Wear-resistant flame-retardant type cigarette tipping paper printing ink and preparation method thereof
A kind of cigarette tipping paper, flame-retardant technology, applied in the direction of ink, application, household utensils, etc., can solve the problems of not having high wear resistance, poor anti-wear performance, easy to burn ink, etc., to improve printing quality, The effect of wide temperature adaptability and wide range of applicable models
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0038] A method for preparing wear-resistant and flame-retardant cigarette tipping paper ink, comprising the following steps:
[0039](1) Weigh raw materials according to the proportion; 120 parts of polyvinyl butyral resin, 70 parts of polyacrylamide resin, 12 parts of modified rosin, 220 parts of ethanol for auxiliary agent, 7 parts of dibutyl ester, 22 parts of titanium dioxide, 22 parts of medical talcum powder, 12 parts of white carbon black, 12 parts of iron oxide red, 28 parts of iron oxide black, 32 parts of iron oxide yellow, 3 parts of borax, 18 parts of antimony oxide-chlorinated paraffin system, polymer material Schiff base 30 parts, 7 parts of magnesium hydroxide, 320 parts of ethanol for dissolving and 22 parts of water.
[0040] (2) Preparation of binder; put ink binder and ink binder additive in a closed reactor, heat to 90°C, stir for 8 hours, then cool to normal temperature;
[0041] (3) Mixing; put wear-resistant fillers, colorants, flame retardant additive...
Embodiment 2
[0046] A method for preparing wear-resistant and flame-retardant cigarette tipping paper ink, comprising the following steps:
[0047] (1) Weigh the raw materials according to the proportion; 80 parts of polyvinyl butyral resin, 30 parts of polyacrylamide resin, 8 parts of modified rosin, 180 parts of ethanol for auxiliary agent, 3 parts of dibutyl ester, 18 parts of titanium dioxide, 18 parts of medical talcum powder, 8 parts of white carbon black, 8 parts of iron oxide red, 22 parts of iron oxide black, 28 parts of iron oxide yellow, 1 part of borax, 12 parts of antimony oxide-chlorinated paraffin system, polymer material Schiff base 20 parts, 3 parts of magnesium hydroxide, 280 parts of ethanol for dissolving and 18 parts of water.
[0048] (2) Preparation of binder; put ink binder and ink binder additive in a closed reactor, heat to 80°C, stir for 4 hours, then cool to normal temperature;
[0049] (3) Mixing; put wear-resistant fillers, colorants, flame retardant additive...
Embodiment 3
[0054] A method for preparing wear-resistant and flame-retardant cigarette tipping paper ink, comprising the following steps:
[0055] (1) Weigh the raw materials according to the proportion; 100 parts of polyvinyl butyral resin, 50 parts of polyacrylamide resin, 10 parts of modified rosin, 200 parts of ethanol for auxiliary agent, 5 parts of dibutyl ester, 20 parts of titanium dioxide, 20 parts of medical talcum powder, 10 parts of white carbon black, 10 parts of iron oxide red, 25 parts of iron oxide black, 30 parts of iron oxide yellow, 2 parts of borax, 15 parts of antimony oxide-chlorinated paraffin system, polymer material Schiff base 20 parts, 5 parts of magnesium hydroxide, 300 parts of ethanol for dissolving and 20 parts of water.
[0056] (2) Preparation of binder; put ink binder and ink binder additive in a closed reactor, heat to 85°C, stir for 6 hours, then cool to normal temperature;
[0057] (3) Mixing; put wear-resistant fillers, pigments, flame retardant addi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com