Environmentally friendly diatom mud wall material and preparation method thereof

A diatom mud and wall material technology, applied in the field of interior decoration coatings, can solve the problems of diatom mud wall materials, such as easy to drop powder, low strength, and not resistant to dirt, achieve good adsorption and degradation functions, improve water repellency, reduce The effect of surface cracks

Inactive Publication Date: 2018-09-25
杨显武
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of environmental protection diatom ooze wall material and preparation method thereof, the preparation process of this diatom ooze wall material is easy to operate, the produced diatom ooze wall material has better anti-mildew and antibacterial properties, and its Excellent strength, flexibility, and crack resistance, which solves the technical problems of diatom mud wall materials that are easy to powder, easy to crack, low strength, and not resistant to dirt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environmentally friendly diatom mud wall material, mainly made of the following raw materials in parts by weight: 50 parts of diatomite, 10 parts of nano-titanium dioxide, 10 parts of heavy calcium, 5 parts of wollastonite powder, 5 parts of quartz powder, and 4 parts of attapulgite powder 4 parts, gray calcium powder 4 parts, graphene 4 parts, propyl gallate 3 parts, negative ion powder 2 parts, sodium hexametaphosphate dispersant 2 parts, surface modifier 5 parts, anti-mold and antibacterial agent 5 parts, inorganic aluminum 2 parts of salt water resistance agent and 5 parts of binder; wherein,

[0027] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmityl glycinate and stearic acid according to the mass ratio of 2:2:1;

[0028] The anti-mildew and antibacterial agent is prepared by the following method: wash 40 parts of aloe, 20 parts of cloves, 15 parts of eucalyptus magnum and 5 parts of vanilla, pulverize them, and pass through a 100-mes...

Embodiment 2

[0039] An environmentally friendly diatom mud wall material, mainly made of the following raw materials in parts by weight: 75 parts of diatomite, 13 parts of nano-titanium dioxide, 12 parts of heavy calcium, 9 parts of wollastonite powder, 8 parts of quartz powder, and 8 parts of attapulgite powder 8 parts, gray calcium powder 8 parts, graphene 6 parts, propyl gallate 7 parts, anion powder 7 parts, acrylate ammonium salt dispersant 15 parts, surface modifier 9 parts, anti-mold and antibacterial agent 10 parts, urea-formaldehyde resin water resistance agent 7 parts and 8 parts of binder; wherein,

[0040] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmityl glycinate and stearic acid according to the mass ratio of 2:2:1;

[0041] The anti-mildew and antibacterial agent is prepared by the following method: 50 parts of aloe, 35 parts of cloves, 25 parts of eucalyptus magnanimum and 15 parts of vanilla are washed, pulverized, and passed through a 120-mesh...

Embodiment 3

[0052] An environmentally friendly diatom mud wall material, mainly made of the following raw materials in parts by weight: 70 parts of diatomite, 12 parts of nano-titanium dioxide, 11 parts of heavy calcium, 8 parts of wollastonite powder, 7 parts of quartz powder, and 7 parts of attapulgite powder 6 parts, 6 parts of gray calcium powder, 5.5 parts of graphene, 6 parts of propyl gallate, 6 parts of negative ion powder, 10 parts of dispersant composed of ammonium acrylate and styrene acrylic acid copolymer, 8 parts of surface modifier, anti 9 parts of mold antibacterial agent, 6 parts of inorganic aluminum salt water resistance agent and 7 parts of binder;

[0053] The surface modifier is made by mixing sodium lauryl sulfate, sodium palmityl glycinate and stearic acid according to the mass ratio of 2:2:1;

[0054] The anti-mildew and antibacterial agent is prepared by the following method: 48 parts of aloe, 34 parts of cloves, 24 parts of eucalyptus magnum and 14 parts of vani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of indoor decoration coating, and relates to an environmentally friendly diatom mud wall material. The material is mainly prepared from, by weight, 50-75 parts of diatomite, 10-13 parts of nanometer titanium dioxide, 10-12 parts of ground calcium carbonate, 5-9 parts of wollastonite powder, 5-8 parts of quartz powder, 4-8 parts of attapulgite powder, 4-8 parts ofsierozem powder, 4-6 parts of graphene, 3-7 parts of propyl gallate, 2-7 parts of negative ion powder, 2-15 parts of a dispersant, 5-9 parts of a surface modifier, 5-10 parts of a mildew-proof antibacterial agent, 2-7 parts of a water resistant agent and 5-8 parts of a binder. The preparation process of the diatom mud wall material is simple, and the diatom mud wall material produced has better mildew-proof and antibacterial properties and excellent strength, flexibility and crack resistance, and overcomes technical problems including easy powder falling, easy cracking, low strength and no stain resistance of diatom mud wall materials.

Description

technical field [0001] The invention belongs to the field of interior decoration coatings, and in particular relates to an environment-friendly diatom mud wall material and a preparation method thereof. Background technique [0002] The main component of diatom mud is diatomaceous earth, and the main component of diatomaceous earth is diatoms. Diatoms are the first single-celled algal organisms that appeared on the earth. They live in seawater or lake water, and their shapes are extremely small. The main component of diatom mud is protein, which is rich in a variety of beneficial minerals and has a soft texture. Use an electron microscope to observe diatom mud. Diatom mineral is a micron-scale porous material. There are countless tiny holes on the surface of the particles, which are regularly and neatly arranged in circles and needles, with a porosity of more than 90. The number of micropores is thousands of times more than that of charcoal. This molecular sieve structure...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14C04B111/20C04B111/34
CPCC04B28/14C04B2111/00017C04B2111/00025C04B2111/00482C04B2111/2092C04B2111/343C04B2201/10C04B2201/50C04B14/08C04B14/305C04B14/28C04B14/043C04B14/06C04B14/102C04B22/064C04B14/024C04B24/045C04B24/16C04B24/085C04B18/248C04B24/2623C04B24/38C04B24/123C04B22/16C04B22/08C04B2103/0068C04B24/04C04B24/302C04B24/26
Inventor 杨显武
Owner 杨显武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com