Light-weight heat-insulating wall body material and preparation method thereof

A heat-insulating wall and light-weight technology, applied in the field of building materials, can solve the problems of not meeting the performance requirements of light-weight and heat preservation, high thermal conductivity, high water absorption rate, etc., and achieve good promotion and application, small thermal conductivity and high water absorption rate low effect

Inactive Publication Date: 2018-06-08
HEFEI FANTENG ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Currently, solid clay bricks, cement mortar lattice bricks, aerated concrete blocks, foam concrete blocks, etc. are mainly used as wall materials. However, these materials not only consume a lot of natural resources such as clay, cement, aggregate, etc. , high water absorption, high thermal conductivity and other defects, which do not meet the performance requirements of modern building materials such as light weight and heat preservation, so it is urgent to develop new wall materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment relates to a light-weight thermal insulation wall material, including the following raw materials in parts by weight: 10 parts of ceramic waste mud, 20 parts of ordinary Portland cement, 15 parts of aluminum electrolytic waste refractory materials, 5 parts of sawdust, and construction waste slag. 12 parts, 18 parts of fly ash, 10 parts of yellow sand, 15 parts of vitrified microbeads, 20 parts of bentonite tailings powder, 13 parts of modified sepiolite, 8 parts of kaolin, 5 parts of borax, 2 parts of foaming agent, 1 part of dispersant, 60 parts of water.

[0033] Wherein, the preparation method of described modified sepiolite is as follows:

[0034] (1) Soak the sepiolite in the mixed solution of sodium carbonate and potassium permanganate for 2 hours, take it out and dry it;

[0035] (2) Add silane coupling agent KH550 equivalent to 2% by weight of sepiolite, sodium lauryl sulfate equivalent to 1% by weight of sepiolite and alumina equivalent to 1% b...

Embodiment 2

[0050] This embodiment relates to a light-weight thermal insulation wall material, including the following raw materials in parts by weight: 20 parts of ceramic waste mud, 30 parts of ordinary Portland cement, 28 parts of aluminum electrolytic waste refractory materials, 10 parts of sawdust, and construction waste slag. 18 parts, 27 parts of fly ash, 20 parts of yellow sand, 30 parts of vitrified microbeads, 40 parts of bentonite tailings powder, 21 parts of modified sepiolite, 14 parts of kaolin, 10 parts of borax, 3 parts of foaming agent, 2 parts of dispersant, 100 parts of water.

[0051] Wherein, the preparation method of described modified sepiolite is as follows:

[0052](1) Soak the sepiolite in the mixed solution of sodium carbonate and potassium permanganate for 4 hours, take it out and dry it;

[0053] (2) Add silane coupling agent KH550 equivalent to 4% of the weight of sepiolite, sodium lauryl sulfate equivalent to 3% of the weight of sepiolite and alumina equiva...

Embodiment 3

[0068] This embodiment relates to a light-weight thermal insulation wall material, including the following raw materials in parts by weight: 13 parts of ceramic waste mud, 22 parts of ordinary Portland cement, 17 parts of aluminum electrolytic waste refractory materials, 7 parts of sawdust, and construction waste slag. 14 parts, 20 parts of fly ash, 13 parts of yellow sand, 22 parts of vitrified microbeads, 25 parts of bentonite tailings powder, 16 parts of modified sepiolite, 10 parts of kaolin, 6 parts of borax, 2.3 parts of foaming agent, 1.2 parts of dispersant, 80 parts of water.

[0069] Wherein, the preparation method of described modified sepiolite is as follows:

[0070] (1) Soak sepiolite in a mixed solution of sodium carbonate and potassium permanganate for 2.5 hours, take it out and dry it;

[0071] (2) Add silane coupling agent KH550 equivalent to 2.5% of the weight of sepiolite, sodium lauryl sulfate equivalent to 1.5% of the weight of sepiolite and alumina equi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light-weight heat-insulating wall body material. The light-weight heat-insulating wall body material is prepared from the following raw materials in parts by weight: 10 to 20parts of ceramic waste mud, 20 to 30 parts of ordinary portland cement, 15 to 28 parts of aluminum electrolysis waste refractory material, 5 to 10 parts of wood sawdust, 12 to 18 parts of building waste muck, 18 to 27 parts of coal ash, 10 to 20 parts of yellow sand, 15 to 30 parts of vitrified micro bubbles, 20 to 40 parts of bentonite tailing meal, 13 to 21 parts of modified sepiolite, 8 to 14parts of kaolin, 5 to 10 parts of borax, 2 to 3 parts of a foaming agent, 1 to 2 parts of a dispersing agent and 40 to 60 parts of water. The light-weight heat-insulating wall body material disclosedby the invention is light in weight, high in strength, low in water absorption rate, small in heat conductivity coefficient and high in heat-insulating performance, and can meet actual application requirements of a building material well.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a lightweight thermal insulation wall material and a preparation method thereof. Background technique [0002] Currently, solid clay bricks, cement mortar lattice bricks, aerated concrete blocks, foam concrete blocks, etc. are mainly used as wall materials. However, these materials not only consume a lot of natural resources such as clay, cement, aggregate, etc. , High water absorption, high thermal conductivity and other defects do not meet the performance requirements of modern building materials such as light weight and heat preservation, so it is urgent to develop new wall materials. Contents of the invention [0003] The present invention provides a light-weight heat-insulating wall material and a preparation method thereof, which solves the problems in the above-mentioned background technology. The light-weight heat-insulating wall material describe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02C04B28/04C04B40/02
CPCC04B28/04C04B40/024C04B2111/40C04B18/26C04B18/165C04B18/16C04B18/08C04B18/12C04B14/06C04B14/24C04B14/106C04B14/042C04B22/08C04B24/16C04B22/16C04B38/02C04B12/04C04B22/10
Inventor 李丹丹
Owner HEFEI FANTENG ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products