Environment-friendly oil production delayed cross-linking profile control agent, method for preparing same and application of environment-friendly oil production delayed cross-linking profile control agent
A delayed cross-linking and environment-friendly technology, applied in chemical instruments and methods, production fluids, earthwork drilling and production, etc., can solve problems such as inability to meet the profile control requirements of low-permeability fractured formations, reduced oil recovery, and reduced strength. Achieve the effects of good application prospects and production potential, good industrialization potential, and excellent thermal stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0053] Example 1: Preparation of environmentally friendly delayed cross-linking profile control agent for oil recovery
[0054] S1: Synthesize salt-resistant polymer solution, specifically:
[0055] In parts by weight, at a constant temperature of 10°C, 18 parts of acrylamide, 5 parts of 2-acrylamido-2-methylpropanesulfonic acid, 0.5 parts of N,N-dimethyl- Cetyl allyl ammonium chloride and 0.05 part of sodium formate, stir well, then slowly add the ternary composite initiator (in parts by weight, 0.2 part of tetramethylethylenediamine, 0.1 part of ammonium persulfate and 0.025 part of ammonium persulfate Part of sodium sulfite mixture), and continue to react at a constant temperature of 10 ° C for 3 hours to obtain the salt-resistant polymer solution;
[0056] S2: hydrolyzing the salt-resistant polymer solution to obtain a hydrolyzate, specifically:
[0057] At a constant temperature of 40 ° C, an appropriate amount of sodium carbonate is added to the salt-resistant polymer ...
Embodiment 2
[0062] Example 2: Preparation of environmentally friendly delayed cross-linking profile control agent for oil recovery
[0063] S1: Synthesize salt-resistant polymer solution, specifically:
[0064] In parts by weight, at a constant temperature of 12 °C, to 100 parts of deionized water, add 20 parts of acrylamide, 3 parts of 2-acrylamido-2-methylpropanesulfonic acid, 1 part of N,N-dimethyl- Cetyl allyl ammonium chloride and 0.05 part of sodium formate, stir well, then slowly add the ternary composite initiator (in parts by weight, 0.4 part of tetramethylethylenediamine, 0.05 part of ammonium persulfate and 0.05 part of ammonium persulfate Parts of sodium sulfite mixture), and continue to react at a constant temperature of 12 ° C for 2 hours to obtain the salt-resistant polymer solution;
[0065] S2: hydrolyzing the salt-resistant polymer solution to obtain a hydrolyzate, specifically:
[0066] At a constant temperature of 50 ° C, an appropriate amount of sodium carbonate is ...
Embodiment 3
[0071] Example 3: Preparation of environmentally friendly delayed cross-linking profile control agent for oil recovery
[0072] S1: Synthesize salt-resistant polymer solution, specifically:
[0073] In parts by weight, at a constant temperature of 11 °C, to 100 parts of deionized water, add 19 parts of acrylamide, 4 parts of 2-acrylamido-2-methylpropanesulfonic acid, 0.75 parts of N,N-dimethyl- Cetyl allyl ammonium chloride and 0.05 part of sodium formate, stir well, and then slowly add the ternary composite initiator (in parts by weight, 0.3 part of tetramethylethylenediamine, 0.075 part of ammonium persulfate and 0.038 part of ammonium persulfate) Part of sodium sulfite mixture), and continue to react at a constant temperature of 11 ° C for 2.5 hours to obtain the salt-resistant polymer solution;
[0074] S2: hydrolyzing the salt-resistant polymer solution to obtain a hydrolyzate, specifically:
[0075] At a constant temperature of 45 ° C, an appropriate amount of sodium c...
PUM
Property | Measurement | Unit |
---|---|---|
strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com