Non-curing rubber asphalt waterproof coating and preparing method thereof

A technology of asphalt waterproof coating and non-curing rubber, which is applied in the direction of asphalt coatings and coatings, which can solve the problems of expensive raw materials, difficulty in achieving full viscosity, hidden safety hazards of modifiers, etc., to solve compatibility problems, The effect of improving waterproof reliability and solving the problem of water channeling

Pending Publication Date: 2019-01-01
中建友(唐山)科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the existing asphalt waterproofing membranes also have a certain degree of elongation, when there are cracks in the base of the building or deformation of the building structure, it is still easy to cause the waterproof layer to crack.
Moreover, in areas with complex structures, it is difficult to achieve full adhesion, resulting in water channeling
Some of the raw materials of the existing non-curing rubber asphalt waterproof coatings are expensive, some materials are not environmentally friendly, the modifiers used have potential safety hazards, and the VOC content is high, which directly restricts the use and promotion of non-curing waterproof coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-curing rubber asphalt waterproof coating and preparing method thereof
  • Non-curing rubber asphalt waterproof coating and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Prepare each raw material according to the following formula, in parts by weight: 44 parts of 90# asphalt, 15 parts of naphthenic oil, 2 parts of modifier A (modified polypropylene wax H430), modifier B (linear phenylacetic acid-isoamyl Diene-styrene thermoplastic block copolymer S1105) 3 parts, modifier C (linear polyisobutylene 680) 3 parts, rosin resin 2 parts, SBR 5 parts, heavy calcium 10 parts, antioxidant (1010) 1 part , 2 parts of thickener (attapulgite);

[0031] Add asphalt and naphthenic oil into the reaction kettle, heat and keep the temperature to 160°C to form the first product; add modifier B to the first product, stir at high speed for 0.5 hours, stop stirring for 15 minutes, and then continue stirring for 0.5 hours, the second product was formed; the second product was cooled to 140° C., SBR was added, and stirred at a constant temperature and high speed for 2 hours to obtain the third product; modifier A, modifier C, Rosin resin and antioxidant were s...

Embodiment 2

[0033] Prepare each raw material according to the following formula, in parts by weight: 50 parts of 90# asphalt, 16 parts of naphthenic oil, 3 parts of modifier A (modified polypropylene wax H430), modifier B (linear phenylacetic acid-isoamyl Diene-styrene thermoplastic block copolymer S1105) 3 parts, modifier C (linear polyisobutylene 680 and 950 mixed at a mass ratio of 1:2) 5 parts, rosin resin 2 parts, SBR 6 parts, heavy calcium 12 parts , 1.5 parts of antioxidant (1010), 2 parts of thickener (attapulgite);

[0034] Add asphalt and naphthenic oil into the reaction kettle, heat and keep the temperature to 165°C to form the first product; add modifier B to the first product, stir at high speed for 0.5 hours, stop stirring for 15 minutes, and then continue stirring for 0.5 After 1 hour, the second product was formed; the second product was cooled to 145° C., SBR was added, and stirred at a constant temperature and high speed for 2 hours to obtain the third product; modifier ...

Embodiment 3

[0036] Prepare each raw material according to the following formula, in parts by weight: 48 parts of 90# asphalt, 18 parts of naphthenic oil, 4 parts of modifier A (modified polypropylene wax H430), modifier B (linear phenylacetic acid-isoamyl Diene-styrene thermoplastic block copolymer S1105) 4 parts, modifier C (linear polyisobutylene 680 and 950 mixed at a mass ratio of 1:1) 4 parts, rosin resin 2 parts, SBR 5 parts, heavy calcium 12 parts , 1.5 parts of antioxidant (1010), 2 parts of thickener (attapulgite);

[0037] Add asphalt and naphthenic oil into the reaction kettle, heat and keep the temperature to 170°C to form the first product; add modifier B to the first product, stir at high speed for 0.5 hours, stop stirring for 15 minutes, and then continue stirring for 0.5 After 1 hour, the second product was formed; the second product was cooled to 150° C., SBR was added, and stirred at a constant temperature and high speed for 2 hours to obtain the third product; modifier ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses non-curing rubber asphalt waterproof coating and a preparing method thereof, and relates to the technical field of waterproof coating. The coating includes, by mass, 44-54 parts of asphalt, 15-25 parts of naphthenic oil, 2-5 parts of a modifier A, 3-6 parts of a modifier B, 3-6 parts of a modifier C, 2-4 parts of rosin resin, 5-10 parts of SBR, 10-20 parts of ground calciumcarbonate, 1-2 parts of an antioxidant and 2-4 parts of a thickener, with the modifier A being modified polypropylene wax H430. The coating has a creep property and a self-healing property, is non-curing after long-term contact with air, can permanently maintain elastic-plastic colloid, has characteristic of high self-healing capability, instant adhesion after contact, difficult stripping, excellent integrated performance, a low cost and a reduced VOC content, can seal basement layer cracks and capillary openings and can adapt to complex construction operation surfaces.

Description

technical field [0001] The invention relates to the technical field of waterproof coatings, in particular to a non-cured rubber asphalt waterproof coating and a preparation method thereof. Background technique [0002] Due to its mature technology, high level of industrialization, stable performance, convenient construction and simple maintenance of equipment, modified bitumen waterproofing membrane is widely used in domestic and foreign construction. Asphalt waterproof membrane (referred to as asphalt membrane) is a layer of waterproof layer laid on the surface of the building, or between the building base and the decorative surface. An important technical means of service life. Asphalt waterproofing membrane is widely used in industrial and civil buildings at home and abroad because of its simple structure, less maintenance workload, long service life, and long-term waterproofing effect in one construction. [0003] Although the existing asphalt waterproofing membrane al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D7/61C09D7/48C09D7/65
CPCC09D7/65C09D195/00C09D7/48C09D7/61C08L2201/08C08L2205/025C08L2205/035C08K2003/265C08L91/00C08L23/12C08L53/02C08L23/20C08L93/04C08L9/06C08K5/1345C08K3/26C08K3/346
Inventor 秦冬彪吴飞孙璐李晋玲武文利黄涛毕瑞超吴建鹏班俊霞
Owner 中建友(唐山)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com