High-strength steel narrow gap welding process and material

A welding process, narrow gap technology, applied in welding/cutting medium/material, welding medium, welding equipment, etc., to achieve the effect of eliminating complicated processes

Inactive Publication Date: 2018-05-25
张宇
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, due to the large difference in energy density and thermal cycle curve between laser welding and arc welding, the performance of the same welding material in the two welding methods is completely different.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength steel narrow gap welding process and material
  • High-strength steel narrow gap welding process and material
  • High-strength steel narrow gap welding process and material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-2

[0050] A solid core wire with a diameter of 1.6mm is used.

[0051] The root opening gap is 5mm.

[0052] The quality and performance of welded joints are shown in Table 3.

Embodiment 3-4

[0054] A solid core wire with a diameter of 1.4mm is used.

[0055] Root opening gap 4mm.

[0056] The quality and performance of welded joints are shown in Table 3.

Embodiment 5-6

[0058] A solid core wire with a diameter of 1.6mm is used.

[0059] The root opening gap is 3mm.

[0060] The quality and performance of welded joints are shown in Table 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength steel narrow gap welding process. According to the process, a laser device with the power being 3-8kW is adopted, the dimensions of rectangular light spots arelarger than or equal to 20mm<2>, and the welding speed is 0.3-0.6m / min; the wire feeding speed is 3-8m / min, the electric current of a welding wire is 180-260A, and a U-shaped groove with the angle being 5-10 degrees is adopted; the welding wire includes 0-0.08% of C, 0-0.1% of Si, 1.5%-3.0% of Mn, 1.0%-3.0% of Cr, 0.05%-0.3% of Ti and 0.01%-0.05% of B; and single-pass through welding of a high-strength steel plate within the thickness being within the range of 20mm is conducted, cracks are avoided, and low-temperature toughness of -40 DEG C is 80J or above.

Description

technical field [0001] The invention relates to a narrow-gap welding process and material for high-strength steel, belonging to the field of welding technology, in particular to a laser welding process and welding wire for 800MPa high-strength steel. Background technique [0002] In recent years, high-strength steel with a tensile strength of 800MPa has been used in large-scale structures such as construction machinery, pressure water pipes, and offshore platforms to improve the bearing capacity and comprehensive performance of structural components. [0003] Welding such steel plates by ordinary arc welding often leads to softening of the weld, and the welding efficiency is not high. In order to improve the negative impact of large heat input caused by arc welding and other methods, recently, laser welding, laser-arc hybrid welding and other methods have begun to be used in the welding of 800MPa high-strength steel. Due to the characteristics of high energy and concentrati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K26/348B23K26/12B23K26/24B23K35/30B23K103/04
CPCB23K26/24B23K26/123B23K26/348B23K35/3073B23K35/308
Inventor 张宇
Owner 张宇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap