PLA-PBSA blown film and preparation method thereof

A technology of film and formulation, applied in the field of PLA biodegradable film and its preparation, can solve the problems of non-tear resistance flexibility, unstudied method of improving the tear strength of PLA film, affecting polylactic acid film, etc., to achieve good biological Compatibility, good bioabsorbability, and the effect of solving white pollution

Inactive Publication Date: 2018-05-11
HEILONGJIANG XINDA ENTERPRISE GRP +1
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The above studies on the modification of PLA films at home and abroad, although the transparency of PLA films can be maintained, have not studied the method of improving the tear strength of PLA films, and the serious brittleness, non-tear resistance and poor flexibility of PLA films are the most important factors. The main problems of wide application of polylactic acid film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PLA-PBSA blown film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: the present invention provides a kind of PLA biodegradable film, and the composition of its formula and the proportioning of mass parts are:

[0028] PLA 80 copies;

[0029] 10 copies of PBSA;

[0030] 9 parts of plasticizer diethylene glycol monobutyl adipate;

[0031] 0.4 part of lubricant ethylene bis stearic acid amide;

[0032] Opening agent erucamide 0.4 parts;

[0033] Antioxidant 168 and 1010 blend 0.2 part by mass ratio 1:1.

[0034] Weigh PLA, PBSA, ethylene bisstearamide, erucamide, 168 and 1010 according to the above formula, mechanically blend each component for 5 minutes, add the mixed raw materials into a twin-screw extruder, and extrude Add the above-mentioned diethylene glycol monobutyl ether adipate quantitatively with a peristaltic pump to the side line of the extruder during the extrusion process. The conditions for extrusion and granulation are: the set temperature of the twin-screw extruder is: Zone 1: 140 o C, District 2: 165 o...

Embodiment 2

[0035] Embodiment 2: each component is taken by following formula and quality:

[0036] 70 copies of PLA;

[0037] 20 copies of PBSA;

[0038] 9 parts of plasticizer diethylene glycol monobutyl adipate;

[0039] 0.4 part of lubricant ethylene bis stearic acid amide;

[0040] Opening agent erucamide 0.5 parts;

[0041] Antioxidant 168 and 1010 blend 0.1 part by mass ratio 1:1.

[0042] This step of extrusion granulation and film blowing process is the same as that of Example 1, the thickness of the film is controlled at 0.04mm, and the mechanical properties and light transmittance of the film are tested. The test results are listed in Table 1.

Embodiment 3

[0043] Embodiment 3: each component is taken by following formula and quality:

[0044] 60 copies of PLA;

[0045] 30 copies of PBSA;

[0046] 9 parts of plasticizer diethylene glycol monobutyl adipate;

[0047] 0.4 part of lubricant ethylene bis stearic acid amide;

[0048] Opening agent erucamide 0.5 part;

[0049] Antioxidant 168 and 1010 blend 0.1 part by mass ratio 1:1.

[0050] This step of extrusion granulation and film blowing process is the same as that of Example 1, the thickness of the film is controlled at 0.04mm, and the mechanical properties and light transmittance of the film are tested. The test results are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a polylactic acid (PLA) / poly(butylene succinate-butylene adipate) (PBSA) blown film and a preparation method thereof. The blown film comprises a mixture of PLA, PBSA, plasticizer diethylene glycol monobutyl ether adipate, a lubricant, a plastic lubricant and an antioxidant. The PLA, the PBSA, the lubricant, the plastic lubricant and the antioxidant are first mechanically mixed into a premix, the premix is added through a feeding port of a twin-screw extruder, meanwhile the plasticizer diethylene glycol monobutyl ether adipate is metered and added in through a liquid feeding port of the twin-screw extruder, modified polylactic acid blown film special resin is prepared by melt-extruding, water-cooling, pelletizing and drying, the modified polylactic acid blown film special resin is blown by a film blowing machine to form a transparent tear-resistant biodegradable film. The PBSA, the plasticizers, the lubricant, the plastic lubricant and the antioxidant can effectively increase the tensile elongation at break and tear strength of polylactic acid films, maintains the transparency of the polylactic acid, and solves the brittleness defects of the polylactic acid films. The polylactic acid (PLA) / poly(butylene succinate-butylene adipate) (PBSA) blown film has good mechanical properties and excellent transparency, and can replace PE, PP, PVC and the like for preparation of films and sheets.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a PLA biodegradable film and a preparation method thereof. Background technique [0002] Unlike traditional petroleum-based plastics, PLA is polymerized from lactic acid fermented from plant starch. This is a renewable resource and has biodegradable properties, which is of great significance to protecting the environment. In the increasingly tense situation of petroleum energy, the development and research of PLA resin is particularly important. The properties of PLA itself are similar to the general-purpose plastic polypropylene, such as high modulus, high tensile strength and good processability. However, the brittleness of PLA is serious, and the impact strength is less than 5 KJ / m 2 , seriously restricting its wide application. [0003] PLA also has good processing performance and transparency, and can be applied to traditional extrusion, injection molding, blow molding and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L67/02C08K13/02C08K5/11C08K5/20B29D7/01
CPCB29D7/01C08J5/18C08J2367/04C08J2467/02C08K2201/014C08L67/04C08L2201/06C08L2201/10C08L2203/16C08L67/02C08K13/02C08K5/11C08K5/20
Inventor 张会良马庆维郝艳平杨慧丽张贵宝白云刚林航谢众崔成杰张海斌
Owner HEILONGJIANG XINDA ENTERPRISE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com