Polyvinyl chloride cable composite material, preparation method thereof and cable

A polyvinyl chloride cable and composite material technology, applied in the direction of circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problems of limited use, unsatisfactory high temperature resistance, poor high temperature resistance, etc., and achieve low temperature resistance Oil resistance, stable performance, and low material cost

Active Publication Date: 2019-03-05
深圳市帝源新材料科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the deficiencies in the above-mentioned prior art, provide a polyvinyl chloride cable composite material and its preparation method, to solve the technical problem of poor high temperature resistance of the existing polyvinyl chloride cable composite material
[0005] Another object of the present invention is to provide a cable to solve the technical problem that the use of existing polyvinyl chloride cables is limited due to unsatisfactory high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride cable composite material, preparation method thereof and cable
  • Polyvinyl chloride cable composite material, preparation method thereof and cable
  • Polyvinyl chloride cable composite material, preparation method thereof and cable

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] On the other hand, the embodiment of the present invention provides a preparation method of the polyvinyl chloride cable composite material in the above embodiment. In one embodiment, the preparation method of the polyvinyl chloride cable composite material includes the following steps:

[0032] Step S01: Weigh the raw materials of each component according to the components contained in the polyvinyl chloride cable composite material and the content of each component in the above-mentioned invention embodiment;

[0033] Step S02: Mixing the weighed polyvinyl chloride resin, filler, stabilizer, crosslinking agent, flame retardant and pre-crosslinking modifier to obtain a first mixed material;

[0034] Step S03: adding the weighed plasticizer into the first mixed material, heating and performing mixing treatment to obtain a second mixed material;

[0035] Step S04: Melt extruding the second mixed material.

[0036] Wherein, the content of each component weighed in the abo...

Embodiment 1

[0050] This embodiment provides a polyvinyl chloride cable composite material and a preparation method thereof. Wherein, the polyvinyl chloride cable composite material includes the following components in parts by weight:

[0051] Polyvinyl chloride resin (polymerization degree 2500): 100 parts,

[0052] Filler I (heavy calcium carbonate 2800): 8 parts,

[0053] Filler II (nano calcium carbonate CCR): 8 parts

[0054] High temperature plasticizer (W-797-ZH): 45 parts,

[0055] Environmental stabilizer (RUP-110C): 6 parts,

[0056] Pre-crosslinking modifier (P95): 15 parts,

[0057] Environmentally friendly flame retardant (antimony trioxide): 6 parts

[0058] Colorant: 2 parts

[0059] Cross-linking agent (TMPTMA): 7

[0060] The preparation method of the polyvinyl chloride cable composite material is as follows:

[0061] S11. Take the corresponding weight fractions of the components contained in the polyvinyl chloride according to the present embodiment;

[0062] S1...

Embodiment 2

[0066] This embodiment provides a polyvinyl chloride cable composite material and a preparation method thereof. Wherein, the polyvinyl chloride cable composite material includes the following components in parts by weight:

[0067] Polyvinyl chloride resin (polymerization degree 2500): 100 parts,

[0068] Filler I (heavy calcium carbonate 2800): 15 parts,

[0069] Filler II (nanometer calcium carbonate CCR): 15 parts

[0070] High temperature plasticizer (UN-380): 60 parts,

[0071] Environmental stabilizer (RUP-110C): 15 parts,

[0072] Pre-crosslinking modifier (P95): 15 parts,

[0073] Environmentally friendly flame retardant (antimony trioxide): 10 parts

[0074] Colorant: 3 parts

[0075] Cross-linking agent (TMPTMA): 10

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyvinyl chloride cable composite material, a preparation method thereof and a cable. The polyvinyl chloride cable composite material comprises the following components in parts by weight: 100 parts of polyvinyl chloride resin, 5-30 parts of filler, 30-60 parts of a plasticizer, 5-15 parts of a stabilizer, 10-25 parts of a pre-crosslinking modifier, 5-10 parts of a flameretardant, 1-3 parts of a coloring agent and 5-10 parts of a cross-linking agent. The cable provided by the invention comprises the polyvinyl chloride cable material provided by the invention. The polyvinyl chloride cable composite material disclosed by the embodiment of the invention has excellent high-temperature resistance, low-temperature resistance and oil resistance, is environmentally friendly, and is free of toxicity. The polyvinyl chloride cable composite material prepared by the preparation method is stable in performance, and cost is reduced.

Description

technical field [0001] The invention belongs to the technical field of polymer composite materials, and in particular relates to a polyvinyl chloride cable composite material, a preparation method thereof and a cable containing the polyvinyl chloride cable composite material. Background technique [0002] At present, from the published technical standards, the highest temperature resistance grade of PVC cable materials in the US UL758 / 1581 standard is 105°C, and the accelerated aging condition is 136°C / 168 hours accelerated constant temperature. In the Chinese GB8815 standard, the highest temperature resistance The temperature grade is 90°C, and the accelerated aging condition is 135°C / 240 hours. In the European VDE0218 standard, the highest temperature resistance level is 90°C, and the accelerated aging condition is 135°C / 336 hours. However, materials with a temperature resistance level of 125°C and above are basically cross-linked polyethylene materials, silicone rubber ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/26C08K3/22C08K5/103H01B3/44
CPCC08K3/2279C08K3/26C08K5/103C08K13/02C08K2003/265C08K2201/011C08K2201/014C08L2201/08C08L2203/202H01B3/443C08L27/06
Inventor 熊陶张万涛曾美昌
Owner 深圳市帝源新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com