A production technology for a high energy gem biology wave health care yarn

A production process and bio-wave technology, applied in the field of yarn production, can solve problems such as damage to guide holes and knitting needles, easy breakage of yarn stretching, and abnormal horizontal stripes on the cloth surface, so as to enhance vitality and health, and relieve pain , the effect of balancing the potential of the human body

Inactive Publication Date: 2018-09-04
南通富尊纺织科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high hardness and high strength of zirconia itself, the yarn is stretched and easily broken during spinning, and the finished yarn is subsequently false-twisted and weaved into a medium-high hardness yarn, which damages the guide hole and the knitting needle. , these problems will cause abnormal horizontal stripes on the cloth surface, and even difficult to weave and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] A production process of high-energy gem biowave health care yarn, comprising the following steps:

[0023] Step 1. Dissolving zirconium oxychloride powder in water to form an aqueous solution of zirconium oxychloride, and adding an appropriate interface agent to protect the reduced zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is: polyvinylpyrrolidone ( PVP), its chemical formula is (C6H9NO)n;

[0024] Step 2. The obtained powder is blended with PET through a twin-screw. In the twin-screw blending production, the reaction temperature is 270°C, and it is carried out under vacuum. H 2 O and HCl are extracted, and the reaction is carried out, and the reaction is as follows:

[0025] ZrOCl 2 ·8H 2 O→Zr(OH) 4 +2HCl+5H 2 O;

[0026] The above method can be made into extremely fine zirconia blended in PET masterbatch, and then drawn into PET plastic yarn by drawing equipment.

specific Embodiment 2

[0027] A production process of high-energy gem biowave health care yarn, comprising the following steps:

[0028] Step 1. Use zirconium oxychloride powder to dissolve in water to form zirconium oxychloride aqueous solution, and add an appropriate interface agent to protect the reduced zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is: dodecyl Sodium sulfate (SDS), its chemical formula is C12H25SO4Na;

[0029] Step 2. The obtained powder is blended with PET through a twin-screw. In the twin-screw blending production, the reaction temperature is 290°C, and it is carried out under vacuum. H 2 O and HCl are extracted, and the reaction is carried out, and the reaction is as follows:

[0030] ZrOCl 2 ·8H 2 O→Zr(OH) 4 +2HCl+5H 2 O;

[0031] The above method can be made into extremely fine zirconia blended in PET masterbatch, and then drawn into PET plastic yarn by drawing equipment.

specific Embodiment 3

[0032] A production process of high-energy gem biowave health care yarn, comprising the following steps:

[0033] Step 1. Dissolve zirconium oxychloride powder in water to form an aqueous solution of zirconium oxychloride, and add an appropriate interface agent to protect the reduced zirconia and avoid secondary agglomeration in the subsequent process; the interface agent is dodecylbenzene Sodium sulfonate (SDBS), its chemical formula is C18H29NaO3S;

[0034] Step 2. The obtained powder is blended with PET through a twin-screw. In the twin-screw blending production, the reaction temperature is 280°C, and it is carried out under vacuum. H 2 O and HCl are extracted, and the reaction is carried out, and the reaction is as follows:

[0035] ZrOCl 2 ·8H2 O→Zr(OH) 4 +2HCl+5H 2 O;

[0036] The above method can be made into extremely fine zirconia blended in PET masterbatch, and then drawn into PET plastic yarn by drawing equipment.

[0037] In the present invention, plastic par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production technology for a high energy gem biology wave health care yarn. The production technology includes the following steps: step 1: dissolving zirconium oxychloride powder into water to form a zirconium oxychloride aqueous solution, adding proper interface agent, for protecting restored zirconia so as to avoid secondary agglomeration in a subsequent process; step 2: performing mixing on obtained powder and PET by using a twin-screw extruder in a vacuumized environment, wherein H2O and HCL are dissociated, allowing a reaction to carry out, PET master batches mixed with extremely fine zirconia can be prepared by the method and is drawn to the PET plastic cement yarn through a drawnwork device. The yarn contains the interface agent, the restored zirconia is protected, the agglomeration is not easy to be generated, the reactant and dyeing and finishing are mingled in the yarn and on the surface of the yarn, the yarn with a height far infrared is generated,a problem of weaving difficulties caused by that yarn guiding holes and a knitting needle are damaged by the PET yarn after drawnwork is solved.

Description

technical field [0001] The invention belongs to the field of yarn production, and in particular relates to a production process of high-energy gem biowave health-care yarn. Background technique [0002] Zirconium dioxide is a stable oxide, which has the characteristics of acid resistance, wear resistance, alkali resistance, corrosion resistance and high temperature resistance, and can release far infrared rays that are beneficial to the human body. What is far-infrared ray? According to the known knowledge of materials science, zirconia is the main ingredient. If it is higher than 0.89, it will have an enhanced positive effect on the human body. Infrared ray is a kind of radiation in the sun's rays; infrared ray is invisible light, which is light that cannot be seen by human eyes. [0003] Gem zirconium materials are mostly used in military and aerospace science and technology. After ten years of research by Tsinghua University’s Polymer Materials Laboratory, it has been us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/02D01D5/08D01F1/10D01F6/92
CPCD02G3/02D01D5/08D01F1/10D01F6/92D10B2331/04D10B2401/13
Inventor 管志祥管蓓莉
Owner 南通富尊纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com