Welding method for increasing material dimension

A welding method and size technology, which is applied in the field of special processing, can solve problems such as increasing material size and falling of wear-resistant blocks, and achieve the effects of saving costs, improving production pass rate, and reducing the number of scrapped

Inactive Publication Date: 2018-06-22
GUIYANG AVIC POWER PRECISION CASTING
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to solve the problem of the drop of the wear-resistant block after brazing, prevent the solder from flowing and clogging the tail edge splitting seam caused by repeated brazing, and determine a welding method for increasing the size of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The specific implementation and effect of a welding method for increasing material size according to the present invention will be described in detail below in conjunction with preferred embodiments.

[0027] A welding method for increasing material size provided by the present invention mainly includes the following steps:

[0028] 1) Confirm the surface of the part to be welded;

[0029] 2) The alloy sheet of the size required for the part is processed by wire cutting;

[0030] 3) Grinding the alloy sheet to clean the oxide film and improve the surface roughness;

[0031] 4) cleaning dust and oil stains and drying the alloy sheet after cleaning;

[0032] 5) The alloy sheet is fixed on the position to be welded by resistance spot welding, wherein the spot welding current is 30A, the spot welding angle is 50°, and the spot welding is carried out around the alloy sheet, and the distance between the welding spots is 8mm;

[0033] 6) Apply brazing material and smear flo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of non-traditional machining, in particular to a welding method for increasing material dimension. According to the welding method, an alloy sheet, made ofthe same material with a matrix alloy, of the needed dimension is machined in a wire-electrode cutting manner, the surface of the alloy sheet is polished, an oxidation film is removed, the oxidationfilm on the surface, to be welded, of a part is removed, the surface, to be welded, of the part is cleaned and dried, and the alloy sheet is spot welded and fixed to the to-be-welded portion in an resistance pot welding manner; then, after a brazing material is smeared and a flow stopping agent is smeared at the position nearby a weld joint zone, the brazing material and the flow stopping agent are dried, vacuum brazing is conducted, vacuum brazing heating in a vacuum brazing furnace, temperature preservation and cooling are conducted, and finally weld joint detection and machining are conducted on the welded portion so that the dimension of the part can be restored. By the adoption of the welding method for increasing material dimension, the part of a smaller dimension can be restored, the number of scrapped parts is reduced, cost is saved, and the production yield is improved.

Description

technical field [0001] The invention relates to the technical field of special processing, in particular to a welding method for increasing material size. Background technique [0002] During the processing of a blade edge plate, if the size is too large, it can be further processed until the part size meets the requirements. However, if the part size is too small, and the design requirements are too small, the size is unacceptable, and the part will be scrapped. Therefore, there is an urgent need to find a suitable method so that the parts are not discarded after being repaired when they are about 1mm smaller, and can also be used in parts that require slightly lower material strength. [0003] In view of this, the present invention provides a welding method for increasing material size. Contents of the invention [0004] The main purpose of the present invention is to solve the problem that the wear-resistant block falls after brazing, prevent the solder from flowing an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B23K1/008
CPCB23K1/008B23P15/00
Inventor 郝粉利吴汉昌周勇强火克莉李新兵李健
Owner GUIYANG AVIC POWER PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products