Production process of puncture-proof fabrics

A production process and fabric technology, applied in two or more different solvent-based treatment materials, fabric surface trimming, heating/cooling fabrics, etc., can solve the difficult weaving of ultra-high molecular weight polyethylene fibers and unstable product quality. and other problems, to achieve the effect of good style and feel, good protection and good flexibility

Inactive Publication Date: 2019-01-15
CHINA TEXTILE ACAD JIANGNAN BRANCH
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the first aspect of the present invention is to solve the problems of difficult weaving of ultra-high molecular weight polyethylene fibers and unstable product quality in the existing production process of stab-resistant fabrics. Innovative design in terms of control methods and other aspects, providing a non-composite, weft-knitted stab-resistant fabric with better air permeability, wearing comfort, flexibility and protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of puncture-proof fabrics
  • Production process of puncture-proof fabrics
  • Production process of puncture-proof fabrics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0088] A kind of production technology of anti-stab fabric, comprises the following steps:

[0089] 1. Raw material performance test and analysis:

[0090]Single-yarn performance tests were performed on high-strength polyester filaments and ultra-high molecular weight polyethylene filaments, and the obtained data were compared, researched and analyzed. The breaking strength of ultra-high molecular weight polyethylene filaments of the same fineness is 3 to 5 times that of high-strength polyester filaments, but the elongation at break is less than half of that of high-strength polyester filaments. When high-strength polyester filaments are tested When the elongation at break of the ultra-high molecular weight polyethylene filament is reached, the force it bears is only about 40% of its own breaking strength. The difference in breaking strength and elongation at break of the two raw materials provides a new idea for the design of the fabric structure and the design of the yarn r...

Embodiment 2

[0146] A kind of production technology of anti-stab fabric, comprises the following steps:

[0147] 1. Raw material performance test and analysis:

[0148] Single-yarn performance tests were performed on high-strength polyester filaments and ultra-high molecular weight polyethylene filaments, and the obtained data were compared, researched and analyzed. The breaking strength of ultra-high molecular weight polyethylene filaments of the same fineness is 3 to 5 times that of high-strength polyester filaments, but the elongation at break is less than half of that of high-strength polyester filaments. When the elongation at break of ultra-high molecular weight polyethylene filament, the force it bears is only about 40% of its own breaking strength. The difference in breaking strength and elongation at break of the two raw materials provides a new idea for the design of the fabric structure and the design of the yarn ratio.

[0149] The specification of the high-strength polyester...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a production process of puncture-proof fabrics. The ultrahigh molecular weight polyethylene filament and high-tenacity polyester filament yarns are taken as raw materials, the performance difference of the ultrahigh molecular weight polyethylene filaments and the high-tenacity polyester filament yarns is analyzed to determine the specifications of the ultrahigh molecular weight polyethylene filaments and the high-tenacity polyester filament yarns and determine the yarn usage amount of the two, through the organization structure design of the fabrics, numbers ofpaths of the ultrahigh molecular weight polyethylene filaments are reasonably distributed, a weaving process employs a weft knitting mode for weaving, a coil structure is employed to perform advantagecomplementation of the two raw materials so as to solve the problem that the ultrahigh molecular weight polyethylene filaments are difficult to weave, the weaved fabrics are processed through adoption a after treatment process to produce a finished product. The novel puncture-proof fabrics by taking the ultrahigh molecular weight polyethylene filaments and the high-tenacity polyester filament yarns as the raw materials are good in breathability, wearing comfort, flexibility and economy.

Description

Technical field: [0001] The invention relates to a stab-proof fabric, in particular to a production process of a stab-proof fabric, belonging to the technical field of special fabric production. Background technique: [0002] Although we are in a peaceful age, violent conflicts, terrorist attacks and other incidents still occur in various countries around the world. With the improvement of people's awareness of protection and anti-terrorism, personal protection has become a hot topic worldwide, and stab-resistant fabrics play an extremely important role in personal protection. [0003] Most of the traditional stab-proof fabrics use metal sheets and wires, and most of them are formed by thermal bonding or stitching of multi-layer fabrics, such as a kind of police protective clothing in patent CN 106490716 A. Because it contains metal components and is composed of multiple layers, the preparation process is complicated, the air permeability and wearing comfort are not good, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/12D06B9/04D06C7/02
Inventor 余浪方虹天党会茹
Owner CHINA TEXTILE ACAD JIANGNAN BRANCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com