Anti-impact polypropylene material and preparation method thereof

A polypropylene material and impact-resistant technology, which is applied in the field of impact-resistant polypropylene material and its preparation, can solve the problems of low impact strength, low density, and impact strength limiting the application range of polypropylene, etc., to broaden the application range, The effect of excellent impact strength

Inactive Publication Date: 2018-06-22
杭州鼎友五金机械制造有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polypropylene has the advantages of greater rigidity, low density, high transparency and heat resistance, but polypropylene has the disadvantage of low impact strength
Low impact strength limits the application range of polypropylene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of impact-resistant polypropylene material, its preparation method comprises the following steps:

[0018] (1) Weigh 65 parts of tetrabutyl titanate, 78 parts of stearic acid, 145 parts of ethanol, 1.7 parts of KH-560 coupling agent and 0.5 parts of Tween 60 into the hydrothermal reaction kettle, and maintain the system temperature at 90 Under the condition of ℃, hydrothermal reaction was carried out for 35 minutes, and the temperature of hydrothermal reaction was raised to 118 ℃ for 4 hours. The product was distilled under reduced pressure at 65 ℃ and -0.07MPa for 45 minutes, dried at -30 ℃ for 25 minutes, and pulverized to obtain titanium dioxide quantum dots;

[0019] (2), weigh 100 parts of diphenylmethane diisocyanate, 6.5 parts of ethylene glycol, 14 parts of 1,4-butanediol, 56 parts of polycarbonate diol, 33 parts of polytetrahydrofuran ether diol, 3.5 parts of poly Ester polyol CM-580 and 0.6 parts of dibutyltin dilaurate were added to the reaction kettle...

Embodiment 2

[0024] A kind of impact-resistant polypropylene material, its preparation method comprises the following steps:

[0025] (1) Weigh 65 parts of tetrabutyl titanate, 75 parts of stearic acid, 137 parts of ethanol, 1 part of KH-560 coupling agent and 0.3 parts of Tween 60 into the hydrothermal reaction kettle to maintain the system temperature at 85 Under the condition of ℃, hydrothermal reaction was carried out for 35 minutes, and the temperature of hydrothermal reaction was raised to 115 ℃ for 4 hours. The product was distilled under reduced pressure at 65 ℃ and -0.07MPa for 45 minutes, dried at -30 ℃ for 25 minutes, and pulverized to obtain titanium dioxide quantum dots;

[0026] (2), weigh 100 parts of diphenylmethane diisocyanate, 6 parts of ethylene glycol, 13 parts of 1,4-butanediol, 52 parts of polycarbonate diol, 30 parts of polytetrahydrofuran ether diol, 3 parts of poly Ester polyol CM-580 and 0.5 parts of dibutyltin dilaurate were added to the reaction kettle, the sti...

Embodiment 3

[0031] A kind of impact-resistant polypropylene material, its preparation method comprises the following steps:

[0032] (1) Weigh 65 parts of tetrabutyl titanate, 86 parts of stearic acid, 151 parts of ethanol, 3 parts of KH-560 coupling agent and 1 part of Tween 60 into the hydrothermal reaction kettle to maintain the system temperature at 93 Under the condition of ℃, hydrothermal reaction was carried out for 35 minutes, and the temperature of hydrothermal reaction was raised to 120 ℃ for 2 hours. The product was distilled under reduced pressure at 65 ℃ and -0.07MPa for 45 minutes, dried at -30 ℃ for 25 minutes, and pulverized to obtain titanium dioxide quantum dots;

[0033] (2), weigh 100 parts of diphenylmethane diisocyanate, 7 parts of ethylene glycol, 15 parts of 1,4-butanediol, 60 parts of polycarbonate diol, 35 parts of polytetrahydrofuran ether diol, 4 parts of poly Ester polyol CM-580 and 1 part of dibutyltin dilaurate were added to the reaction kettle, the stirring...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-impact polypropylene material, which is prepared from the following raw material ingredients including modified polypropylene, titanium dioxide quantum dots, antioxidants 1076 and calcium stearate, wherein the modified polypropylene is prepared from polypropylene, 1-butyl-3-methyl imidazole stearate, stearic acid and polyurethane resin through reaction. The 1-butyl-3-methyl imidazole stearate is prepared from stearic acid, 1-butyl-3-methyl imidazole acetate, 1-butyl-3-methyl imidazole chlorine salt and ethyl alcohol through reaction; the polyurethane resin is prepared from diphenylmethane diisocyanate, glycol, 1,4-butanediol, polycarbonate diol, polytetrahydrofuran ether diol, polyester polyol CM-580 and dibutyl tin laurate through reaction; the titanium dioxide quantum dots are prepared from tetrabutyl titanate, stearic acid, ethanol, KH-560 couplin agents and Tween 60 through reaction. The anti-impact polypropylene material has excellent impact intensity.

Description

technical field [0001] The invention relates to an impact-resistant polypropylene material and a preparation method thereof. Background technique [0002] Polypropylene has the advantages of greater rigidity, low density, high transparency, and heat resistance, but polypropylene has the disadvantage of low impact strength. Low impact strength limits the range of applications for polypropylene. Polypropylene is usually widely used in computer and mobile phone film, plastic food packaging, water delivery pipes, food boxes, municipal water supply and drainage pipes, automobile bumpers and other fields. [0003] At present, the impact strength of polypropylene materials needs to be further improved. The invention uses modified polypropylene, titanium dioxide quantum dots, antioxidant 1076, and calcium stearate to prepare an impact-resistant polypropylene material, and the impact-resistant polypropylene material prepared by the method has excellent impact strength. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L75/04C08K13/02C08K5/3472C08K5/09C08K3/22
CPCC08K2003/2241C08K2201/011C08L23/12C08L75/04C08K13/02C08K5/3472C08K5/09C08K3/22
Inventor 董荣雪
Owner 杭州鼎友五金机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com