heavy metal ions have a faster and more efficient adsorption effect, and have excellent stability and persistence, which can effectively realize the treatment of waste with waste. It is a kind of efficient and environment-friendly adsorption and separation material with good application value.

Description

technical field [0001] The invention belongs to the technical field of biomedicine. More specifically, it relates to an oyster shell powder modified water treatment agent and its preparation method and application. Background technique [0002] Oysters are the economical shellfish with the largest farming output in China. While we enjoy the delicious food, we also produce a lot of discarded oyster shells. At present, there is relatively little processing of oyster shells in my country, and most oyster shells are discarded or landfilled, and some organic matter in oyster shells will deteriorate due to long-term stacking, causing environmental pollution and waste of resources. Oysters have left and right shells, the right shell is also called the upper shell, and the left shell is also called the lower shell. The oyster shell is divided into three layers according to the formation method and tissue structure: the outermost layer is the cuticle or cortex (periostracum), which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/26B01J20/30C02F1/28C02F101/20
Inventor 谷长生李泳张兆霞郝晓敏洪鹏志蔡鹰孙省利余传明景占鑫廖铭能
Owner GUANGDONG OCEAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com