High-efficiency quantum dot thin film capable of reflecting blue light and preparation method and application thereof

A quantum dot, high-efficiency technology, applied in the field of high-efficiency quantum dot film and its preparation, can solve the problems of large eye damage and general luminous efficiency of quantum dot film, and achieve the effect of improving luminous efficiency, protecting eyes and preventing damage

Inactive Publication Date: 2018-10-02
NINGBO JIANGBEI EXCITON NEW MATERIAL TECH CO LTD
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the high-energy blue light in the current quantum dot display has great damage to the eyes and the luminous efficiency of the quantum dot film is general, the present invention provides a high-efficiency quantum dot film that can reflect blue light and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-efficiency quantum dot thin film capable of reflecting blue light and preparation method and application thereof
  • High-efficiency quantum dot thin film capable of reflecting blue light and preparation method and application thereof
  • High-efficiency quantum dot thin film capable of reflecting blue light and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0081] The preparation method of the high-efficiency quantum dot thin film that can reflect blue light provided by the present invention, described method comprises the following steps:

[0082] (1) Configure the water-oxygen barrier coating, mix glue A and glue B according to a certain ratio, stir at high speed for 30 minutes, and set aside;

[0083] (2) Apply the water-oxygen barrier coating evenly on the functional anti-blue light film, and cure it with UV light to obtain the water-oxygen barrier layer;

[0084] (3) Mix the adhesive, titanium dioxide particles, silicon dioxide particles, and red and green quantum dots, and stir at high speed for 30 minutes to obtain a quantum dot glue solution;

[0085] (4) Evenly apply the quantum dot glue solution on the surface of the upper water oxygen barrier layer, and obtain the quantum dot glue layer by UV light curing;

[0086] (5) Apply the water-oxygen barrier coating evenly on the surface of the quantum dot glue layer, and obta...

Embodiment 1

[0097] The high-efficiency quantum dot film capable of reflecting blue light provided by the invention consists of a quantum dot glue layer, a functional anti-blue light layer or film, an upper water oxygen barrier layer, a lower water oxygen barrier layer and an anti-scratch coating. The upper and lower surfaces of the quantum dot glue layer are provided with a water-oxygen barrier layer, the lower surface of the lower water-oxygen barrier layer is provided with an anti-scratch coating, and the upper surface of the upper water-oxygen barrier layer is provided with a functional anti-blue light layer or film. The functional anti-blue light layer or film can characteristically reflect blue light, and use the reflected blue light to re-excite quantum dots to improve the utilization rate of blue light.

[0098] The quantum dot layer comprises 100 parts by weight of UV curing acrylic adhesive; 2 parts by weight of red quantum dots; 6 parts by weight of green quantum dots; 5 parts by...

Embodiment 2

[0100] As the high-efficiency quantum dot film that can reflect blue light provided in Example 1, the quantum dot glue layer includes 100 parts by weight of adhesive; 3 parts by weight of red quantum dots; 7 parts by weight of green quantum dots; 5 parts by weight Titanium dioxide particles, the particle size of the titanium dioxide particles is 0.2-0.5 μm; 10 parts by weight of silicon dioxide particles, the particle size of the silicon dioxide particles is 1-2 μm; the thickness of the quantum dot layer is 150 μm The thickness of the anti-scratch coating is 5-10 μm, the particles in the anti-scratch coating are PMMA, and the particle size of the anti-scratch particles is 10-20 μm; the upper water oxygen barrier layer, The thickness of the water oxygen barrier layer is 2-10 μm; the thickness of the functional anti-blue light film or layer is 70 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an optical thin film, in particular to a quantum dot thin film. The invention aims to solve the problems that at present, high-energy blue light in quantum dot display severely hurts eyes and the luminous efficiency of a quantum dot thin film is general. The invention provides a high-efficiency quantum dot thin film capable of reflecting blue light and a preparation methodand application of the high-efficiency quantum dot thin film. The quantum dot thin film and a blue-light-resistant film (reflective) are integrated. The high-efficiency quantum dot thin film comprises a quantum dot glue layer, water-oxygen blocking layers and a functional blue-light-resistant layer or film, wherein the water-oxygen blocking layers coat the upper surface and the lower surface of the quantum dot glue layer; and the functional blue-light-resistant layer or film is attached to the upper water-oxygen blocking layer. The functional blue-light-resistant layer or film can reflect blue light, the reflected blue light secondarily stimulates quantum dots, the utilization rate of the blue light is increased, and the luminous efficiency of the quantum dot thin film is qualitatively improved. By the high-efficiency quantum dot thin film, the use amount of the quantum dots can be reduced, an effect of saving cost is achieved well, furthermore, part of blue light can be filtered out,and effects of relieving visual fatigue and protecting eyes are achieved.

Description

technical field [0001] The invention relates to the field of optical thin films, and more specifically relates to a high-efficiency quantum dot thin film capable of reflecting blue light and its preparation method and application. Background technique [0002] Quantum dot TV is a TV that uses quantum dot technology as a backlight source. Like traditional LCD display technology, quantum dot display is also a non-luminous display device that requires a backlight module to provide light. The difference between the two is that traditional LCDs use white light as a light source, while quantum dot liquid crystal displays require blue light to excite the red and green quantum dots in the quantum dot film to obtain a white light source. The light source excited by quantum dots is the purest backlight, revolutionary Realize the full color gamut display, and restore the image color most realistically. [0003] However, while quantum dot TV achieves high color gamut display, it also b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02F1/13357C09K11/88C09K11/02
CPCC09K11/02C09K11/883G02F1/133621G02F1/133614
Inventor 张彦孙书政徐良霞李培源刘伟陈冲徐雍捷唐海江李刚
Owner NINGBO JIANGBEI EXCITON NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com