Preparation method of antibacterial electromagnetic shielding type plywood

A shielding, plywood technology, used in the joining of wooden veneers, manufacturing tools, wood processing utensils, etc., can solve the problems of poor electromagnetic shielding performance, human health threats, and poor bacteriostatic effect. Wear resistance, improve electromagnetic shielding performance, enhance the effect of antibacterial effect

Inactive Publication Date: 2019-02-22
赵顺全
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is aimed at the defect that the plywood existing on the market is easy to breed miscellaneous bacteria and has poor antibacterial effect during use, which will pose a great threat to human health, and its electromagnetic shielding performance is poor. A preparation method of antibacterial electromagnetic shielding plywood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029]Mix aniline, potassium dichromate, and hydrochloric acid with a mass fraction of 15% according to a mass ratio of 3:1:3, then pour it into a reaction kettle, and stir and react for 1 hour at a temperature of 150°C. After the reaction, poly Aniline: the polyaniline obtained above and the m-cresol solution with a mass fraction of 12% are mixed in a volume ratio of 2:1, then poured into a magnetic stirrer, and stirred and mixed at a speed of 300r / min for 30min to obtain modified polyaniline solution; put the wood core board in an oven, and dry it for 40 minutes at a temperature of 50°C to obtain a pretreated wood core board, put the pretreated wood core board into the above-mentioned modified polyaniline solution, and after immersing for 6 hours, Dry to obtain a modified wood core board; put the honeysuckle in a pulverizer and pulverize it for 20 minutes to obtain a honeysuckle pulverized product, mix the honeysuckle pulverized product and an ethanol solution with a mass fra...

example 2

[0031] Mix aniline, potassium dichromate, and hydrochloric acid with a mass fraction of 15% according to a mass ratio of 3:1:3 and pour it into a reaction kettle. Stir and react for 1.5 hours at a temperature of 160°C. After the reaction is completed, get Polyaniline; the polyaniline obtained above and the m-cresol solution with a mass fraction of 12% are mixed in a volume ratio of 2:1, then poured into a magnetic stirrer, and stirred and mixed for 35min at a speed of 350r / min to obtain a modified polyaniline. Aniline solution; put the wood core board in an oven, and dry it for 45 minutes at a temperature of 55°C to obtain a pretreated wood core board, put the pretreated wood core board into the above-mentioned modified polyaniline solution, and dip for 7 hours , dried to obtain a modified wood core board; put the honeysuckle into a pulverizer and pulverize it for 25 minutes to obtain a honeysuckle crush, and mix the honeysuckle powder and an ethanol solution with a mass fracti...

example 3

[0033] Mix aniline, potassium dichromate, and hydrochloric acid with a mass fraction of 15% according to a mass ratio of 3:1:3 and pour it into a reaction kettle. Stir and react for 2 hours at a temperature of 170°C. After the reaction, poly Aniline: the polyaniline obtained above is mixed with a mass fraction of 12% m-cresol solution in a volume ratio of 2:1, then poured into a magnetic stirrer, and stirred and mixed for 40 minutes at a speed of 400r / min to obtain modified polyaniline solution; put the wood core board in an oven, and dry it for 50 minutes at a temperature of 60° C. to obtain a pretreated wood core board. Put the pretreated wood core board into the above-mentioned modified polyaniline solution, and after 8 hours of immersion, Dry to obtain a modified wood core board; put the honeysuckle in a pulverizer and pulverize it for 30 minutes to obtain a honeysuckle pulverized product, mix the honeysuckle pulverized product and an ethanol solution with a mass fraction o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an antibacterial electromagnetic shielding type plywood, and belongs to the technical field of plates. According to the method, the polyaniline monomersare used as raw materials, the arrangement and conformation of the polyaniline main chains are changed; the conductivity of the polyaniline reaches the maximum value; the electromagnetic shielding performance of the modified polyaniline solution is greatly improved; the wood core board is placed in the modified polyaniline solution for dipping, so that the modified polyaniline solution with the electromagnetic shielding effect is attached to the surface of the wood core plate; the honeysuckle contains rich achyranthes bidentata, inositol, tannic acid and other effective components and can beused for inhibiting various bacteria; silica gel is amorphous silicon dioxide, the chlorhexidine acetate solution can be adsorbed by silica gel, due to the use of the chlorhexidine acetate solution, the antibacterial performance of the plywood prepared by the method can be improved; 3-Glycidoxypropylthrimethoxysilane is used as a coupling agent, mixed and stirred with silica gel adsorbed with chlorhexidine acetate, so that the antibacterial silica gel adhesive is fully fused into an adhesive state. The antibacterial electromagnetic shielding type plywood has a wide application prospect.

Description

technical field [0001] The invention discloses a preparation method of antibacterial electromagnetic shielding type plywood, which belongs to the technical field of boards. Background technique [0002] Plywood is one of the commonly used materials for furniture and is a kind of wood-based panel. Plywood is a three-layer or multi-layer board-like material that is made of wood sections that are peeled into veneers or sliced ​​into thin wood, and then glued with adhesives. Usually, odd-numbered veneers are used, and adjacent layers of veneers are used. The fiber directions are glued perpendicular to each other. One of the commonly used materials for furniture is a wood-based panel. A group of veneers are usually assembled and glued together according to the direction of the wood grain of adjacent layers perpendicular to each other. Usually, the surface board and inner layer board are symmetrically arranged on both sides of the center layer or core. The slab made of the vene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27D1/08
CPCB27D1/08
Inventor 赵顺全陈珺王素香
Owner 赵顺全
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products