High-temperature-resistant flame-retardant electrostatic flocking fabric and preparation method thereof

An electrostatic flocking and high-temperature-resistant technology, which is applied to the device for coating liquid on the surface, textiles, papermaking, coating, etc., can solve the problems of poor flame-retardant durability, insufficient high-temperature resistance, and easy combustion, and achieve flocking High fastness, good flame retardant effect

Inactive Publication Date: 2019-01-29
山东领潮新材料有限公司 +2
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, common flocking fabrics generally have problems such as burning and dripping. Flocking products with flame-retardant treatment have problems such as insufficient high temperature resistance, poor flame-retardant durability, or poor environmental protection performance. Applications such as decoration are potentially dangerous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A high-temperature-resistant flame-retardant electrostatic flocking fabric includes a fluff layer, an adhesive layer and a base cloth layer.

[0025] The fluff layer is basalt ultra-short fiber, the fluff length is 0.5mm, and the fineness is 1.0D;

[0026] The base fabric layer is a basalt fiber warp and weft knitted fabric, and the mass per unit area of ​​the fabric is 100g / m 2 ;

[0027] The adhesive layer is epoxy resin with a viscosity of 14,000 cps.

[0028] The preparation method of the above-mentioned high temperature resistant flame retardant electrostatic flocking fabric comprises the following steps:

[0029] Step 1, preparation of high temperature resistant flame retardant ultra-short fiber

[0030] The high-temperature-resistant and flame-retardant basalt fiber strips are cut, and then the fluff is treated with soaring performance to make fluff for flocking; the soaring performance is 12s, the moisture content is 0.5%, and the surface resistance is 1.6*10...

Embodiment 2

[0044] A high-temperature-resistant flame-retardant electrostatic flocking fabric includes a fluff layer, an adhesive layer and a base cloth layer.

[0045] The fluff layer is polyimide ultra-short fiber, the fluff length is 1.0mm, and the fineness is 1.5D;

[0046] The base fabric layer is a basalt fiber warp and weft knitted fabric, and the mass per unit area of ​​the fabric is 100g / m 2 ;

[0047] The adhesive layer is polyimide with a viscosity of 42,000 cps.

[0048] The preparation method of the above-mentioned high temperature resistant flame retardant electrostatic flocking fabric comprises the following steps:

[0049] Step 1, preparation of high temperature resistant flame retardant ultra-short fiber

[0050] The high-temperature-resistant polyimide fiber strips are cut, and then the fluff is treated with flying performance to make fluff for flocking; the flying performance is 9s, the moisture content is 1.2%, and the surface resistance is 2.3*10 6 Ω, pilling rate...

Embodiment 3

[0064] A high-temperature-resistant flame-retardant electrostatic flocking fabric includes a fluff layer, an adhesive layer and a base cloth layer.

[0065] The fluff layer is basalt ultra-short fiber, the fluff length is 1.2mm, and the fineness is 2.0D;

[0066] The base fabric layer is a carbon fiber warp and weft woven fabric, and the mass per unit area of ​​the fabric is 350g / m 2 ;

[0067] The adhesive layer is polyimide with a viscosity of 42,000 cps.

[0068] The preparation method of the above-mentioned high temperature resistant flame retardant electrostatic flocking fabric comprises the following steps:

[0069] Step 1, preparation of high temperature resistant flame retardant ultra-short fiber

[0070] The high-temperature-resistant basalt fiber strips are cut, and then the fluff is treated with flying performance to make fluff for flocking; the flying performance is 20s, the moisture content is 0.8%, and the surface resistance is 3.2*10 6 Ω, pilling rate 0.1%. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Finenessaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-temperature-resistant flame-retardant fiber electrostatic flocking fabric and a preparation method thereof, wherein the flocking fabric comprises a fluff layer, an adhesive layer and a base cloth layer; the fluff layer adopts one or more of aramid fiber 1313, polyimide, polyphenylene sulfide, polysulfonamide, polyacrylonitrile or viscose pre-oxidized yarns, polyether-ether-ketone, poly (p-phenylene benzobisoxazole), basalt fiber, ceramic fiber and glass fiber as fluff fiber, and the length of the fluff is 0.5-3 mm, and the fineness is 0.8-50 D. The flocking fabrichas remarkable flame-retardant properties: the flame-retardant effect is good, the permanent flame-retardant effect is achieved, and the flame-retardant grade can reach A-grade flame retardancy according to GB / T5455.

Description

technical field [0001] The invention relates to a high-temperature-resistant flame-retardant fiber electrostatic flocking fabric and a preparation method thereof, belonging to the field of electrostatic flocking. Background technique [0002] The so-called flocking fabric is made of all kinds of fabrics as the base fabric, with nylon fluff or viscose fluff planted on the front, and then processed by drying and washing. of favor. [0003] At present, common flocking fabrics generally have problems such as burning and dripping. Flocking products with flame-retardant treatment have problems such as insufficient high temperature resistance, poor flame-retardant durability, or poor environmental protection performance. Applications such as decoration are potentially dangerous. [0004] Therefore, there is an urgent need to design a high temperature resistant flame retardant electrostatic flocking fabric to further meet people's needs. Contents of the invention [0005] In vi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N7/00B05D1/06
CPCB05D1/06D06N7/0097D06N2209/067
Inventor 赵丽罗欣郝新敏孟庆荣
Owner 山东领潮新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com