All-wood brush

A technology of wood and bristles, applied in the direction of brushes, brush bodies, bristles, etc., can solve the problems of easy mold, formaldehyde, and easy residual moisture in the bristles, and achieve the effect of good air permeability and strong wear resistance.

Inactive Publication Date: 2018-12-18
安徽玉达工具有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wood brushes currently on the market are made of mixed wood chips, and the adhesive contains formaldehyde, which is not environmentally friendly.
Secondly, the current brush bristles are easy to drip when dipped in paint, and after the bristles are used, moisture is easy to remain between the bristles, and it is easy to mold after a long time, shortening the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • All-wood brush
  • All-wood brush

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] see Figure 1-2 As shown, an all-wood brush includes a brush handle 1, a brush head 2, one end of the brush handle 1 is provided with a block 3, one end of the block 3 is provided with an edge block 4, the brush handle 1, the block 3, and the edge block 4 is an integrally formed structure. One end of the brush head 2 is provided with a card slot 5 that is compatible with the block 3 and the edge block 4. The brush handle 1, the brush head 2, the block 3, and the edge block 4 are all carved from wood. The other end of the brush head 2 is provided with bristles 6, and the handle is provided with perforations 7.

[0026] The bristle is composed of the following raw materials in parts by weight: 80 parts of bamboo fiber, 6 parts of nano titanium dioxide, 100 parts of tourmaline powder, 15 parts of polyvinyl alcohol resin, 2 parts of phase solvent and 1 part of dispersant.

[0027] The bristles are prepared as follows:

[0028] (1) Take the raw materials of corresponding w...

Embodiment 2

[0034] The structure of the all-wood brush in this embodiment is the same as that of Embodiment 1, except that the raw material composition and preparation method of the bristles are different.

[0035] The bristle is composed of the following raw materials in parts by weight: 83 parts of bamboo fiber, 7 parts of nano-titanium dioxide, 110 parts of tourmaline powder, 23 parts of polyvinyl alcohol resin, 3 parts of phase solvent, and 2 parts of dispersant.

[0036] The bristles are prepared as follows:

[0037] (1) Take the raw materials of corresponding weight parts respectively;

[0038] (2) Put nano-titanium dioxide, polyvinyl alcohol resin, phase solvent, and dispersant into a kneader, knead for 1.5 hours, obtain auxiliary materials, and set aside;

[0039] (3) Tourmaline powder is made into microfiber, obtains tourmaline powder fiber, for subsequent use;

[0040] (4) Divide the auxiliary material into two parts on average, one part is put into the kneader with bamboo fib...

Embodiment 3

[0043] The structure of the all-wood brush in this embodiment is the same as that of Embodiment 1, except that the raw material composition and preparation method of the bristles are different.

[0044] The bristle is composed of the following raw materials in parts by weight: 86 parts of bamboo fiber, 8 parts of nano-titanium dioxide, 120 parts of tourmaline powder, 30 parts of polyvinyl alcohol resin, 5 parts of phase solvent and 3 parts of dispersant.

[0045] The bristles are prepared as follows:

[0046] (1) Take the raw materials of corresponding weight parts respectively;

[0047] (2) Put nano-titanium dioxide, polyvinyl alcohol resin, phase solvent, and dispersant into a kneader, knead for 2 hours, obtain auxiliary materials, and set aside;

[0048] (3) Tourmaline powder is made into microfiber, obtains tourmaline powder fiber, for subsequent use;

[0049] (4) The auxiliary material is divided into two parts on average, one part is put into the kneader with bamboo fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an all-wood brush comprising a brush handle and a brush head. One end of the brush handle is provided with a clamp block. One end of the clamp block is provided with a prismatic block. The brush handle, the clamp block and the prismatic block are integrally formed. One end of the brush head is provided with a clamp groove matching the clamp block and the prismatic block. The brush handle, the brush head, the clamp block and the prismatic block are all carved from wood. The other end of the brush head is provided with bristles. The all-wood brush is environmentally friendly and durable, and the bristles are not easy to mildew, so that the service life of the bristles can be prolonged.

Description

technical field [0001] The invention relates to a hairbrush device, in particular to an all-wood brush. Background technique [0002] The brush is a traditional labor tool that originated in China. The brush was invented by the working people of the ancient Han nationality in the production practice. With the continuous development of human society, the industrious and intelligent Han nationality is constantly summing up experience, keeping its essence, discarding its dross, and bravely exploring and innovating. Made an outstanding contribution. At present, the brush handle of the brush is divided into two kinds of materials, plastic and wood, and the plastic is not environmentally friendly. However, the wood brushes currently on the market are synthesized by bonding miscellaneous wood chips, and the adhesive contains formaldehyde, which is not environmentally friendly. Secondly, the current bristles are easy to drip when dipped in paint, and after the bristles are used,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A46B5/00A46B9/02A46D1/00A46D1/04
CPCA46B5/00A46B9/02A46D1/006A46D1/0207A46D1/04
Inventor 汪超汪靖福
Owner 安徽玉达工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com