Detection method for stabilizing broken stone gradation by cement

A cement-stabilized gravel and detection method technology, applied in the direction of measuring devices, instruments, scientific instruments, etc., to achieve the effect of reducing variance, reducing cement residue, and improving repeatability

Inactive Publication Date: 2018-09-28
ZHANJIANG JIANKE ENG QUALITY TESTING CENT CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the technical problem to be solved by the present invention is to overcome the lack of effective detection of cement-stabilized macadam gradation in the prior art, thereby providing a detection method for cement-stabilized macadam gradation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Detection method for stabilizing broken stone gradation by cement
  • Detection method for stabilizing broken stone gradation by cement
  • Detection method for stabilizing broken stone gradation by cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] This embodiment provides a cement dissolving agent, comprising the following components: 15 parts by weight of citric acid, 15 parts by weight of hydrochloric acid, 0.1 part by weight of sodium ethylenediamine tetramethylene phosphonate, and 5 parts by weight of sodium dodecylbenzenesulfonate .

[0049] This embodiment also provides the preparation method of the above-mentioned cement dissolving agent, comprising the steps of: weighing the citric acid, hydrochloric acid, sodium ethylenediamine tetramethylene phosphonate and sodium dodecylbenzenesulfonate of the above-mentioned components and dissolving them in water , mix uniformly, and finally make citric acid containing 15wt%, 15wt% hydrochloric acid, 0.1wt% sodium ethylenediamine tetramethylene phosphonate and 5wt% sodium dodecylbenzenesulfonate and mixed aqueous solution, to obtain cement dissolver.

Embodiment 2

[0051] This embodiment provides a cement dissolving agent, comprising the following components: 20 parts by weight of citric acid, 5 parts by weight of hydrochloric acid, 2 parts by weight of sodium ethylenediamine tetramethylene phosphonate, and 0.1 part by weight of sodium dodecylbenzenesulfonate .

[0052] The present embodiment also provides the preparation method of the above-mentioned cement dissolving agent, comprising the steps of: taking the citric acid, hydrochloric acid, sodium ethylenediamine tetramethylene phosphonate and sodium dodecylbenzenesulfonate of the above-mentioned components and dissolving them in water, Mix evenly, and finally make 20wt% citric acid, 5wt% hydrochloric acid, 2wt% sodium ethylenediamine tetramethylene phosphonate and 0.1wt% sodium dodecylbenzenesulfonate and a mixed aqueous solution to obtain cement Solvent.

Embodiment 3

[0054] This embodiment provides a cement dissolving agent, comprising the following components: 18 parts by weight of citric acid, 12 parts by weight of hydrochloric acid, 0.5 parts by weight of sodium ethylenediamine tetramethylene phosphonate, and 2.5 parts by weight of sodium dodecylbenzenesulfonate .

[0055] The present embodiment also provides the preparation method of the above-mentioned cement dissolving agent, comprising the steps of: taking the citric acid, hydrochloric acid, sodium ethylenediamine tetramethylene phosphonate and sodium dodecylbenzenesulfonate of the above-mentioned components and dissolving them in water, Mix evenly, and finally make citric acid containing 18wt%, 12wt% hydrochloric acid, 0.5wt% sodium ethylenediamine tetramethylene phosphonate and 2.5wt% sodium dodecylbenzenesulfonate and mixed aqueous solution, to obtain cement dissolver.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a detection method for stabilizing broken stone gradation by cement. According to the invention, a mass m0 of a broken stone sample stabilized by cement is measured in the step1-step 7, the mass m1 and the mass m2 of the broken stone sample stabilized by cement after drying are respectively measured, the mass m3 of the dried particles having a particle size being greater than or equal to 0.075 mm in an aggregate can be measured, and the grader retained mass mi of the aggregate at a filter sieve with a diameter of the sieve aperture being I is measured; according to theabove m0, m1, m2, m3 and the cement dosage omega, the water content Rho of the broken stone stabilized by cement, the mass of the cement and aggregate and ma, the aggregate mass mb and the aggregategradation parameter can be calculated, the gradation detection of the broken stone stabilized by cement is realized, full dissolving of the cement in the broken stone stabilized by cement can be guaranteed through the step 5), a mixture m3 the sieve does not contain the cement, the gradation detection accuracy is increased, and gradation parameter of the broken stone stabilized by cement on on-site construction can be accurately reflected, so that the broken stone stabilized by cement is subjected to mass monitoring from the construction process and result.

Description

technical field [0001] The invention relates to the field of material testing and analysis, in particular to a method for detecting the gradation of cement-stabilized gravel. Background technique [0002] In recent years, the scale of my country's highway construction has continued to expand. With the rapid growth of road traffic, especially the rapid growth of heavy vehicle traffic, high requirements have been put forward for the carrying capacity and use intensity of roads. At present, the pavement structure of my country's highways mainly adopts the semi-rigid base asphalt pavement structure, which is made of various aggregates and soils stabilized by hydraulic materials (also known as inorganic binders) as the semi-rigid base, and paved on the semi-rigid base. A certain thickness of asphalt mixture surface layer is formed. [0003] Cement-stabilized crushed stone is a roadbed material formed by adding a small amount of cement and water to graded crushed stone, which is u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N5/00
CPCG01N5/00
Inventor 周大强
Owner ZHANJIANG JIANKE ENG QUALITY TESTING CENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com