Environment-friendly high temperature grease and preparation method thereof
A technology of lubricating grease and grease composition, which is applied in the field of lubricating grease, can solve the problems of not being able to maintain lubrication for a long time, equipment downtime, manpower, waste, etc., achieve good elasticity and flexibility, good biodegradability, and not easy The effect of oxidation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] Weigh 180.16g of glucose and 1412.3g (2.5mol) of dimer acid into the reaction kettle respectively, add 2.4g of lanthanum oxide, stir and heat to 210°C, fully react for 10 hours, depressurize and drain water twice during the reaction, and reduce the pressure after the reaction is completed. Press out the water, which is a grease composition, which can be directly used as an environment-friendly high-temperature grease.
[0031] Apply the high-temperature lubricating grease prepared in this example on the guide rail of the high-temperature aluminum casting furnace (the guide rail originally used graphite / molybdenum disulfide high-temperature grease, and the guide rail has been worn for a period of time). After a period of use, the guide rail obviously runs smoothly .
Embodiment 2
[0033] Weigh 180.16g of glucose and 1129.84g (2mol) of dimer acid into the reaction kettle respectively, stir and heat to 240°C, fully react for 8 hours, depressurize and drain water twice during the reaction, and drain water under depressurization after the reaction is completed, which is a A grease composition.
[0034] Weigh 950g of the grease composition and 50g of polytetrafluoroethylene, stir for 60 minutes at a temperature of 220°C, and cool naturally to obtain an environmentally friendly high-temperature grease.
Embodiment 3
[0036] Weigh 180.16g of glucose and 1694.76g (3 mol) of dimer acid into the reaction kettle respectively, add 20g of phosphoric acid (marked effective content 85%) and stir and heat to 180°C, fully react for 12 hours, decompress and drain 3 times in the middle of the reaction, and react After completion, depressurize and discharge water, which is a grease composition.
[0037] Weigh 900g of grease composition, 60g of polytetrafluoroethylene, 20g of trilauryl phosphate, 10g of zinc oxide, and 10g of antioxidant (Irganox L57), stir for 30 minutes at a temperature of 240° C., and cool naturally to obtain An environmentally friendly high temperature grease.
[0038] The environment-friendly high-temperature lubricating grease prepared above was subjected to the roller stability test according to SH / T0122:
[0039] project
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap