Intermediate temperature crackled glaze porcelain for daily use and preparation method thereof

A technology of cracked glaze and daily-use porcelain, which is applied in the field of medium-temperature cracked-glazed daily-use porcelain and its preparation, can solve the problems of product quality, food safety hazards, food safety hazards, and high production costs, so as to shorten preparation time, improve quality, and resist The effect of improving the folding strength

Active Publication Date: 2019-03-26
HUNAN HUALIAN CHINA IND
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cracked glaze product obtained by method 1 uses ink, which penetrates into the green body from the glaze crack, showing a crack effect, and there are certain hidden dangers in food safety, so it is generally only used in decorative art porcelain such as vases.
However, the cracked glaze product obtained by method 2 must be fired for the second time, and the rate of porcelain frying (generally 10-20%) is higher during the second firing, resulting in higher production costs.
The crackle effect of the crackle glaze product obtained by the above two methods is relatively large and rough. After a period of time, the cracking situation in the later stage of secondary cracking is more serious, which has a potential hidden danger to the quality of the product and food safety in the later stage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Intermediate temperature crackled glaze porcelain for daily use and preparation method thereof
  • Intermediate temperature crackled glaze porcelain for daily use and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A medium-temperature cracked glaze daily-use porcelain, including a blank and a glaze, and the blank includes the following components and their parts by weight: 10 parts of Jiangxi Pingxiang washed quartz powder, 33 parts of Hengshan albite, 20 parts of Shaoguan washed kaolin, and 33 parts of Fujian washed kaolin parts, Henan Nanyang porcelain clay 7 parts, dolomite mineralizer 0.7 parts.

[0038] The preparation method of medium-temperature cracked glaze daily-use porcelain: 1) prepare materials according to each component and the weight of each component, put the raw materials into a ball mill, add an appropriate amount of water, and wet ball mill together for 12 hours to obtain a fineness of 250 mesh sieve 0.05-0.15% base slurry, sieving, iron removal, mud pressing, mud refining, sinking, and then roll forming to obtain a wet billet, drying, and trimming to obtain a green billet; the mass ratio of raw materials, ball stones, and water is 1:1.7:1.3;

[0039] 2) The ...

Embodiment 2

[0041] A medium-temperature cracked glaze daily-use porcelain, including a blank and a glaze. The blank includes the following components and their parts by weight: 12 parts of Jiangxi Pingxiang washed quartz powder, 28 parts of Hengshan albite, 27 parts of Shaoguan washed kaolin, and 28 parts of Fujian washed kaolin 1 part, 5 parts of Henan Nanyang porcelain clay, 1 part of dolomite mineralizer.

[0042] The preparation method of medium-temperature cracked glaze daily-use porcelain: 1) prepare materials according to each component and the weight of each component, put the raw materials into a ball mill, add an appropriate amount of water, and wet ball mill together for 12 hours to obtain a fineness of 250 mesh sieve 0.05-0.15% base slurry, sieving, iron removal, mud pressing, mud refining, sinking, and then roll forming to obtain a wet billet, drying, and trimming to obtain a green billet; the mass ratio of raw materials, ball stones, and water is 1:1.5:1.2;

[0043] 2) The ...

Embodiment 3

[0045] A medium-temperature cracked glaze daily-use porcelain, including a blank and a glaze. The blank includes the following components and their parts by weight: 15 parts of Jiangxi Pingxiang washed quartz powder, 29 parts of Hengshan albite, 25 parts of Shaoguan washed kaolin, and 25 parts of Fujian washed kaolin parts, Henan Nanyang porcelain clay 10 parts, dolomite mineralizer 0.5 parts.

[0046] The preparation method of medium-temperature cracked glaze daily-use porcelain: 1) prepare materials according to each component and the weight of each component, put the raw materials into a ball mill, add an appropriate amount of water, and wet ball mill together for 12 hours to obtain a fineness of 250 mesh sieve 0.05-0.15% base slurry, sieving, iron removal, mud pressing, mud refining, sinking, and then roll forming to obtain a wet billet, drying, and trimming to obtain a green billet; the mass ratio of raw materials, ball stones, and water is 1:1.4:1.3;

[0047] 2) The gre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses intermediate temperature crackled glaze porcelain for daily use. The intermediate temperature crackled glaze porcelain for daily use comprises a blank and glaze, wherein the blank is prepared from the following components in parts by weight: 10-15 parts of washed quartz powder, 28-33 parts of feldspar, 50-55 parts of washed kaolin, 5-10 parts of petuntse, and 0.5-1 part ofdolomite mineralizer. The adopted blank can realize one-step fast firing, the firing period can be shortened to 5-8 h, the ball-milling time is shortened to 12 h, and on the basis of ensuring the strength of the green body, the preparation time of the intermediate temperature crackled glaze porcelain for daily use can be shortened, the quality of a final product is improved, the quality standard of the porcelain for daily use can be met, and the water absorption ratio of the prepared intermediate temperature crackled glaze porcelain for daily use is below 0.5%.

Description

technical field [0001] The invention belongs to the technical field of daily-use ceramics, and in particular relates to a medium-temperature cracked-glazed daily-use porcelain and a preparation method thereof. Background technique [0002] Crackle glaze is also called grain glaze and broken grain glaze. The formation of cracks on the glaze is a defect of ceramic products, but the cracked glaze is artificially causing clear cracks in the glaze, so that the ceramic products have a unique artistic effect. Due to the different shapes of cracks, their names also vary accordingly, such as caviar grain, rubbish crack, ice crack, crab claw grain and other varieties. The most precious one is called "gold wire iron thread" or "eel claw pattern", which is interwoven with fine red and yellow cracks in the rough black grain, and the dark and shallow cracks set off each other. Crackle glazes are currently used in daily-use ceramics, but there are many defects such as product color absor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/24C04B33/16C04B33/13C04B33/04C04B41/86
CPCC04B33/04C04B33/13C04B33/16C04B33/24C04B41/5022C04B41/86C04B2235/321C04B2235/3472C04B2235/6567C04B2235/96
Inventor 麦潮棠叶守明
Owner HUNAN HUALIAN CHINA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap