Flash rust-proof acrylic roof waterproof coating and preparation method thereof

A waterproof coating and acrylic technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of easy flash rust and poor anti-flash rust effect of waterproof coatings, and achieve durable waterproof effect, strong adhesion, human health and surrounding environment harmless effect

Inactive Publication Date: 2019-05-24
KESHUN WATERPROOF TECH CO LTD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides an acrylic roof waterproof coating, which solves the defects that the acrylic metal roof waterproof coating is easy to flash rust and has poor anti-flash rust effect by using anti-rust slurry and anti-flash rust additives, making the acrylic metal roof waterproof coating Longer usability and durable waterproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flash rust-proof acrylic roof waterproof coating and preparation method thereof
  • Flash rust-proof acrylic roof waterproof coating and preparation method thereof
  • Flash rust-proof acrylic roof waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a roof waterproof coating with anti-flash rust function, which specifically includes the following raw materials in parts by weight: 35.2 parts of acrylic emulsion, 50 parts of antirust slurry, 5 parts of plasticizer, 0.3 part of dispersant, disinfectant 0.2 parts of foaming agent, 0.15 parts of substrate wetting agent, 0.5 parts of anti-flash rust additive, 0.3 parts of film-forming aid, 8 parts of deionized water, 0.15 part of cellulose ether, 0.1 part of fungicide, and 0.05 part of coupling agent , 0.05 parts of pH regulator.

[0034] The anti-rust slurry is composed of the following components by weight: 20 parts of acrylic emulsion, 2 parts of zinc phosphate, 5 parts of aluminum tripolyphosphate, 43.4 parts of 800 mesh heavy calcium, 5 parts of titanium iron powder, 20 parts of deionized water, 4.5 parts of dispersant, 0.1 part of defoamer.

[0035] Wherein, the acrylic emulsion is pure acrylic emulsion for U.S. Dow Rohm and Haas Bailimo E...

Embodiment 2

[0056] This embodiment provides a roof waterproof paint with anti-flash rust function, which specifically includes the following raw materials in parts by weight: 30.2 parts of acrylic emulsion, 55 parts of antirust slurry, 5 parts of plasticizer, 0.3 part of dispersant, disinfectant 0.2 parts of foaming agent, 0.15 parts of substrate wetting agent, 0.5 parts of anti-flash rust additive, 0.3 parts of film-forming aid, 8 parts of deionized water, 0.15 part of cellulose ether, 0.1 part of fungicide, and 0.05 part of coupling agent , 0.05 parts of pH regulator.

[0057] The anti-rust slurry is composed of the following components by weight: 20 parts of acrylic emulsion, 2 parts of zinc phosphate, 5 parts of aluminum tripolyphosphate, 43.4 parts of 800 mesh heavy calcium, 5 parts of titanium iron powder, 20 parts of deionized water, 4.5 parts of dispersant, 0.1 part of defoamer.

[0058] Wherein, the acrylic emulsion is pure acrylic emulsion for U.S. Dow Rohm and Haas Bailimo EC4...

Embodiment 3

[0071] This embodiment provides a roof waterproof coating with anti-flash rust function, which specifically includes the following raw materials in parts by weight: 40.2 parts of acrylic emulsion, 45 parts of antirust slurry, 5 parts of plasticizer, 0.3 part of dispersant, disinfectant 0.2 parts of foaming agent, 0.15 parts of substrate wetting agent, 0.5 parts of anti-flash rust additive, 0.3 parts of film-forming aid, 8 parts of deionized water, 0.15 part of cellulose ether, 0.1 part of fungicide, and 0.05 part of coupling agent , 0.05 parts of pH regulator.

[0072] The anti-rust slurry is composed of the following components by weight: 20 parts of acrylic emulsion, 2 parts of zinc phosphate, 5 parts of aluminum tripolyphosphate, 43.4 parts of 800 mesh heavy calcium, 5 parts of titanium iron powder, 20 parts of deionized water, 4.5 parts of dispersant, 0.1 part of defoamer.

[0073] Wherein, the acrylic emulsion is pure acrylic emulsion for U.S. Dow Rohm and Haas Bailimo E...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of water proofing of metal roofs and particularly discloses a flash rust-proof acrylic roof waterproof coating which is prepared from, by weight, the following raw materials: 30-50 parts of an acrylic emulsion, 25-60 parts of antirust slurry, 1-5 parts of a plasticizer, 0.3-5 parts of a dispersing agent, 0.1-1 part of a defoaming agent, 0.1-1 part of a base material wetting agent, 0.1-2 parts of an anti-flash rust additive, 1-4 parts of a film forming assistant, 3-10 parts of water, 0.01-0.5 part of cellulose ether, 0.1-0.5 part of a bactericide, 0.01-0.5 part of a coupling agent and 0.01-0.5 part of a pH adjusting agent. The flash rust-proof waterproof effect of the roof waterproof coating with a flash rust-proof function is longer lasting than that of acommon metal roof waterproof coating, the anti-ultraviolet effect is good, and the service life of a base material is prolonged. The waterproof coating has high elongation rate, good elasticity, strong base layer deformation resistance, the capability of shielding cracks, water proofing and breathability.

Description

technical field [0001] The invention relates to the field of building waterproofing, in particular to an anti-flash rust acrylic roof waterproof coating and a preparation method thereof. Background technique [0002] For the waterproof treatment of metal roofs, the requirements are different according to the degree of newness and oldness of the metal surface. Generally, it is divided into two situations: one is the steel structure building that has been used for more than 2 to 3 years, and the metal surface of the roof has been used. In this case, the waterproofing of the metal surface should adopt the process of antirust and anticorrosion first, and then waterproof construction; the other is a new steel structure building or a building using aluminum plate or galvanized plate as the roof panel. The condition of the metal surface is very good, and it can be directly waterproofed after the surface is cleaned and painted with metal surface treatment agent. At present, the tra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D125/14C09D5/10C09D7/61C09D7/63
Inventor 黄思墨龚兴宇黄莉恒李雪梅顾家豪胡全超
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com