Graphene-metal composite material and preparing raw material, method and application thereof

A metal composite material and composite material technology, applied in the field of graphene-metal composite materials and their preparation raw materials, can solve the problems of battery life reduction, excessive power usage, slow online business operations, etc., and achieve good heat dissipation efficiency, Easy operation and simple process

Inactive Publication Date: 2018-09-14
厦门奈福新材料股份有限公司
View PDF9 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Applying the graphene-metal composite material to the heat conduction and heat dissipation components of electronic products can effectively solve the serious heating of electro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-metal composite material and preparing raw material, method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preformed ingot for the preparation of graphene-metal composite materials, the preformed ingot is made of graphene powder and aluminum powder, graphene accounts for 0.015% of the total weight of the preformed ingot, which is single-layer graphene, multi-layer graphene, mechanical One or more of exfoliated graphene, graphene oxide, reduced graphene oxide, and graphene derivatives; the purity of the aluminum powder is ≥99.9%, and the mesh size is ≥600 mesh.

[0027] A kind of graphene-metal composite material, this composite material is made of metal material and aforementioned prefabricated ingot, according to the composition of this composite material in parts by weight: 10 parts of prefabricated ingot, 85.9 parts of aluminum, 0.4 part of silicon, 0.2 part of iron , 0.1 part of copper, 0.3 part of manganese, 2.7 parts of magnesium, 0.3 part of chromium, and 0.1 part of titanium, the graphene includes single-layer graphene, multi-layer graphene, mechanically exfoliated ...

Embodiment 2

[0035] A prefabricated ingot for the preparation of a graphene-metal composite material, the prefabricated ingot is made of graphene powder and aluminum powder, and the graphene accounts for 0.15% of the total weight of the preformed ingot, which is single-layer graphene, multilayer graphene 1. One or more of mechanically exfoliated graphene, graphene oxide, reduced graphene oxide, and graphene derivatives; the purity of the aluminum powder is ≥99.9%, and the mesh number is ≥600 mesh.

[0036] A kind of graphene-metal composite material, this composite material is made of metal material and aforementioned prefabricated ingot, according to the composition of this composite material in parts by weight: 50 parts of prefabricated ingot, 45.9 parts of aluminum, 0.4 part of silicon, 0.2 part of iron , 0.1 part of copper, 0.3 part of manganese, 2.7 parts of magnesium, 0.3 part of chromium, and 0.1 part of titanium, the graphene includes single-layer graphene, multi-layer graphene, mec...

Embodiment 3

[0043] A prefabricated ingot for the preparation of a graphene-metal composite material, the prefabricated ingot is made of graphene powder and aluminum powder, and the graphene accounts for 0.3% of the total weight of the preformed ingot, which is single-layer graphene, multilayer graphene 1. One or more of mechanically exfoliated graphene, graphene oxide, reduced graphene oxide, and graphene derivatives, the purity of the aluminum powder is ≥99.9%, and the mesh number is ≥600 mesh.

[0044] A kind of graphene-metal composite material, this composite material is made of metal material and aforementioned prefabricated ingot, prefabrication is as follows according to the composition of this composite material of weight part: prefabricated ingot 95.9 parts, silicon 0.4 part, iron 0.2 part, copper 0.1 part 0.3 parts, 0.3 parts of manganese, 2.7 parts of magnesium, 0.3 parts of chromium, and 0.1 parts of titanium. one or several species.

[0045] The preparation method of above-m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Meshaaaaaaaaaa
Login to view more

Abstract

The invention discloses a graphene-metal composite material and a preparing raw material, method and application thereof. Firstly, graphene is evenly scattered in single metal aluminum or copper in anano scattering manner, and a prefabricated ingot in which graphene is evenly scattered, and later usage is convenient is prepared; the prefabricated ingot and a metal material comprising one or moremetal components are evenly fused through a co-smelting and stirring manner, and the graphene-metal composite material excellent in heat conduction and heat dissipation efficiency and high in mechanical strength is prepared. The graphene-metal composite material is applied to heat conduction and heat dissipation elements of electronic products, and the problems that heat emitting of the electronicproducts is serious, the electric quantity is used rapidly, shutdown is automatic, operation is in failure, the service life of a battery is shortened, online business operation is slow, and potential safety hazards exist can be effectively solved.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a graphene-metal composite material and its preparation raw material, method and application. Background technique [0002] With the rapid development of modern technology, electronic products tend to be small, thin, light, and multi-functional, which also makes electronic components more miniaturized, the main frequency of chips continues to increase, and the power consumption of a single chip gradually increases. These changes As a result, the heat flux density increases sharply, electronic products heat up severely, and then there are a series of problems such as excessive power consumption, automatic shutdown, operation failure, reduced battery life, slow online business operations, and potential safety hazards. More studies have shown that more than 55% of electronic products fail in the form of overheating, so the heat dissipation of electronic components plays a pivotal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C9/04C22C21/08C22C1/05
CPCC22C1/05C22C9/04C22C21/08C22C32/0084
Inventor 陈锦裕
Owner 厦门奈福新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap