A production process of packaging composite film

A production process and composite film technology, which are applied in the directions of devices and coatings for coating liquid on the surface, can solve the problems of complex preparation process of packaging composite films, and the barrier properties of packaging composite films are difficult to meet the requirements of high-barrier drug packaging. Achieve the effect of eliminating the corona step, shortening the working hours, and simplifying the process steps

Active Publication Date: 2021-02-19
SICHUAN HUILI IND
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a production process of packaging composite film to solve the problem that the existing packaging composite film preparation process is complicated, and the barrier performance of the packaging composite film prepared by the process is difficult to meet the requirements of high barrier drug packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production process of packaging composite film
  • A production process of packaging composite film
  • A production process of packaging composite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] Preparation of hyperbranched cationic mussel-like polymer P1:

[0072]2,3,4-Trihydroxybenzoyl-isobenzoyl-(2-aminoethyl)acrylamide, N-(2-aminoethyl)(meth)acrylamide hydrochloride, 4-azide 2,3,5,6-tetrafluorobenzoylethylamine (meth)acrylamide, polyethylene glycol methyl ether acrylate (PEGMEA), polyethylene glycol diacrylate (PEGDEA, ethylene glycol The degree of polymerization is 22) and the RAFT reagent is added to the N,N-dimethylformamide solution with the concentration of 0.012M as the initiator 4,4'-azobis(4-cyanovaleric acid). Among them, the degree of polymerization of ethylene glycol in PEGMEA is 15, the degree of polymerization of ethylene glycol in PEGDEA is 22, 4,4'-azobis(4-cyanovaleric acid), RAFT reagent and all monomers involved in polymerization The molar ratio of the first reaction mixture is 1:2:100. 2,3,4-trihydroxybenzoyl-isobenzoyl-(2-aminoethyl)acrylamide:N-(2-aminoethyl) (Meth)acrylamide hydrochloride: 4-azido-2,3,5,6-tetrafluorophenacylethylamin...

Embodiment 2

[0079] Preparation of hyperbranched cationic mussel-like polymer P2:

[0080] 2,3,4-trihydroxybenzoyl p-benzamide ethyl (meth)acrylamide hydrochloride, N-(3-aminopropyl) (meth)acrylamide hydrochloride, 4- Nitro-2,3,5,6-tetrafluorobenzoylethylamine (meth)acrylamide, polyethylene glycol methyl ether acrylate (PEGMEA), polyethylene glycol diacrylate (PEGDEA) and RAFT The reagent is added to the N,N-dimethylformamide solution with the concentration of 0.012M of the initiator 2,2'-azobis(2-methylpropionitrile). Among them, the degree of polymerization of ethylene glycol in PEGMEA is 45, the degree of polymerization of ethylene glycol in PEGDEA is 10, 2,2'-azobis(2-methylpropionitrile), RAFT reagent and all monomers participating in polymerization The molar ratio of the first reaction mixture is 1:2:100. 2,3,4-trihydroxybenzoylbenzamide ethyl (meth)acrylamide hydrochloride: N-(3-aminopropyl) (Meth)acrylamide hydrochloride: 4-azido-2,3,5,6-tetrafluorophenacylethylamine (meth)acryla...

Embodiment 3

[0088] Preparation of hyperbranched cationic mussel-like polymer P3:

[0089] 2,3-Dihydroxybenzoylbenzoate amine ethyl (meth)acrylamide hydrochloride, N-(4-aminobutyl) (meth)acrylamide hydrochloride, 4-azide Base-phenacylethylamine (meth)acrylamide, polyethylene glycol methyl ether acrylate (PEGMEA), polyethylene glycol diacrylate (PEGDEA) and RAFT reagent 2-(dodecyltrithio Carbonate group)-2-methylpropionic acid was added to the N,N-dimethylformamide solution with a concentration of 0.012M of the initiator 2,2'-azobis(2-methylpropionitrile). Among them, the degree of polymerization of ethylene glycol in PEGMEA is 5, the degree of polymerization of ethylene glycol in PEGDEA is 8, 2,2'-azobis(2-methylpropionitrile), RAFT reagent and all monomers participating in polymerization The molar ratio of the first reaction mixture is 1:2:100. 2,3-Dihydroxybenzoylbenzoate amine ethyl(meth)acrylamide hydrochloride: N-(4-aminobutyl) (Meth)acrylamide hydrochloride: 4-azido-phenacylethylam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process of a packaging composite film, comprising the following steps: (A) configuring a hyperbranched cationic mussel imitating polymer into an aqueous binder solution, the hyperbranched cationic mussel imitating polymer comprising polyphenolic hydroxyl di Benzophenone enamide monomer, cationic monomer and photoresponsive monomer; (B) preparing graphene oxide solution; (C) immersing the polymer film in the aqueous binder solution, taking it out and drying it, and immersing the polymer film in (D) soak the polymer film prepared in the step (C) in the aqueous binder solution, take out and soak the polymer film in the graphene oxide solution after drying; (E) repeat steps ( D); (F) putting the polymer film prepared in the step (E) into an aqueous reducing agent solution, heating to reflux and condensing to obtain a packaging composite film. The invention saves the corona step, not only reduces the process cost, but also simplifies the process steps.

Description

technical field [0001] The invention relates to the field of packaging materials, in particular to a production process of a packaging composite film. Background technique [0002] As the main packaging material of pharmaceuticals, polymer film packaging materials have become more and more important in daily life. However, due to the influence of the plastic film production process and its own physical and chemical characteristics, it is difficult for the barrier properties of plastics to oxygen, water vapor, liquid substances and other low molecular weight substances to meet the requirements of most pharmaceutical packaging. The penetration of small molecular gases such as oxygen and water vapor into packaging materials will lead to oxidative deterioration of the active ingredients in the drug, which in turn will cause the reproduction of microorganisms and other phenomena. The direct consequence is that the shelf life of the drug is greatly shortened. Therefore, it is of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/04C08J7/04C08J5/18C08F283/06C08F220/60C08L67/02
CPCC08F283/065C08J5/18B05D7/04C08F2438/03C08J2367/02C08J7/0423C08F220/603C08F220/606C08F220/60
Inventor 柏金枝张辉闫斌
Owner SICHUAN HUILI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap