A kind of continuous extrusion preparation method of graphene aluminum alloy wire

A technology of aluminum alloy wire and graphene, which is applied in metal processing equipment, transportation and packaging, etc., can solve the problems affecting the production efficiency of aluminum wire, the limitation of wire length, and the deterioration of material performance, so as to achieve energy saving, good performance stability, Good product performance

Active Publication Date: 2021-10-08
新疆烯金石墨烯科技有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the traditional melting casting method, due to the large density difference between the two and the non-wetting of the interface, it is difficult for graphene to disperse uniformly in the aluminum liquid. In addition, the high-temperature interface reaction between the two may occur during the material preparation process to form Al 4 C 3 Brittle phase, deteriorating material properties
A disadvantage of the traditional powder metallurgy method is the discontinuity of production, the length of the wire is limited, and a series of auxiliary operations such as separation, pressing, and filling of the billet are required between the extrusion of the front and rear billets, which affects the production efficiency of the aluminum wire.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of continuous extrusion preparation method of graphene aluminum alloy wire
  • A kind of continuous extrusion preparation method of graphene aluminum alloy wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of preparation method of graphene aluminum alloy composite material, this method comprises the following steps:

[0035] (1) Take graphene and -200~400 purpose aluminum alloy powder, graphene accounts for 0.5% of total mass;

[0036] (2) Graphene is ultrasonically dispersed in alcohol solution for 0.5h to obtain a mixed solution of graphene and alcohol;

[0037] (3) Add the alloy powder into the graphene and alcohol mixed solution in batches, at a rotating speed of 100r / min, at a temperature of 40°C, and mix for 2 hours to obtain a semi-solid paste graphene and alloy mixed powder;

[0038] (4) placing the uniformly mixed graphene and alloy mixed powder at the feeding place of the continuous extrusion equipment;

[0039] (5) Open the feed valve, and perform dynamic vacuum degassing during the downward flow of the graphene and alloy mixed powder. The flow rate is 1.0L / min, the heating temperature is 300°C, and the vacuum degree is 2.0×10 -3 Pa;

[0040] (6) Cont...

Embodiment 2

[0042] A kind of preparation method of graphene aluminum alloy composite material, this method comprises the following steps:

[0043] (1) Take graphene and -200~400 purpose alloy powder, graphene accounts for 1.0% of total mass;

[0044] (2) Graphene is ultrasonically dispersed in alcohol solution for 1.0h to obtain a mixed solution of graphene and alcohol;

[0045] (3) adding the alloy powder into the graphene and alcohol mixed solution in batches, at a rotating speed of 500r / min, at a temperature of 60°C, and mixing for 1h to obtain a semi-solid paste graphene alloy mixed powder;

[0046] (4) placing the uniformly mixed graphene alloy powder at the feeding place of the continuous extrusion equipment;

[0047] (5) Open the feed valve, and perform dynamic vacuum degassing during the downward flow of the graphene alloy mixed powder, with a flow rate of 5.0L / min, a heating temperature of 400°C, and a vacuum degree of 5.0×10 -3 Pa;

[0048](6) Continuously extruding the graph...

Embodiment 3

[0050] A kind of preparation method of graphene aluminum alloy composite material, this method comprises the following steps:

[0051] (1) Take graphene and -200~400 purpose aluminum alloy powder, graphene accounts for 0.7% of total mass;

[0052] (2) Graphene is ultrasonically dispersed in alcohol solution for 1.5h to obtain a mixed solution of graphene and alcohol;

[0053] (3) Add the alloy powder into the graphene and alcohol mixed solution in batches, at a rotating speed of 250r / min, at a temperature of 50°C, and mix for 1.5h to obtain a semi-solid paste graphene alloy mixed powder;

[0054] (4) placing the uniformly mixed graphene alloy powder at the feeding place of the continuous extrusion equipment;

[0055] (5) Open the feed valve, and perform dynamic vacuum degassing during the downward flow of the graphene alloy mixed powder. The flow rate is 3.5L / min, the heating temperature is 350°C, and the vacuum degree is 3.5×10 -3 Pa;

[0056] (6) Continuously extruding th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
breaking strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a continuous extrusion preparation method of a graphene aluminum alloy wire. The preparation method comprises powder mixing, vacuum degassing and extrusion with continuous extrusion equipment provided with an extrusion module and a powder degassing module. The alloy composite material prepared by the technical solution provided by the invention has both the strength of the alloy and the conductivity of pure aluminum; the uniformity of the structure is good, and the performance stability is good; the utilization rate of the material is high, generally up to 95%; the heat generated by friction is used to raise the temperature , without heating, saving energy; few processes, high production efficiency, high product yield; continuous production of products can be realized without interval time; suitable for both large-scale production and small-batch multi-variety production; product performance is good, size High precision and good finish.

Description

technical field [0001] The invention relates to a preparation method of a composite material, in particular to a continuous extrusion preparation method of a graphene aluminum alloy wire. Background technique [0002] With the improvement of power transmission and transformation technology and the development of power transmission and transformation lines, more and more large spans require the use of wires that can transmit large currents and withstand large tensions. Aluminum alloy wires are more and more showing their superiority in this aspect, and they have exclusive advantages in long-distance, large-span, and ultra-high voltage power transmission. At present, the materials of aluminum alloy wires include pure aluminum and aluminum-magnesium-silicon alloy, but the matching of the mechanical properties and electrical properties of the two is relatively low. Pure aluminum has good electrical conductivity, but its strength is low; the addition of Mg, Si and other alloying...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F3/20B22F3/22B22F5/12C22C1/05C22C1/10C22C21/08
CPCC22C1/0416C22C1/05C22C21/08B22F3/20B22F3/22B22F5/12B22F2998/10B22F1/10
Inventor 马冰卢科伟王杰丰王成军钟小勇
Owner 新疆烯金石墨烯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com