Production method using chlorination process by-product for inorganic coating of titanium dioxide
A technology of inorganic coating and production method, which is applied in chemical instruments and methods, inorganic pigment treatment, fibrous fillers, etc., can solve the problems of high cost of cerium salt, improved light resistance of titanium dioxide, and unfavorable long-term operation of titanium dioxide manufacturers. Achieve low cost, solve light fastness and whiteness problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] Sand mill the kiln products of sulfuric acid process titanium dioxide qualified for calcining, and then import the slurry with qualified particle size into the coating tank, and control the concentration of the slurry to 250g / L (based on TiO 2 meter), while raising the temperature to 40°C; adding 0.15%TiCl within 40min 4 (with TiO 2 count), while adding 3%NaH 2 PO 4 and Na 3 PO 4 , Homogenized for 60min. Heating to 80°C, using NaAlO 2 Adjust pH to 6.8-7.0, 1.0% H 3 PO 4 with 2%NaAlO 2 Parallel flow, keep pH=6.0-7.5, 90min to finish adding, homogenize for 45min. 4% NaAlO 2 (in Al 2 o 3 count) and H 2 SO 4 Maintain pH=6.0-7.5 in parallel flow, finish adding in 150 minutes, homogenize for 45 minutes; use dilute H 2 SO 4 Adjust the pH value of the slurry to 5.3-5.5. Homogenized for 1 hour, washed three times, flash steamed and steamed to obtain the finished product.
Embodiment 2
[0020] Sand mill the kiln products of sulfuric acid process titanium dioxide qualified for calcining, and then introduce the slurry with qualified particle size of the sand mill into the coating tank, and control the concentration of the slurry to 300g / L (based on TiO 2 meter), while raising the temperature to 40°C; adding 0.4%TiCl within 50min 4 (with TiO 2 count), while adding 2%NaH 2 PO 4 and Na 3 PO 4 , Homogenized for 60min. Heating to 80°C, using NaAlO 2 Adjust pH to 6.8-7.0, 2.0% H 3 PO 4 with 2%NaAlO 2 Parallel flow, keep pH=6.0-7.5, finish adding in 60 minutes, homogenize for 45 minutes. 3% NaAlO 2 (in Al 2 o 3 count) and H 2 SO 4 Maintain pH=6.0-7.5 in parallel flow, finish adding in 120 minutes, homogenize for 45 minutes; use dilute H 2 SO 4 Adjust the pH value of the slurry to 5.3-5.5. Homogenized for 1.5h, washed three times, flash steamed and steamed to get the finished product.
Embodiment 3
[0022] Sand mill the kiln products of sulfuric acid process titanium dioxide that is qualified for calcining, and then introduce the slurry with a qualified particle size of the sand mill into the coating tank, and control the concentration of the slurry to 350g / L (based on TiO 2 meter), while raising the temperature to 40°C; adding 0.6%TiCl within 50min 4 (with TiO 2 count), while adding 4%NaH 2 PO 4 and Na 3 PO 4 , Homogenized for 60min. Heating to 80°C, using NaAlO 2 Adjust pH to 6.8-7.0, 3.0% H 3 PO 4 with 2%NaAlO 2 Parallel flow, keep pH=6.0-7.5, finish adding in 60 minutes, homogenize for 45 minutes. 6% NaAlO 2 (in Al 2 o 3 count) and H 2 SO 4 Maintain pH=6.0-7.5 in parallel flow, finish adding in 120 minutes, homogenize for 45 minutes; use dilute H 2 SO 4 Adjust the pH value of the slurry to 5.3-5.5. Homogenized for 1.5h, washed three times, flash steamed and steamed to get the finished product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com