Functional polyester production method and production system and functional polyester fiber

A production system and production method technology, applied in the direction of adding pigments to single-component polyester artificial filaments and spinning solutions, can solve the problems of difficult spinning of fine denier or ultrafine denier, difficulty of functional powder, functional polymer Problems such as poor spinning performance of ester melt, to achieve the effect of easy industrial implementation, improving spinning performance and increasing production efficiency

Active Publication Date: 2019-05-03
CHINESE TEXTILE ACAD +1
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of preparing functional polyester fiber by masterbatch method, since the dispersion of functional powder in high-viscosity polyester melt mainly depends on the mechanical shear force provided by mixing equipment, it is difficult for functional powder to be highly uniform in polyester melt Dispersion, the spinning performance of the prepared functional polyester melt is poor, and it is difficult to spin functional polyester fibers with fine denier or ultra-fine denier

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional polyester production method and production system and functional polyester fiber
  • Functional polyester production method and production system and functional polyester fiber
  • Functional polyester production method and production system and functional polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] S1, the raw material slurry of the polyester oligomer slurry with the alkyd molar ratio of terephthalic acid and ethylene glycol being 1.13 is continuously and uniformly transported to the vertical machine with a flow rate of 4613kg / h The esterification reaction is carried out in the esterification reaction system composed of the first esterification reactor and the vertical second esterification reactor. The reaction temperature of the first esterification reactor is 260°C, and the reaction temperature of the second esterification reactor is 265°C. The catalyst ethylene glycol antimony solution with a concentration of 3 wt% was continuously and uniformly injected into the second esterification reaction tank at a flow rate of 54.8 kg / h. When the acid value of the polyester oligomer reaches 15mgKOH / g, the oligomer delivery metering device composed of the oligomer pump and the oligomer flowmeter is continuously and stably extracted from the second esterification reactor at...

Embodiment 2

[0059] S1, the polyester oligomer slurry prepared by terephthalic acid and ethylene glycol with an alkyd molar ratio of 1.13 is continuously and uniformly transported to the vertical The esterification reaction is carried out in the esterification reaction system composed of the first esterification reactor and the vertical second esterification reactor. The reaction temperature of the first esterification reactor is 260°C, and the reaction temperature of the second esterification reactor is 265°C. The catalyst ethylene glycol antimony solution with a concentration of 3 wt% was continuously and uniformly injected into the second esterification reaction tank at a flow rate of 54.8 kg / h. When the acid value of the polyester oligomer reaches 15mgKOH / g, the oligomer delivery metering device composed of the oligomer pump and the oligomer flowmeter is continuously and stably extracted from the second esterification reactor at a flow rate of 3931kg / h. out.

[0060] S2, blend terepht...

Embodiment 3

[0065] S1, the raw material slurry of the polyester oligomer slurry with the alkyd molar ratio of terephthalic acid and ethylene glycol being 1.13 is continuously and uniformly transported to the vertical machine with a flow rate of 4613kg / h The esterification reaction is carried out in the esterification reaction system composed of the first esterification reactor and the vertical second esterification reactor. The reaction temperature of the first esterification reactor is 260°C, and the reaction temperature of the second esterification reactor is 265°C. The catalyst ethylene glycol antimony solution with a concentration of 3 wt% was continuously and uniformly injected into the second esterification reaction tank at a flow rate of 54.8 kg / h. When the acid value of the polyester oligomer reaches 15mgKOH / g, the oligomer delivery metering device composed of the oligomer pump and the oligomer flowmeter is continuously and stably extracted from the second esterification reactor at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer material synthesis, and particularly relates to a functional polyester production system. The functional polyester production system comprises apolyester main production system, and further comprises a functional powder slurry concentrate preparation system, the polyester main production system comprises an esterification system, a pre-polycondensation system and a final polycondensation system which are connected in sequence, the functional powder slurry concentrate preparation system comprises an online adding device which is connectedwith the esterification system or a part between the esterification system and the pre-polycondensation system. The functional powder slurry concentrate preparation system is introduced in the polyester main production system, and can continuously prepare a functional powder slurry concentrate with low hydroxyl value and low pressure filtration value, and the prepared functional powder slurry concentrate and a polyester oligomer are uniformly mixed for polycondensation reaction to obtain functional polyester with uniformly dispersed functional powder. The invention further relates to a functional polyester production method.

Description

technical field [0001] The invention belongs to the technical field of polymer material synthesis, and in particular relates to a functional polyester production method, production system and functional polyester fiber. Background technique [0002] At present, the preparation method of functional polyester fiber is mainly the masterbatch method. First, the functional powder and the carrier resin are melted and mixed to obtain a functional masterbatch with high functional powder content, and then the functional masterbatch melt is mixed with the polyester for spinning. The ester melts are evenly mixed to obtain functional polyester fibers through the spinning process. In the process of preparing functional polyester fiber by masterbatch method, since the dispersion of functional powder in high-viscosity polyester melt mainly depends on the mechanical shear force provided by mixing equipment, it is difficult for functional powder to be highly uniform in polyester melt Disper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/183C08G63/78D01F6/92D01F1/04
CPCC08G63/183C08G63/78D01F1/04D01F6/92
Inventor 李鑫邱志成王颖张厚羽金剑李志勇刘玉来王雪马肖刘建立
Owner CHINESE TEXTILE ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com