Polyester HOY fibers and preparation method thereof

A technology of HOY and polyester, which is applied in the field of polyester HOY fiber and its preparation, can solve the problems of the adverse effect of polyester performance and the inability to significantly reduce the cyclic oligomers in polyester, and achieve the effect of excellent performance

Active Publication Date: 2018-06-08
JIANGSU HENGLI CHEM FIBER
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the problem that the above-mentioned prior art cannot significantly reduce the content of cyclic oligomers in polyester and will adversely affect the performance of polyester itself, and provide a method that can significantly reduce the content of cyclic oligomers in polyester. The content of polymer can effectively improve the preparation method of polyester fiber, mainly by adding a branched diol with a specific structure to the polyester raw material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester HOY fibers and preparation method thereof
  • Polyester HOY fibers and preparation method thereof
  • Polyester HOY fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] A kind of preparation method of polyester HOY fiber, concrete steps are as follows:

[0069] (1) Preparation of modified polyester:

[0070] (a) Esterification reaction; make a slurry of terephthalic acid, ethylene glycol and 2-ethyl-2-methyl-1,3-propanediol with a molar ratio of 1:1.2:0.03, and add antimony trioxide , titanium dioxide and triphenyl phosphate are mixed evenly, and the esterification reaction is carried out under pressure in a nitrogen atmosphere. The pressurized pressure is normal pressure, and the temperature of the esterification reaction is 250°C. 90% of the value is the end point of the esterification reaction, wherein the addition of antimony trioxide is 0.01% of the weight of terephthalic acid, the addition of titanium dioxide is 0.20% of the weight of terephthalic acid, and the addition of triphenyl phosphate 0.05% of the weight of terephthalic acid, wherein the structural formula of 2-ethyl-2-methyl-1,3-propanediol is as follows:

[0071]

...

Embodiment 2

[0077] A kind of preparation method of polyester HOY fiber, concrete steps are as follows:

[0078] (1) Preparation of modified polyester:

[0079] (a) Esterification reaction; prepare terephthalic acid, ethylene glycol and 2,2-diethyl-1,3-propanediol in a molar ratio of 1:1.3:0.04 into a slurry, add antimony ethylene glycol and titanium dioxide After mixing with trimethyl phosphate evenly, carry out the esterification reaction under pressure in a nitrogen atmosphere, the pressurized pressure is normal pressure, and the temperature of the esterification reaction is 260°C. 91% is the end point of the esterification reaction, wherein the addition of ethylene glycol antimony is 0.02% of the weight of terephthalic acid, the addition of titanium dioxide is 0.21% of the weight of terephthalic acid, and the addition of trimethyl phosphate is 0.02% of the weight of terephthalic acid. 0.03% by weight of phthalic acid, wherein the structural formula of 2,2-diethyl-1,3-propanediol is as...

Embodiment 3

[0086] A kind of preparation method of polyester HOY fiber, concrete steps are as follows:

[0087] (1) Preparation of modified polyester:

[0088] (a) Esterification reaction: terephthalic acid, ethylene glycol, and 2-butyl-2-ethyl-1,3-propanediol in a molar ratio of 1:1.4:0.05 are made into a slurry, and antimony acetate and titanium dioxide are added After mixing evenly with trimethyl phosphite, carry out the esterification reaction under pressure in a nitrogen atmosphere, the pressurized pressure is 0.1MPa, and the temperature of the esterification reaction is 252°C. 92% is the end point of the esterification reaction, wherein the addition of antimony acetate is 0.03% of the weight of terephthalic acid, the addition of titanium dioxide is 0.23% of the weight of terephthalic acid, and the addition of trimethyl phosphite is 0.03% of the weight of terephthalic acid. 0.01% by weight of phthalic acid, wherein the structural formula of 2-butyl-2-ethyl-1,3-propanediol is as foll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Initial modulusaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to polyester HOY fibers and a preparation method thereof. The preparation method comprises the steps of carrying out metering, extrusion, cooling, oiling and high-speed winding of a modified polyester melt to obtain the polyester HOY fibers, wherein the high-speed winding speed of the high-speed winding is more than or equal to 6000 m / min; during cooling, the vertical heightis kept unchanged and the cross section area of a slow cooling chamber is increased; at the same time, the slow cooling chamber maintains the plate surface temperature of a spinneret plate by the wayof heat preservation. The fibers are made of modified polyester having a molecular chain including a terephthalic acid chain segment, an ethylene glycol chain segment and a diol chain segment with a branched chain, and diol with the branched chain has the structural formula described in the specification, wherein R1 and R2 are independently selected from straight-chain alkylene with the carbon atom number of 1-3 , R3 is selected from alkyl with the carbon atom number of 1-5, and R4 is selected from alkyl with the carbon atom number of 2-5; the chromatic aberration [delta]E of the prepared fibers is less than 0.200. The method is simple and reasonable in preparation process, and the prepared fibers have good properties.

Description

technical field [0001] The invention belongs to the field of fiber preparation, and relates to a polyester HOY fiber and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is a polymer with excellent properties. PET is widely used in fibers, bottles because of its advantages such as high modulus, high strength, good shape retention and good barrier properties. In the fields of packaging, film and sheet materials, the output is increasing year by year, and the industry status has been significantly improved. [0003] However, during the polycondensation reaction of synthesizing ethylene terephthalate, especially when producing linear high polymers, linear and cyclic oligomers are also accompanied by high-temperature oxidative degradation, and cyclic oligomers are polycondensed The stage is formed due to the back-biting and cyclization of the macromolecular chain ends. More than 70% of the cyclic oligomers are cyclic trimers. The cycl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92C08G63/183D01D5/088
CPCC08G63/183D01D5/088D01F6/92
Inventor 汤方明王雪邵义伟王建根晏金龙
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com