A kind of double bond polymer quantum dot film and preparation method thereof

A quantum dot film and polymer technology, applied in chemical instruments and methods, electronic equipment, other household appliances, etc., can solve the problems of low yield, no light emission, and quantum dot light emission distortion, so as to reduce the manufacturing cost and improve the barrier. Ability, the effect of simplifying the process

Active Publication Date: 2022-01-28
四川东方绝缘材料股份有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult to process the barrier film by this method, the yield is low, and the cost is very high
Simultaneously, this method can be in contact with air at the edge coating layer of quantum dot film interlayer, causes the quantum dot of quantum dot film to luminously distort or does not emit light (edge ​​failure), promptly at 85 ℃ of temperature, 85% humidity or 60 ℃ of temperature, 90% After 1000 hours of treatment under humidity conditions, the edge failure exceeds the width of 0.5mm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of double bond polymer quantum dot film and preparation method thereof
  • A kind of double bond polymer quantum dot film and preparation method thereof
  • A kind of double bond polymer quantum dot film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～20

[0034] 1. Embodiments 1-20: a method for preparing a double-bond polymer quantum dot film, the steps are:

[0035] Step a: First blend 0.1-5 parts by mass of micron-scale light diffusing agent, 0-95 parts by mass of polyolefin resin and 0-95 parts by mass of vinylidene chloride-methyl acrylate copolymer (ie PVDC resin) A layer material, and then 0.02 to 2 mass parts of quantum dots and 0.1 to 10 mass parts of micron light diffusing agent and 80 to 99 mass parts of polyolefin resin are blended into B layer material; the A layer material and B After the layer material is melted at 220°C to 280°C (temperature 1) in extruder 1 and 220°C to 280°C (temperature 2) in extruder 2, it is heated through 220°C to 280°C (temperature 3) ) under the three-layer co-extrusion die mouth extrusion, drool on the cold drum at 60 ~ 100 ℃ (temperature 4) to make an ABA structure film with a thickness of A layer of 10 ~ 200 μm and a thickness of B layer of 18 ~ 300 μm or in Cast sheet on cold drum a...

Embodiment 21

[0057] A double-bond polymer quantum dot film, the double-bond polymer quantum dot film is made of A-layer material and B-layer material through three-layer co-extrusion salivation or biaxial stretching, the thickness of A layer is 10 μm, and the thickness of B layer A quantum dot primary base film with a 300 μm ABA three-layer film structure, and then fluorinated on both surfaces of the quantum dot primary base film to prepare a quantum dot secondary base film with an ABA three-layer film structure, and then in Double-bond polymer quantum dot film prepared by coating thermosetting resin on both surfaces of the quantum dot secondary base film and forming a coating with a drying thickness of 1 μm;

[0058] The A-layer material is a mixture of 0.1 parts by mass of micron-scale light diffusing agent and 95 parts by mass of vinylidene chloride-methyl acrylate copolymer (PVDC resin for short);

[0059] The B layer material is composed of 0.02 parts by mass of quantum dots, 0.1 part...

Embodiment 22

[0063] A double-bond polymer quantum dot film, the double-bond polymer quantum dot film is made of A-layer material and B-layer material through three-layer co-extrusion salivation or biaxial stretching, and the thickness of A layer is 200 μm, and the thickness of B layer is A quantum dot primary base film with an ABA three-layer film structure of 18 μm, and then fluorinated on the double surface of the quantum dot primary base film to prepare a quantum dot secondary base film with an ABA three-layer film structure. Double-bond polymer quantum dot film prepared by coating thermosetting resin on both surfaces of the quantum dot secondary base film and forming a coating with a drying thickness of 10 μm;

[0064] The A-layer material is a mixture of 5 parts by mass of micron-scale light diffusing agent and 95 parts by mass of polyolefin resin;

[0065] The B layer material is composed of 2 parts by mass of quantum dots, 10 parts by mass of micron light diffusing agent and 99 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a double-bond polymer quantum dot film and a preparation method thereof. The prepared ABA three-layer quantum dot primary base film with a thickness of 10-200 μm and B layer with a thickness of 18-300 μm is prepared, and then processed by fluorination technology on both surfaces of the quantum dot primary base film. Double-bond polymer quantum dots prepared by obtaining a quantum dot secondary base film with an ABA three-layer film structure, and then coating a thermosetting resin on both surfaces of the quantum dot secondary base film and forming a coating with a drying thickness of 1-10 μm Membrane; the water vapor transmission rate of the membrane is 0.01~0.1g / m 2 ·24 hours, 1000 hours at 85℃, 85% humidity or 60℃, 90% humidity, the edge failure is 0~0.2mm, used in various display fields, can increase the luminous effect, and make the color more colorful.

Description

technical field [0001] The invention belongs to an optical organic polymer composite film and its preparation, and relates to a double-bond polymer quantum dot film and a preparation method thereof. The double-bond polymer quantum dot film of the present invention is a double-bond polymer quantum dot film based on polyolefin resin and vinylidene chloride (abbreviated as VDC)-methyl acrylate (abbreviated as MA) copolymer (ie PVDC resin for short) film. Dot film, the double-bond polymer quantum dot film can be used in various display fields to increase the luminous effect and make the color more colorful. Background technique [0002] In recent years, liquid crystal displays have been widely popularized. In order to further improve its color gamut, quantum dot light-emitting technology can be used to achieve the goal. Because the quantum dots emit more pure light, after the red and green quantum dots are excited by blue light, the color gamut coverage can be increased to 110%...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/14C08L25/10C08L27/16C08L23/06C08L23/08C08K3/08C08K3/22C08K3/30C08K3/36C08J7/12C09D129/04C09D175/04C09D163/00C09D7/61B32B27/08B32B27/06B32B27/32B32B27/30B32B27/18B32B33/00
CPCC09D129/04C09D163/00C09D175/04C08J7/12C08L23/06C08L23/12C08L27/16C09D7/61B32B27/08B32B27/18B32B27/302B32B27/304B32B27/32B32B33/00C08J2327/16C08J2323/06C08J2323/12C08K2201/003C08K2201/011C08K2003/2241B32B2255/10B32B2255/26B32B2250/40B32B2307/7246B32B2457/202C08L23/0823C08L23/145C08L25/10C08K3/36C08K3/22C08K3/00C08K3/30C08K3/08C08K3/346
Inventor 舒维赵贵红马雅琳罗春明唐安斌李建学
Owner 四川东方绝缘材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com