Coffee ring laser containing silver telluride quantum dots and preparation method thereof

A technology of quantum dots and silver telluride is applied in the field of semiconductor optoelectronic devices, which can solve the problems of reducing the stability and life of lasers, and achieve high stability and improve stability and life.

Inactive Publication Date: 2019-02-01
NANJING UNIV OF POSTS & TELECOMM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, directly exposing the quantum dots to air reduces the stability and lifetime of the laser

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coffee ring laser containing silver telluride quantum dots and preparation method thereof
  • Coffee ring laser containing silver telluride quantum dots and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further explained below in conjunction with the accompanying drawings.

[0021] Such as figure 2 As shown, the coffee ring laser containing silver telluride quantum dots of the present invention includes a quartz substrate 2 arranged upward in sequence, and a silicon dioxide ring 3 containing silver telluride quantum dots.

[0022] The silicon dioxide ring 3 containing silver telluride quantum dots is composed of a silicon dioxide ring and silver telluride quantum dots 1 embedded in the silicon dioxide ring. The silver telluride quantum dots 1 are uniformly distributed in the silicon dioxide ring. Silver telluride quantum dots 1 as figure 1 shown. The silver telluride quantum dot 1 is an optical gain medium, and the silver telluride quantum dot 1 with only double spin degeneracy in the lowest quantum state with low toxicity can realize near-infrared optical gain with a low threshold. Embedding silver telluride quantum dots 1 into silic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a coffee ring laser containing silver telluride quantum dots. The coffee ring laser comprises a quartz substrate and a silicon dioxide circular ring containing silver telluride quantum dots which are arranged upwards in order. The coffee ring laser replaces the minimum quantum state 8-fold degenerate lead salt quantum dots with the harmfulless minimum quantum state2-fold degenerate silver telluride quantum dots to achieve near-infrared light gain of a low threshold value. The quantum dots are inlaid into the silicon dioxide to improve the stability and the lifeof the laser. The mixing liquid of the silver telluride quantum dots and perhydro polysilazane is employed to prepare a coffee ring to finally obtain a coffee ring near-infrared light quantum dot laser with a low threshold value, high stability and a friendly environment.

Description

technical field [0001] The invention relates to a coffee ring laser containing silver telluride quantum dots and a preparation method thereof, belonging to the technical field of semiconductor optoelectronic devices. Background technique [0002] Near-infrared lasers can be widely used in fields such as optical communication, remote sensing, and coherent plasma generation. Benefiting from the quantum confinement effect, semiconductor quantum dots exhibit a variety of superior properties as optical gain materials, such as tunable emission wavelength with size, potentially low laser threshold and temperature-insensitive laser performance. At present, near-infrared quantum dot lasers prepared by molecular beam epitaxy have begun commercial applications. Compared with epitaxially grown quantum dots, colloidal quantum dots have a smaller size and a more uniform size distribution, so they have stronger quantum confinement effects and narrower emission peaks. The most common near...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01S5/10
CPCH01S5/10
Inventor 廖晨
Owner NANJING UNIV OF POSTS & TELECOMM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com