Shell powder reinforcing air purification material and preparation method thereof
A technology of air purification materials and shell powder, which is applied in chemical instruments and methods, gas treatment, and other chemical processes, can solve the problems of low recycling rate, limited adsorption capacity, poor stability, etc., and achieve high recycling rate and improved Effect of surface activity and stability improvement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A shell powder reinforced air purification material, which is composed of the following raw materials in parts by weight:
[0020] Activated shell powder 16, melamine 1, sodium alkylbenzene sulfonate 0.5, trimethylolpropane 2, methylpyrrolidone 5, diatomaceous earth 65, tetradecanedioic acid 1, 1,2-dimethylimidazole 0.8 .
[0021] The preparation method of described activation shell powder, comprises the following steps:
[0022] Take 50-60 parts by weight of shell powder, add it to a hydrochloric acid solution with a concentration of 0.7mol / l, soak for 2 hours, filter, wash the precipitate with water, dry it at room temperature, mix it with 1 part by weight of oleic acid, and keep it warm at 65°C Stir for 30 minutes, add to 5 times the weight of the mixture in deionized water, sonicate for 10 minutes, filter, place the precipitate in an oven at 50°C, and dry it completely to obtain the product.
[0023] A preparation method of shell powder reinforced air purification...
Embodiment 2
[0029] A shell powder reinforced air purification material, which is composed of the following raw materials in parts by weight:
[0030] Activated shell powder 20, melamine 2, sodium alkylbenzene sulfonate 1, trimethylolpropane 2, methylpyrrolidone 7, diatomaceous earth 70, tetradecanedioic acid 2, 1,2-dimethylimidazole 1 .
[0031] The preparation method of described activation shell powder, comprises the following steps:
[0032] Take 60 parts by weight of shell powder, add it to a hydrochloric acid solution with a concentration of 1 mol / l, soak for 3 hours, filter, wash the precipitate with water, dry it at room temperature, mix it with 2 parts by weight of oleic acid, and keep stirring at 70°C for 40 minutes , added to deionized water that was 7 times the weight of the mixture, ultrasonicated for 14 minutes, filtered, and the precipitate was placed in an oven at 55°C and dried completely to obtain the product.
[0033] A preparation method of shell powder reinforced air...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com